Search

Hematite (α-Fe2O3) is one of the most promising and widely used semiconductors for application in photoelectrochemical (PEC) water splitting, owing to its moderate bandgap in the visible spectrum and earth abundance. However, α-Fe2O3 is limited by short hole-diffusion lengths. Ultrathin α-Fe2O3 films are often used to limit the distance required for hole transport, therefore mitigating the impact of this property. The development of highly controllable and scalable ultrathin film deposition techniques is therefore crucial to the application of α-Fe2O3. Here, a plasma-enhanced atomic layer deposition (PEALD) process for the deposition of homogenous, conformal, and thickness-controlled α-Fe2O3 thin films (2 plasma co-reactant at relatively low reactor temperatures, ranging from 200 to 300 °C. Optimisation of deposition protocols was performed using the thin film growth per cycle and the duration of each cycle as optimisation metrics. Linear growth rates (constant growth per cycle) were measured for the optimised protocol, even at high cycle counts (up to 1200), confirming that all deposition is ‘true’ atomic layer deposition (ALD). Photoelectrochemical water splitting performance was measured under solar simulated irradiation for pristine α-Fe2O3 deposited onto FTO, and with a α-Fe2O3-coated TiO2 nanorod photoanode.

The reactivity of the racemic N-heterocyclic stannylene [{MeHCN(tBu)}Sn] (1) with the chalcogenide elements O2, S, Se, and Te has been investigated. In the case of the reaction of 1 with molecular oxygen, the cyclic tristannoxane complex [{MeHCN(tBu)}2Sn(μ-O)]3 (3) was isolated and characterised. NMR studies (1H, 13C, and 119Sn) show the formation of D3- and C2- symmetric assemblies. The reaction of 1 with S, Se, and Te, respectively, yielded the cyclo-distannachalcogenide complexes, [{MeHCN(tBu)}2Sn(μ-E)]3 (4: E = S, 5: E = Se, 6: E = Te), again with multinuclear NMR studies proving the formation of C2- and Cs-symmetric assemblies. Single crystal X-ray diffraction studies have been used to elucidate the molecular structures of the products of oxidative addition, 3, 4, 5, and 6.

A new series of tin(II) complexes (1, 2, 4, and 5) were successfully synthesized by employing hydroxy functionalized pyridine ligands, specifically 2-hydroxypyridine (hpH), 8-hydroxyquinoline (hqH), and 10-hydroxybenzo[h]quinoline (hbqH) as stabilizing ligands. Complexes [Sn(μ-κ2ON-OC5H4N)(N{SiMe3}2)]2 (1) and [Sn4(μ-κ2ON-OC5H4N)6(κ1O-OC5H4N)2] (2) are the first structurally characterized examples of tin(II) oxypyridinato complexes exhibiting {Sn2(OCN)2} heterocyclic cores. As part of our study, 1H DOSY NMR experiments were undertaken using an external calibration curve (ECC) approach, with temperature-independent normalized diffusion coefficients, to determine the nature of oligomerisation of 2 in solution. An experimentally determined diffusion coefficient (298 K) of 6.87 × 10−10 m2 s−1 corresponds to a hydrodynamic radius of Ca. 4.95 Å. This is consistent with the observation of an averaged hydrodynamic radii and equilibria between dimeric [Sn{hp}2]2 and tetrameric [Sn{hp}2]4 species at 298 K. Testing this hypothesis, 1H DOSY NMR experiments were undertaken at regular intervals between 298 K–348 K and show a clear change in the calculated hydrodynamic radii form 4.95 Å (298 K) to 4.35 Å (348 K) consistent with a tetramer ⇄ dimer equilibria which lies towards the dimeric species at higher temperatures. Using these data, thermodynamic parameters for the equilibrium (ΔH° = 70.4 (±9.22) kJ mol−1, ΔS° = 259 (±29.5) J K−1 mol−1 and ΔG°298 = −6.97 (±12.7) kJ mol−1) were calculated. In the course of our studies, the Sn(II) oxo cluster, [Sn6(m3-O)6(OR)4:{Sn(II)(OR)2}2] (3) (R = C5H4N) was serendipitously isolated, and its molecular structure was determined by single-crystal X-ray diffraction analysis. However, attempts to characterise the complex by multinuclear NMR spectroscopy were thwarted by solubility issues, and attempts to synthesise 3 on a larger scale were unsuccessful. In contrast to the oligomeric structures observed for 1 and 2, single-crystal X-ray diffraction studies unambiguously establish the monomeric 4-coordinate solid-state structures of [Sn(κ2ON-OC9H6N)2)] (4) and [Sn(κ2ON-OC13H8N)2)] (5).