Search

Conducting polymers integrated with metal oxides create opportunities for hybrid capacitive electrodes. In this work, we report a one-pot oxidative polymerization for the synthesis of integrated conductive polyindole/nickel oxide (PIn/NiO), polyindole/zinc oxide (PIn/ZnO), and polyindole/nickel oxide/zinc oxide (PNZ). The polymers were analyzed thoroughly for their composition and physical as well as chemical properties by X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), ultraviolet–visible spectroscopy (UV–Vis), and thermogravimetric analysis (TGA). The PIn and its composites were processed into electrodes, and their use in symmetrical supercapacitors in two- and three-electrode setups was evaluated by cyclic voltammetry (CV), galvanostatic discharge (GCD), and electrochemical impedance spectroscopy (EIS). The best electrochemical charge storage capability was found for the ternary PNZ composite. The high performance directly correlates with its uniformly shaped nanofibrous structure and high crystallinity. For instance, the symmetrical supercapacitor fabricated with PNZ hybrid electrodes shows a high specific capacitance of 310.9 F g−1 at 0.5 A g−1 with an energy density of 42.1 Wh kg−1, a power density of 13.2 kW kg−1, and a good cycling stability of 78.5% after 5000 cycles. This report presents new electrode materials for advanced supercapacitor technology based on these results.

Water pollution caused by industrial wastes containing heavy metals and dyes is a major environmental problem. This study reports on the synthesis, characterization, and utilizations of Polyaniline (PANI) and its composites with Fe3O4 for the removal of hexavalent chromium Cr(VI) and divalent nickel Ni(II) ions from water. The adsorption data were fitted in Freudlich, Langmuir, Tempkin, Dubbanin&ndash, Ruddishkawich (D&ndash, R), and Elovich adsorption isotherms. The Freundlich isotherm fits more closely to the adsorption data with R2 values of 0.9472, 0.9890, and 0.9684 for adsorption of Cr(VI) on Fe3O4, PANI, and PANI/Fe3O4 composites, respectively, while for adsorption of Ni(II) these values were 0.9366, 0.9232, and 0.9307 respectively. The effects of solution pH, initial concentration, contact time, ionic strength, and adsorbent dosage on adsorption behavior were investigated. The adsorption ability of composites was compared with pristine PANI and Fe3O4 particles. Activation energy and other thermodynamic properties such as changes in enthalpy, entropy, and Gibbs free energy indicated spontaneous and exothermic adsorption.

An eco-friendly solid-state symmetric ultracapacitor (Uc) device was fabricated using a polyaniline graphene oxide composite co-doped with sulfuric acid (H2SO4) and dodecyl benzene sulfonic acid (DBSA) or camphor sulfonic acid (CSA), as electrode material utilizing gold sheets as current collectors. The device showed specific capacitance value of 150 F/g at 1 A/g current density, with a capacitance retention value of 93.33% at higher current density (10 A/g), indicating a high rate capability. An energy density of 15.30 Whkg−1 with a power density of 1716 Wkg−1 was obtained at the current density of 1 A/g. The values of areal capacitance, power density, and energy density, achieved at the current density of 5 mAcm−2, were 97.38 mFcm−2, 9.93 mWhcm−2, and 1.1 Wcm−2, respectively. Additionally, the device showed very low solution and charge transfer resistance (0.885 Ω and 0.475 Ω, respectively). A device was also fabricated utilizing copper as current collector; however, a lower value of specific capacitance (82 F/g) was observed in this case.

The use of electroactive polyaniline (PANI) as an electrode material for a symmetric supercapacitor has been reported. The material was synthesized via interfacial polymerization, using ammonium per sulfate, dodecylbenzene sulfonic acid (DBSA), and gasoline, respectively, in the oxidant, dopant, and novel organic phase, and was subsequently employed as an electrode material to design a binder-free symmetric capacitor. As properties of PANI rely on the method of synthesis as well as reaction parameters, the present combination of reactants, at pre-optimized conditions, in the interfacial polymerization, led to the formation of PANI exhibiting a high specific capacitance (712 Fg&minus, 1 at 0.5 Ag&minus, 1), a good rate capability (86% capacitance retention at 10 Ag&minus, 1), a very low solution resistance (Rs = 0.61 &Omega, ), and a potential drop (IR = 0.01917 V). The device exhibited a high energy density of 28 Whkg&minus, 1, at a power density of 0.28 kWkg&minus, 1, and retained as high as 15.1 Whkg&minus, 1, at a high power density of 4.5 kWkg&minus, 1. Moreover, it showed an excellent cycling stability and retained 98.5% of coulombic efficiency after 5000 charge discharge cycles, without showing any signs of degradation of polymer.