In this work, a highly alloyed cold work tool steel, Uddeholm Vanadis 4 Extra, was manufactured via the electron beam melting (EBM) technique. The corresponding material microstructure and carbide precipitation behavior as well as the microstructural changes after heat treatment were characterized, and key mechanical properties were investigated. In the as-built condition, the microstructure consists of a discontinuous network of very fine primary Mo- and V-rich carbides dispersed in an auto-tempered martensite matrix together with ≈15% of retained austenite. Adjusted heat treatment procedures allowed optimizing the microstructure by the elimination of Mo-rich carbides and the precipitation of fine and different sized V-rich carbides, along with a decrease in the retained austenite content below 2%. Hardness response, compressive strength, and abrasive wear properties of the EBM-manufactured material are similar or superior to its as-HIP forged counterparts manufactured using traditional powder metallurgy route. In the material as built by EBM, an impact toughness of 16–17 J was achieved. Hot isostatic pressing (HIP) was applied in order to further increase ductility and to investigate its impact upon the microstructure and properties of the material. After HIPing with optimized protocols, the ductility increased over 20 J. [ABSTRACT FROM AUTHOR]

Electron beam melting (EBM) is currently hampered by the low number of materials available for processing. This work presents an experimental study of process parameter development related to EBM processing of stainless steel alloy 316LN. Area energy (AE) input and beam deflection rate were varied to produce a wide array of samples in order to determine which combination of process parameters produced dense (>99%) material. Both microstructure and tensile properties were studied. The aim was to determine a process window which results in dense material. The range of AE which produced dense materials was found to be wider for 316LN than for many other reported materials, especially at lower beam deflection rates. Tensile and microstructural analysis showed that increasing the beam deflection rate, and consequently lowering the AE, resulted in material with a smaller grain size, lower ductility, lower yield strength, and a narrower window for producing material that is neither porous nor swelling. [ABSTRACT FROM AUTHOR]