The Al-Si alloy prepared by the traditional powder metallurgy method has the problems of difficult sintering and low mechanical properties. In this paper, rotary extrusion combined with rapid solidification/powder metallurgy technology (RS/PM) is proposed and designed to produce an Al-10Si alloy. In subsequent sintering at different temperatures, better metallurgical bonding between particles can be achieved to fulfil the aim of improving the mechanical properties of the material. Additionally, the continuous preparation of materials can be achieved. Finally, it is verified that the density of the Al-10Si alloy sintered at 525 °C is 2.61 g/cm3, reaching 97.0% of the theoretical density, and the tensile strength reaches 336 MPa, which is much higher than that of the alloy prepared by the traditional casting method and powder metallurgy method.

Based on previous work, where Al-Si-Cu-Ni alloy was successfully manufactured by laser powder bed fusion (PBF-LB/M) technology, in this study, we further observe the microstructure of the alloy, analyze the formation mechanism of the microstructure during solidification, and discuss their implications for the mechanical properties. The results indicate that the microstructure comprises multi-level cellular heterogeneous structures, with an α-Al matrix in the interior of the cellular structure and Cu- and Ni-rich phases clustered at the boundaries, intertwined with the silicon network. During solidification, α-Al solidifies first and occupies the core of the cells, while Si phases and Cu- and Ni-rich phases deposit along the cellular boundaries under the influence of surface tension. During the solidification process of cellular boundaries, influenced by spinodal decomposition and lattice spacing, Si phases and Cu- and Ni-rich phases interconnect and distribute crosswise, collectively forming multi-level cellular structures. The refined cellular microstructure of the PBF-LB/M Al-Si-Cu-Ni alloy enhances the mechanical properties of the alloy. The alloy exhibits a bending strength of 766 ± 30 MPa, a tensile strength and yield strength of 437 ± 6 MPa and 344 ± 4 MPa, respectively, with a relatively low fracture elongation of approximately 1.51 ± 0.07%. Subsequent improvement can be achieved through appropriate heat treatment processes.

The goal of the fluidity test is to evaluate the ability of the melt to fill the cavity of the mold, which is one of the factors affecting the final quality of the castings. It is a technological test that is basically not standardized, therefore it is realized in different forms, for example using “horizontal” and “vertical” molds. The “horizontal” mold makes it easier to fulfill the condition of repeatability, therefore it was used to calculate the capability of the test by the Measurement Systems Analysis (MSA) method. The results of the tests in both molds were used to calculate regression equations that allow the fluidity to be determined with strong reliability based on variables such as melt temperature, casting speed, and mold temperature. In addition, the effects of input data variability (uncertainty) on the resulting fluidity value were analyzed using regression equations and the Monte Carlo simulation. The contribution of the article is the analysis of the capability of the measurement process of the fluidity and a prediction of the results of its tests using the Monte Carlo simulation method.

Unmodified hypoeutectic silumins have a microstructure composed of large-sized phases, which are the reason for their low mechanical properties. Many years of research have shown the modifying effects of many chemical elements and their compounds, including the master alloy consisting of Al-Ti-B, often in the form of the finished AlTi5B alloy. In this work, it was decided to check how the proportions of Ti and B content in the Al or AlSi-based master alloy affect the microstructure and mechanical properties of a hypoeutectic silumin, AlSi7Mg. It has been shown that a master alloy containing silicon (with the participation of Al + Ti + B) has a more effective impact on the refinement of the microstructure, and thus an increase in the mechanical properties of the AlSi7Mg alloy, than a master alloy without silicon. It has been shown that the ratio of titanium to boron content in the very-often-used AlTi5B modifier is not always optimal. It has been shown that the use of a master alloy with a composition similar to that of modified silumin with titanium and boron in a 2:1 ratio allows the obtaining of an AlSi7Mg alloy with higher mechanical properties than the alloy after the modification of the AlTi5 master alloy.

