Search

Peroxo-heteropoly compound PO4[W(O)(O2)2] was synthesized on calcium-deficient hydroxyapatite using a reaction of surface [HPO4]2− groups on hydroxyapatite with a Na2[W2O3(O2)4] aqueous solution. The vibration of [HPO4]2− at 875 cm−1 became very weak, and the vibration of the peroxo-oxygen bond [O–O]2− at 845 cm−1 appeared in the FT-IR spectrum of the solid product, indicating that PO4[W(O)(O2)2] was formed on the surface of hydroxyapatite. The formed solid sample was further reacted with PdCl2(PhCN)2 in an acetone solution to fix PdCl2 between the O sites on the hydroxyapatite. Elemental analyses proved that the resultant solid contained 1.2 wt.% Pd, implying that PdCl2 molecules were immobilized on the surface of hydroxyapatite. The hydroxyapatite-based hybrid compound containing Pd and PO4[W(O)(O2)2] was used as a heterogeneous catalyst in a methanol solvent for propylene epoxidation by molecular oxygen in an autoclave batch reaction system. A propylene conversion of 53.4% and a selectivity for propylene oxide of 88.7% were obtained over the solid catalyst after reaction at 363 K for 8 h. The novel catalyst could be reused by a simple centrifugal separation, and the yield of propylene oxide did not decrease after the reaction for five runs. By prolonging the reaction time to 13 h, the highest yield of propylene oxide at 363 K over the solid catalyst was obtained as 53.8%, which was almost the same as that of the homogeneous catalyst containing PdCl2(PhCN)2 and [(C6H13)4N]2{HPO4[W(O)(O2)2]2} for the propylene epoxidation. Methanol was used as a solvent as well as a reducing agent in the propylene epoxidation by molecular oxygen. Small particles of Pd metal were formed on the surface of the hybrid solid catalyst during the reaction, and acted as active species to achieve the catalytic turnover of PO4[W(O)(O2)2] in the propylene epoxidation by molecular oxygen in methanol. [ABSTRACT FROM AUTHOR]

Al-modified hexagonal mesoporous silica (HMS) materials were synthesized using dodecylamine as a template according to the methods reported in the literature. FT-IR spectra proved that Al3+ ions entered in the HMS framework in Al-HMS (prepared by sol-gel reaction) but Al3+ ions existed in the extra-framework in Al/HMS (prepared by post-modification). NH3-TPD indicated that either Al-HMS or Al/HMS had solid acid sites on the surface, and the acidic strength of Al/HMS was stronger than that of Al-HMS. For ethylene oligomerization at 200 °C under 1 MPa, Ni/Al-HMS showed an ethylene conversion of 96.3%, which was much higher than that over Ni/Al/HMS (45.6%). The selectivity for C4H8, C6H12, C8H16, and C8+ was 37.7%, 24.5%, 24.0%, and 9.1% for ethylene oligomerization over Ni/Al-HMS, respectively. Ni/Al-MCM-41, which has been reported as an effective catalyst for ethylene oligomerization in the literature, showed a high ethylene conversion (95.2%) similar to that of Ni/Al-HMS in this study. However, the selectivity for C8H16 over Ni/Al-MCM-41 (16.3%) was lower than that over Ni/Al-HMS (24.0%) in the ethylene oligomerization. For ethanol dehydration at 300 °C under 1 MPa, a commercial H-ZSM-5 catalyst showed a high ethylene yield (91.2%) after reaction for 24 h using a feed containing 90 wt.% ethanol and 10 wt.% water. In this study, a two-step process containing two fixed-bed reactors and one cold trap was designed to achieve the direct synthesis of higher olefins from bio-ethanol. The cold trap was used to collect the water formed from ethanol dehydration. By using H-ZSM-5 as a catalyst for ethanol dehydration in the first reactor and using Ni/Al-HMS as a catalyst for ethylene oligomerization in the second reactor, higher olefins were continuously formed by feeding a mixture containing 90 wt.% ethanol and 10 wt.% water. The yields of higher olefins did not decrease after reaction for 8 h in the two-step reaction system. [ABSTRACT FROM AUTHOR]

Peroxo-heteropoly compound PO 4 [W(O)(O 2 ) 2 ] was synthesized on calcium-deficient hydroxyapatite using a reaction of surface [HPO 4 ] 2- groups on hydroxyapatite with a Na 2 [W 2 O 3 (O 2 ) 4 ] aqueous solution. The vibration of [HPO 4 ] 2- at 875 cm -1 became very weak, and the vibration of the peroxo-oxygen bond [O-O] 2- at 845 cm -1 appeared in the FT-IR spectrum of the solid product, indicating that PO 4 [W(O)(O 2 ) 2 ] was formed on the surface of hydroxyapatite. The formed solid sample was further reacted with PdCl 2 (PhCN) 2 in an acetone solution to fix PdCl 2 between the O sites on the hydroxyapatite. Elemental analyses proved that the resultant solid contained 1.2 wt.% Pd, implying that PdCl 2 molecules were immobilized on the surface of hydroxyapatite. The hydroxyapatite-based hybrid compound containing Pd and PO 4 [W(O)(O 2 ) 2 ] was used as a heterogeneous catalyst in a methanol solvent for propylene epoxidation by molecular oxygen in an autoclave batch reaction system. A propylene conversion of 53.4% and a selectivity for propylene oxide of 88.7% were obtained over the solid catalyst after reaction at 363 K for 8 h. The novel catalyst could be reused by a simple centrifugal separation, and the yield of propylene oxide did not decrease after the reaction for five runs. By prolonging the reaction time to 13 h, the highest yield of propylene oxide at 363 K over the solid catalyst was obtained as 53.8%, which was almost the same as that of the homogeneous catalyst containing PdCl 2 (PhCN) 2 and [(C 6 H 13 ) 4 N] 2 {HPO 4 [W(O)(O 2 ) 2 ] 2 } for the propylene epoxidation. Methanol was used as a solvent as well as a reducing agent in the propylene epoxidation by molecular oxygen. Small particles of Pd metal were formed on the surface of the hybrid solid catalyst during the reaction, and acted as active species to achieve the catalytic turnover of PO 4 [W(O)(O 2 ) 2 ] in the propylene epoxidation by molecular oxygen in methanol.