This paper presents the results of atom probe tomography studies on radiation-induced phase formation in light-water reactor pressure vessel steels after neutron irradiation under various conditions in comparison with the literature data. The given irradiation conditions are fluence (10–100) × 1022 m−2, flux (5–2700) × 1014 m−2s−1 and irradiation temperature (50–400) °C. The composition of the studied steels varies in a wide range for the elements significantly affecting radiation and thermal resistance of steels: Ni in the range of 0.2–6.0 wt.%, Mn–0.03–1.1 wt.%, Cu–0.01–0.16 wt.%, and P–0.01–0.03 wt.%. The number density, volume fraction, size, composition, and nucleation sites of precipitates are determined. The regularities of the effect of various operational factors on the phase formation in these steels have been analyzed and revealed. The study shows that in materials with high copper content, Cu-rich precipitates are formed by a radiation-enhanced mechanism. In materials with low copper content, their formation upon irradiation at 300 °C occurs by a radiation-induced mechanism since the main nucleation sites are point defect clusters formed in cascades. At the same time, the density, volume fraction, and composition of the precipitates depend on the steel composition (Ni and Mn content). In the steel with increased Ni content up to 5 wt.% but with ultra-low Mn content ≤ 0.03 wt.%, it is possible to suppress the formation of Ni-Si-Mn precipitates under irradiation. [ABSTRACT FROM AUTHOR]

The existing knowledge about the effect of neutron irradiation on the mechanical properties of reactor pressure vessel steels under reactor service conditions relies to a large extent on accelerated irradiations realized by exposing steel samples to a higher neutron flux. A deep understanding of flux effects is, therefore, vital for gaining service-relevant insight into the mechanical property degradation. The existing studies on flux effects often suffer from incomplete descriptions of the irradiation-induced microstructure. Our study aims to give a detailed picture of irradiation-induced nanofeatures by applying complementary methods using atom probe tomography, positron annihilation, small-angle neutron scattering and transmission electron microscopy. The characteristics of the irradiation-induced nanofeatures and the dominant factors responsible for the observed increase of Vickers hardness are identified. Microstructural changes due to high flux conditions are smaller nm-sized solute atom clusters with almost the same volume fraction and a higher concentration of vacancies and sub-nm vacancy clusters compared to low flux conditions. The results rationalize why pronounced flux effects on the nanofeatures, in particular on solute atom clusters, only give rise to small or moderate flux effects on hardening. [ABSTRACT FROM AUTHOR]