The effects of Fe, Cr and thermal exposure on the microstructure and mechanical properties of Al-Si alloy were investigated in this work. The results indicated that the main phases of the Al-Si-Cu-Ni-Mg-(0.6–0.9%) Fe (wt. %) alloy were α-Al, Si, Al5Cu2Mg8Si6, Al3CuNi, Al7Cu4Ni, Al2Cu, and AlFeSi at room temperature. The size of the AlSiFe phase increased with increasing the weight fraction of Fe. The shape of Fe-rich phase changed from rod-like to star-like, followed by long needle-like with Fe varying from 0.6% to 0.9%. The mechanical properties of the studied alloys at elevated temperatures increased with Fe. The ultimate tensile strength of the three alloys at 350 °C was 111.2 MPa, 124 MPa, and 128.7 MPa, respectively. In addition, the ductility and strength of the studied alloys at room temperature decreased with increasing the Fe, due to the large size of the hard and brittle Fe-rich phase strictly cleaved the aluminum matrix. After thermal exposure, the properties of the alloy at room temperature and elevated temperature decreased obviously at the beginning of 0.5~8 h, and then tend to be stabilized during thermal exposure at 350 °C for approximately 32~64 h. Fe-rich was a thermal stable phase at 350 °C.

AlSi12(Fe), AlSi10Mg(Fe), AlSi10MnMg, and AlMg4Fe2 die-casting alloys were produced by high-pressure die casting (HPDC) and vacuum-assisted high-pressure die casting (VADC) under a vacuum level of 200 mbar. The chemical composition, hardness, gas and shrinkage porosity, and mechanical properties were analyzed. The parts under study were subjected to a T6 heat treatment. The VADC led to a decrease in the percentage of defects in the as-cast state for all the alloys, due to a reduction in the amount of gas porosities. After heat treatment, the quantity of gas and shrinkage porosities increased. The efficiency and level of vacuum used were not sufficient to improve the mechanical properties in the as-cast state. The ductility of AlSi10Mg(Fe) and AlSi10MnMg alloys was improved after heat treatment; however, the YS and UTS of AlSi10Mg(Fe) did not increase. The primary aluminum alloys presented higher elongation values than the secondary aluminum alloys due to the reduced amount of the needle-like β-Al5FeSi phase.

The physical and mechanical properties of an entirely (wrought alloys) or partly (cast alloys) dendritically solidified alloy strongly depend on the secondary dendrite arm spacing (SDAS). The casting practice and the simulation of solidification need a usable but simple method to calculate the SDAS during and at the end of solidification as a function of the cooling rate. Based on many solidification experiments, a simple equation to calculate the SDAS (empirical method) is known to use the local solidification time, which can be obtained from the measured cooling curves (equiaxed solidification), or can be calculated from the temperature gradient and front velocity (directional solidification). This equation is not usable for calculating the SDAS during solidification. Kirkwood developed a semi-empirical method based on the liquid phase’s diffusion, which contains only one geometric factor that seems constant for different alloys. This equation contains some physical parameters that depend on the temperature, so the equation cannot be integral in closed form. In the present work, first, we show the effect of the curvature of the solid/liquid interface on the equilibrium concentrations and then the different processes of SDA coarsening. In our earlier paper, we demonstrated that using the empirical method, the final SDAS can be calculated with acceptable correctness in the case of four unidirectional solidification experiments of Al-7wt%Si alloy. The present work shows that numerically integrated Kirkwood’s equations used the known cooling curve; the SDAS can be calculated at the end and during solidification in good agreement with these experimental results. Compared to the two calculation methods, we stated that the correctness of the methods is similar. Still, the results of the solidification simulation (the microsegregation) will be more correct using the dynamical method. It is also shown that with the dynamical method, the SDAS can be calculated from any type of cooling curve, and using the dynamical method, it is proved that some different SDASs could belong to the same local solidification time.

