Search

A comparative research on stability, viscosity (µ), and thermal conductivity (k) of carbon nanosphere (CNS) and carbon nanopowder (CNP) nanofluids was performed. CNS was synthesized by the hydrothermal method, while CNP was provided by the manufacturer. Stable nanofluids at high concentrations 0.5, 1.0, and 1.5 vol% were prepared successfully. The properties of CNS and CNP nanoparticles were analyzed with Fourier-transform infrared spectroscopy (FT-IR), scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), specific surface area (SBET), X-ray powder diffraction (XRD), thermogravimetry/differential thermal analysis (TG/DTA), and energy dispersive X-ray analysis (EDX). The CNP nanofluids have the highest k enhancement of 10.61% for 1.5 vol% concentration compared to the base fluid, while the CNS does not make the thermal conductivity of nanofluids (knf) significantly higher. The studied nanofluids were Newtonian. The relative µ of CNS and CNP nanofluids was 1.04 and 1.07 at 0.5 vol% concentration and 30 °C. These results can be explained by the different sizes and crystallinity of the used nanoparticles. [ABSTRACT FROM AUTHOR]

Nanofluids obtained from halloysite and de-ionized water (DI) were prepared by using surfactants and changing pH for heat-transfer applications. The halloysite nanotubes (HNTs) nanofluids were studied for several volume fractions (0.5, 1.0, and 1.5 vol%) and temperatures (20, 30, 40, 50, and 60 °C). The properties of HNTs were studied with a scanning electron microscope (SEM), energy-dispersive X-ray analysis (EDX), Fourier-transform infrared (FT-IR) spectroscopy, X-ray powder diffraction (XRD), Raman spectroscopy and thermogravimetry/differential thermal analysis (TG/DTA). The stability of the nanofluids was proven by zeta potentials measurements and visual observation. With surfactants, the HNT nanofluids had the highest thermal conductivity increment of 18.30% for 1.5 vol% concentration in comparison with the base fluid. The thermal conductivity enhancement of nanofluids containing surfactant was slightly higher than nanofluids with pH = 12. The prepared nanofluids were Newtonian. The viscosity enhancements of the nanofluid were 11% and 12.8% at 30 °C for 0.5% volume concentration with surfactants and at pH = 12, respectively. Empirical correlations of viscosity and thermal conductivity for these nanofluids were proposed for practical applications. [ABSTRACT FROM AUTHOR]

Effects of different reaction parameters in the hydrothermal synthesis of molybdenum oxides (MoO3) were investigated and monoclinic (β-) MoO3 was prepared hydrothermally for the first time. Various temperatures (90/210 °C, and as a novelty 240 °C) and durations (3/6 h) were used. At 240 °C, cetyltrimethylammonium bromide (CTAB) and CrCl3 additives were also tested. Both the reaction temperatures and durations played a significant role in the formation of the products. At 90 °C, h-MoO3 was obtained, while at 240 °C the orthorhombic (α-) MoO3 formed with hexagonal rod-like and nanofibrous morphology, respectively. The phase transformation between these two phases was observed at 210 °C. At this temperature, the 3 h reaction time resulted in the mixture of h- and α-MoO3, but 6 h led to pure α-MoO3. With CTAB the product was bare o-MoO3, however, when CrCl3 was applied, pure metastable m-MoO3 formed with the well-crystallized nanosheet morphology. The gas sensing of the MoO3 polymorphs was tested to H2, which was the first such gas sensing study in the case of m-WO3. Monoclinic MoO3 was found to be more sensitive in H2 sensing than o-MoO3. This initial gas sensing study indicates that m-MoO3 has promising gas sensing properties and this MoO3 polymorph is promising to be studied in detail in the future. [ABSTRACT FROM AUTHOR]

In this study, Bi2WO6 was prepared by the hydrothermal method. The effects of reaction temperature (150/170/200 °C) and reaction time (6/12/24 h) were investigated. The role of strongly acidic pH (1 >) and the full range between 0.3 and 13.5 were studied first. Every sample was studied by XRD and SEM; furthermore, the Bi2WO6 samples prepared at different temperatures were examined in detail by EDX and TEM, as well as FT-IR, Raman and UV-vis spectroscopies. It was found that changing the temperature and time slightly influenced the crystallinity and morphology of the products. The most crystallized product formed at 200 °C, 24 h. The pure, sheet-like Bi2WO6, prepared at 200 °C, 24 h, and 0.3 pH, gradually transformed into a mixture of Bi2WO6 and Bi3.84W0.16O6.24 with increasing pH. The nanosheets turned into a morphology of mixed shapes in the acidic range (fibers, sheets, irregular forms), and became homogenous cube- and octahedral-like shapes in the alkaline range. Their band gaps were calculated and were found to vary between 2.66 and 2.59 eV as the temperature increased. The specific surface area measurements revealed that reducing the temperature favors the formation of a larger surface area (35.8/26/21.6 m2/g belonging to 150/170/200 °C, respectively). [ABSTRACT FROM AUTHOR]

In this study, Bi 2 WO 6 was prepared by the hydrothermal method. The effects of reaction temperature (150/170/200 °C) and reaction time (6/12/24 h) were investigated. The role of strongly acidic pH (1 >) and the full range between 0.3 and 13.5 were studied first. Every sample was studied by XRD and SEM; furthermore, the Bi 2 WO 6 samples prepared at different temperatures were examined in detail by EDX and TEM, as well as FT-IR, Raman and UV-vis spectroscopies. It was found that changing the temperature and time slightly influenced the crystallinity and morphology of the products. The most crystallized product formed at 200 °C, 24 h. The pure, sheet-like Bi 2 WO 6 , prepared at 200 °C, 24 h, and 0.3 pH, gradually transformed into a mixture of Bi 2 WO 6 and Bi 3.84 W 0.16 O 6.24 with increasing pH. The nanosheets turned into a morphology of mixed shapes in the acidic range (fibers, sheets, irregular forms), and became homogenous cube- and octahedral-like shapes in the alkaline range. Their band gaps were calculated and were found to vary between 2.66 and 2.59 eV as the temperature increased. The specific surface area measurements revealed that reducing the temperature favors the formation of a larger surface area (35.8/26/21.6 m 2 /g belonging to 150/170/200 °C, respectively).