The gadolinium, gallium, aluminum garnet doped with cerium and co-doped with dysprosium ions were prepared using sol gel method. The SEM images show that after synthesis, the grains are below 100 nm. The powders were ultrasonically mixed with graphene nanoflakes and ceramics were prepared using the high pressure low temperature sintering technique. A series of the ceramics was prepared using different graphene content. The structure of the samples was examined using X-ray diffraction (XRD), scanning electron microscope (SEM) and Raman techniques. The spectroscopic properties were checked using conventional and persistent luminescence spectra measurements. The thermoluminescence glow curves and fading time of persistent luminescence measurements were performed to check how the graphene presence affects the electron traps number and depth. It was found that the addition of graphene improved the thermal conductivity of co-doped samples. This resulted in faster release of deeper traps and an increase in fading of persistent luminescence. The possibility of releasing energy from deep traps without additional stimulation may allow the use in different applications, the matrices and luminescent ions, which so far did not show persistent luminescence at room temperature. [ABSTRACT FROM AUTHOR]

Recently, to meet the growing demand for stable and flexible batteries, anodes in the form of thin films have drawn the attention of researchers. It is clear that mass production of such batteries would bring the worldwide distribution of flexible devices and wearable electronics closer. Currently, electrodes are deposited on a flexible substrate and consist of conductive and binding agents that increase the volume/weight of the electrode. Here, we propose free-standing and non-active-material-free thin films based on reduced graphene oxide (rGO), titanium dioxide (TiO2) and manganese dioxide (MnO2) as working electrodes in lithium-ion half-cells prepared via the vacuum-assisted filtration method. The electrochemical performance of the assembled half-cells exhibited good cyclic stability and a reversible capacity at lower current densities. The addition of TiO2 and MnO2 improved the capacity of the rGO film, while rGO itself provided a stable rate performance. rGO/TiO2/MnO2 film showed the highest discharge capacity (483 mAh/g at 50 mA/g). In addition, all assembled cells displayed excellent repeatability and reversibility in cyclic voltammetry measurements and good lithium-ion diffusion through the electrolyte, SEI layer and the active material itself. [ABSTRACT FROM AUTHOR]