This study fabricated a thixoformed Al-7% Si alloy using the cooling slope technique and subjected it to heat treatment before processing with severe plastic deformation to determine the effect of this combination method on the microstructure refinement and hardness of Al-Si alloys (300 Series). Each as-cast and thixoformed Al-Si alloy sample was subjected to equal-channel angular pressing (ECAP) and high-pressure torsion (HPT) individually at room temperature before and after heat treatment. ECAP was conducted in a mould with a 120° channel angle via route A, and HPT was applied with 0.75 and 5 turns. The heat-treated thixoformed Al-Si alloy subjected to the HPT process had an ultra-fine grain microstructure and showed a fine and homogeneous redistribution of the eutectic phase in the Al matrix. For the as-cast alloy, the hardness of the heat-treated thixoformed Al-7% Si alloy increased from 63 HV to 124 and 215 Hv after two ECAP passes and five turns of HPT due to the reduced and redistributed eutectic phase in the Al matrix. Subjecting the Al-7% Si alloy to a combination of semisolid and heat treatment processes before subjecting it to severe plastic deformation resulted in microstructural refinement and improved the hardness of the Al-Si alloy. The results indicate that HPT is a more effective method than ECAP for increasing the hardness of the thixoformed Al-Si alloy due to microstructure refinement.

Fabrication condition greatly influences the microstructures and properties of Al alloys. However, most of the available reports focus on a single fabrication technique, indicating there is still a lack of systematic comparisons among wider ranges of fabrication methods. In this paper, with conventional casting (via sand/Fe/Cu mold) and additive manufacturing (AM, via selective laser melting, SLM) methods, the effects of cooling rate (Ṫ) on the microstructures and mechanical properties of hypoeutectic Al-10Si-0.5Mg alloy are systematically investigated. The results show that with increasing cooling rate from sand-mold condition to SLM condition, the grain size (d) is continuously refined from ~3522 ± 668 μm to ~10 μm, and the grain morphology is gradually refined from coarse dendrites to a mixed grain structure composed of columnar plus fine grains (~10 μm). The eutectic Si particles are effectively refined from blocky shape under sand/Fe-mold conditions to needle-like under Cu-mold conditions, and finally to fine fibrous network under SLM condition. The tensile yield strength and elongation is greatly improved from 125 ± 5 MPa (sand-mold) to 262 ± 3 MPa (SLM) and from 0.8 ± 0.2% (sand-mold) to 4.0 ± 0.2% (SLM), respectively. The strengthening mechanism is discussed, which is mainly ascribed to the continuous refinement of grains and Si particles and an increase in super-saturation of Al matrix with increasing cooling rate.

Al-Si alloys exhibit promising wear resistance, thus being mainly employed to weld Al alloy parts and processed into components of equipment. During the new continuous casting direct rolling (CCDR) process, the raw material gradually cools and solidifies, simultaneously plastically deformed. Hence, the materials manufactured through the CCDR process presented an unparalleled microstructure. The experimental results indicated that the strength of the CCDR Al-Si alloy can be increased through cold rolling. A two-stage heat treatment (solid solution and aging treatment) was introduced to improve the ductility and satisfy the industrial application. Furthermore, the erosion wear characteristics and fracture mechanism of the CCDR Al-Si alloy dominated by the ductility were confirmed. Both cold rolling specimens (FR) and those with heat treatment (FRH) showed greater wear resistance than as-manufactured (F). The FR specimens exhibited greater wear resistance owing to a higher Al matrix strength at a lower impact angle; on the other hand, at a higher impact angle, the FRH specimens with a softer Al matrix presented better wear resistance due to the formation of a lip structure to reduce material removal. The TEM results confirmed that the nanoscale grains formation was induced in the erosion-affected region and affected the Si concentration. Conclusively, the heat-treated CCDR Al-Si alloy possessed excellent erosion resistance and workability, which can serve as a reference processed as wear-resistant mechanical parts.

Cooling rate plays a critical role in determining the thermal conductivity of Al-Si alloys. Although the effect of morphology and size of Si (changed by heat treatment) on its thermal conductivity has been investigated, the effect of cooling rates on thermal conductivity has not been well studied. In this study, we investigated the microstructure of an Al-8Si (with and without modification by Strontium (Sr)) alloy with cooling rates from 46.2 °C/s to 234 °C/s. It was found that the effect of cooling rate on thermal conductivity of Sr modification and Sr-free samples are opposite from each other. As a result, while the cooling rate increased from 46.2 °C/s to 234 °C/s, the calculated thermal conductivity increased from 145.3 MS/m to 151.5 MS/m for Sr-free Al-8Si alloy, and the calculated thermal conductivity was reduced from 187.5 MS/m to 176.7 MS/m for the Sr-modified Al-8Si alloy. By discussing how thermal conductivity correlates with eutectic silicon morphology and secondary dendrite arm spacing, the relationship between cooling rate and thermal conductivity were explained. This work suggests a new design strategy for improving the thermal conductivity of Al-Si hypoeutectic alloys.

