The optical properties of InGaN/GaN violet light-emitting multiple quantum wells with different thicknesses of GaN quantum barriers are investigated experimentally. When the barrier thickness decreases from 20 to 10 nm, the photoluminescence intensity at room temperature increases, which can be attributed to the reduced polarization field in the thin-barrier sample. However, with a further reduction in the thickness to 5 nm, the sample's luminescence intensity decreases significantly. It is found that the strong nonradiative loss process induced by the deteriorated crystal quality and the quantum-tunneling-assisted leakage of carriers may jointly contribute to the enhanced nonradiative loss of photogenerated electrons and holes, leading to a significant reduction in photoluminescence intensity of the sample with nanoscale ultrathin GaN quantum barriers. [ABSTRACT FROM AUTHOR]

Optical properties of wurtzite violet InGaN/GaN quantum well (QW) structures, with the same well-plus-barrier thickness, grown by metal-organic chemical vapor deposition (MOCVD) on c-plane sapphire substrates, were investigated using temperature-dependent photoluminescence (TDPL) and excitation-power-dependent photoluminescence (PDPL). Two samples were compared: one had a thicker well (InGaN/GaN 3/5 nm); the other had a thicker barrier (InGaN/GaN 2/6 nm). It was found that the GaN barrier thickness in the InGaN/GaN MQWs plays an important role in determining the optical characteristics of the MQWs. The peak energy of the two samples varied with temperature in an S-shape. The thicker-barrier sample had a higher turning point from blueshift to redshift, indicating a stronger localization effect. From the Arrhenius plot of the normalized integrated PL intensity, it was found that the activation energy of the nonradiative process also increased with a thicker barrier thickness. The radiation recombination process was dominated in the sample of the thicker barrier, while the non-radiation process cannot be negligible in the sample of the thicker well. [ABSTRACT FROM AUTHOR]