Search

The wide application of magnesium alloys as biodegradable implant materials is limited because of their fast degradation rate. Hydroxyapatite (HA) coating can reduce the degradation rate of Mg alloys and improve the biological activity of Mg alloys, and has the ability of bone induction and bone conduction. The preparation of HA coating on the surface of degradable Mg alloys can improve the existing problems, to a certain extent. This paper reviewed different preparation methods of HA coatings on biodegradable Mg alloys, and their effects on magnesium alloys' degradation, biocompatibility, and osteogenic properties. However, no coating prepared can meet the above requirements. There was a lack of systematic research on the degradation of coating samples in vivo, and the osteogenic performance. Therefore, future research can focus on combining existing coating preparation technology and complementary advantages to develop new coating preparation techniques, to obtain more balanced coatings. Second, further study on the metabolic mechanism of HA-coated Mg alloys in vivo can help to predict its degradation behavior, and finally achieve controllable degradation, and further promote the study of the osteogenic effect of HA-coated Mg alloys in vivo. [ABSTRACT FROM AUTHOR]

Here, we elucidate the significant impact of carbon nanotubes (CNTs) on the electrochemical behavior of Mg-based amorphous composite materials that were reinforced with CNTs while using pressure die casting. The addition of 3 vol % CNTs led to an increase in the compressive strength of Mg-based amorphous material from 812 MPa to 1007 MPa, and the fracture strain from 1.91% to 2.67% in the composite. Interestingly, the addition of CNTs significantly contributed to the enhancement of corrosion resistance of Mg-based glass by ~30%. The superior mechanical properties are primarily related to the fact that the addition of CNTs hindered the growth of shear bands (cracks), while the high corrosion resistance is related to inferior wettability and the bridging effect between adherent corrosive oxide film and the matrix that provided enhanced corrosion resistance. [ABSTRACT FROM AUTHOR]

Herein, the influence of inter-pass cooling (IC) and conventional two-stage rolling (CTR), on microstructural evolution and plastic deformation behavior of ultra-heavy EH47 plates, is demonstrated. It is reported that the deformation amount and deformation rate, in every deformation pass during rough rolling, at 1/4- and 1/2-thickness of IC steel were higher than the CTR steel. The volume fraction of ferrite and acicular ferrite was 45% and 18%, at 1/4-thickness, and 35% and 50% at 1/2-thickness of IC steel, respectively, whereas the sum of both ferrite phases was smaller than 25% in the CTR steel. The austenite grain boundary area and high-angle grain boundary fraction in the IC steel were higher than the CTR steel. The high density of fine and shapeless pearlite has been observed in IC steel, whereas large-size carbides, with hexagonal structure, have been observed in CTR steel. Compared to the CTR steel, the density of precipitates was apparently lower in IC steel. Two kinds of Nb containing precipitates, such as (Ti, Nb)(C, N) and (Nb, Ti)C, were observed in the tested steels. Total ductility and uniform elongation of the IC steel were higher than the CTR steel. During the tensile process, the crack initiation energy and crack propagation energy of the IC steel were higher than the CTR steel. Moreover, the volume fraction of retained austenite (FCC) was reduced from 7.71% to 0.42% near the tensile fracture in IC steel at 1/4-thickness. In additon, the strain of synergetic plastic deformation of the IC steel was higher than the CTR steel. Meanwhile, compared to the CTR steel, the synergetic plastic deformation of the IC steel occurred at low stress after the yield point, which can be ascribed to the presence of fewer microcracks in the IC steel. Hence, a delayed fracture has been observed in the IC steel plate. [ABSTRACT FROM AUTHOR]

We elucidate here the determining role of Nb interlayer on mechanical properties of Ti/steel clad plate fabricated by vacuum rolling cladding (VRC) as a function of different heating temperatures. A critical analysis on the clad interface via electron probe micro-analyzer, X-ray diffractometer and shear testing were conducted to investigate the influence of TiC, Fe-Nb and TiFe compounds and Nb-Ti solid solution on microstructural evolution and shear properties of Ti/steel clad plate. The inter-diffusion between Ti, C and Fe was effectively restrained by adding the Nb interlayer at heating temperature of 800 °C, and average shear strength of 279 MPa was achieved. With increase of heating temperature, Nb-Ti solid solution was formed at the Ti/Nb interface, which reduced mechanical properties of clad plate at 900 °C. At 1000 °C, TiC and Nb-Fe compounds and Nb-Ti solid solution were formed at the interface, and minimum average shear strength of 152 MPa was achieved. The detailed analysis on the clad interface suggested that ideal shear strength can be obtained through the addition of Nb interlayer and selecting appropriate heating temperature. [ABSTRACT FROM AUTHOR]

In this study, the impact of different surface treatment and degree of vacuum on the interface and mechanical properties of 304/Q345 stainless steel clad plate was investigated. The study indicated that more continuous or aggregated Al2O3 and Si-Mn composite oxides were formed at the interface after brush grinding. However, less inclusions such as Al2O3, MnS and Ca-Mg-Al-Si composite oxides were formed at the interface after pickling treatment. For the vacuum degrees of 10−2 Pa, 1 Pa and 105 Pa, the oxidation reaction became more intense with the decrease in vacuum degree. The interface inclusions were gradually changed from Al2O3 and Si-Mn complex oxides to oxide scale and MnCr2O4 spinel oxide. The interfacial bonding strength of stainless steel clad plate was improved with the increase in degree of vacuum. The bonding strength was 55 MPa at vacuum of 105 Pa, but it was 484 MPa at vacuum of 10−2 Pa, which is far greater than that of the national standard, and an excellent performance was obtained. [ABSTRACT FROM AUTHOR]