The microstructure of the Si phase in Al-20Si alloys solidified under high pressure was investigated. The results demonstrate that the morphology of Si phase transformed (bulk→short rod→long needle) with the increase of superheat temperature under high pressure. At a pressure of 3 GPa and a superheat temperature of 100 K, a microstructure with a uniform distribution of fine Si phases on the α-Al matrix was obtained in the Al-20Si alloy. In addition, a mathematical model was developed to analyze the spacing variation of the lamellar Al-Si eutectics under the effect of pressure. The lamellar Al-Si eutectics appeared at 2 GPa and superheat temperatures of 70–150 K, and at 3 GPa and superheat temperatures of 140–200 K. With the increase of pressure from 2 GPa to 3 GPa, the average spacing of lamellar Al-Si eutectics decreased from 1.2–1.6 μm to 0.9–1.1 μm. In binary alloys, the effect of pressure on the eutectic spacing is related to the volume change of the solute phase from liquid to solid. When the volume change of the solute phase from liquid to solid is negative, the lamellar eutectic spacing decreases with increasing pressure. When it is positive, the eutectic spacing increases with increasing pressure.

In this paper, the effects of size, morphology and distribution of eutectic silicon on the thermal conductivity of Al-8Si alloy modified by Sr (0.04, 0.08, 0.12 wt.%) and Sb (0.1, 0.3, 0.5 wt.%) elements with T6 heat treatment were investigated. The results show that the modified fibrous eutectic silicon has a significant capability of improvement of thermal conductivity, while the amount of the modifier has a relatively weak effect on thermal conductivity. After T6 treatment, the fracture or spheroidization of the flake eutectic silicon and the disappearance of clustering phenomenon could raise thermal conductivity, but the coarsening of fibrous eutectic silicon is inconducive to thermal conductivity. Finally, the effect of eutectic silicon on electron transport is analyzed in detail, which could provide a reference for enhancing the thermal (or electrical) conductivity of hypoeutectic Al-Si alloy through effective microstructure control.

The present study investigated the effect of the casting conditions for the reduced pressure test (RPT) on the melt quality of Al-Si alloy. The casting conditions considered in RPT were the atmospheric exposure during melting, sampling method, and mold pre-heating temperature. Density Index (DI) was measured to quantify the melt quality of the Al-Si alloy casted with the different casting conditions for the RPT. The sample with blocking atmospheric exposure during melting was 5.6% lower in DI than the one without blocking. DI showed a 1.9% gap between scooping-out and pouring sampling methods. Increasing mold pre-heating temperature from 100 °C to 250 °C increased the DI of the alloy from 8.5% to 18.7%. On the other hand, when the mold pre-heating temperature was 350 °C, the DI of the alloy dropped sharply to 0.9%. The melt quality of the alloys was analyzed by measuring the pores and microstructure and simulating the solidification of the samples. It was presumed that the oxides and inclusions in the molten alloys caused the difference in DI according to the atmospheric exposure and the sampling method. The difference in DI according to the mold pre-heating temperature could be understood by calculating the solidification starting time and hydrogen diffusion coefficient during the solidification of the alloys in RPT.

Compound casting has received a great deal of attention as a useful method for fabricating a single complicated part from dissimilar metallic materials. For example, in the case of automobile cylinder blocks, research is being carried out to compound cast iron with aluminum alloys. In order to manufacture such as composite parts, it is essential to control the intermetallic compound formed at the interface between two metals. In this research, the type and growth behavior of compounds formed at the interface between cast iron and aluminum, or Al–Si alloy, were investigated. It was observed that the Al5Fe2 phase was mainly formed at the interface between the pure aluminum melt and the solid cast iron, and the thickness of the interfacial compound increased proportionally with increasing contact time. On the other hand, more complex phases were formed at the interface between the Al–Si alloy melt and the solid cast iron. In the case of a specimen having a contact time of 10 min, Al4.5FeSi, Al8Fe2Si and Al5Fe2 phases appeared to occupy the largest portion of the interfacial compound region. The total thickness of the interfacial compounds also increased in proportion to the contact time.

Aluminum composites reinforced with ceramic whiskers exhibited a unique combination of high specific strength and superior specific modulus. A 20 vol.% Si3N4w/Al-11.5Si-1.0Mg-0.5Cu-0.5Ni (wt.%) composite was fabricated via squeeze casting in the present study. It was observed that the addition of silicon nitride (Si3N4) whiskers in the Al-Si cast alloy promoted extensive twinning in the eutectic silicon particles due to a coupled role of thermal stresses between the matrix and silicon and residual stresses present in the composite. Double aging peaks were present in the age-hardening curves. The precipitation mechanism involved the formation of Mg2Si and Al2CuMg phases. The presence of Si3N4 whiskers in the composite retarded the nucleation process of Mg2Si precipitate while enhancing its growth rate.

In this paper, the relationship between the liquid structure and the corresponding solidified microstructure of an Al-Si-Mg-P alloy was studied. Experimental results show that Mg can reduce the phosphorous-modification effect if it was added after adding Al-P alloy. However, when it is added before adding Al-P alloy, Mg has no effect on the phosphorous-modification. It is considered that the difference in liquid structure induced by changing the adding order of Mg should be responsible for the above phenomenon, and was investigated by ab initio molecular dynamics simulation (AIMD). It was believed that the high-active Mg atoms could bond P atoms to form P-Mg clusters and then reduce the modification effect of AlP, when pure Mg was added into the prepared Al-Si-P melt. When the pure Mg was added into Al-Si melt before adding Al-P alloy, the Mg atoms would be first occupied by Si atoms to form Mg-Si clusters, and thus lose the ability to eliminate P-Al clusters which dissolve into melt later, leading to a good phosphorous-modification effect.

The role of the roll separating force in the high-speed twin-roll casting of aluminum alloys was examined. In horizontal-type twin-roll casting, as the casting speed increased upon decreasing the roll separating force, the strip texture changed from a shear and rolling texture to a random texture. Direct temperature measurements during high-speed twin-roll casting showed that the roll separating force played a significant role in maintaining a good contact between the strip and the roll surface. This resulted in a high cooling rate around the roll nip and enabled the fabrication of a sound strip with a fine microstructure. Moreover, the high casting speed and lowered roll separating force gave a band structure consisting of fine globular grains in the mid-thickness region of the strip, which could be considered beneficial in the formation of a well-dispersed center segregation.

Proper understanding and knowledge of primary particle or grain size is of paramount importance in manufacturing processes as it directly affects various properties including mechanical behavior. Application of optical microscopy coupled with etching techniques has been used conventionally and in conjunction with color metallography (polarized microscopy) has been the preferred method for grain size measurement. An advanced technique as an alternative to light microscopy is using electron backscatter diffraction (EBSD). A comparison is made between these two techniques using Al-7Si alloy produced with various casting techniques to highlight the cost and time of the sample preparation and analysis for both techniques. Results showed that color metallography is certainly a faster technique with great accuracy and a much cheaper alternative in comparison with EBSD.

High energy mechanical milling followed by hot-pressing consolidation has been used to produce nanostructured Al–5 wt %Si alloy. X-ray diffraction (XRD), scanning electron microscopy equipped with energy dispersive X-ray detector (SEM-EDX), Vickers hardness, and compression measurements were used to examine the effect of milling duration on microstructure and mechanical properties of the nanostructured consolidated alloys. Crystallite sizes and lattice strains were determined by X-ray peak broadening analysis using the Williamson-Hall (W-H) method. Increasing the milling time reduced the crystallite size, and the minimum crystallite size of about 33 nm was achieved for both consolidated and powdered samples after 50 h of milling. Based on the SEM-EDX observations, the best distribution of silicon into Al matrix was obtained after 20 h of milling and remained unchanged afterwards. Hardness of both consolidated and powder samples increased with milling time, which can be attributed to the reduction of crystallite size and the better distribution of silicon in the aluminum matrix. Similarly, increased milling time increased the yield and compressive strengths of consolidated samples.