Search

Thin films of lead sulfide (PbS) are being extensively used for the fabrication of optoelectronic devices for commercial and military applications. In the present work, PbS films were fabricated onto a soda lime glass substrate by using an electron beam (e-beam) evaporation technique at a substrate temperature of 300 °C. Samples were annealed in an open atmosphere at a temperature range of 200–450 °C for 2 h. The deposited films were characterized for structural, optical, and electrical properties. Structural properties of PbS have been studied by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS), and Rutherford backscattering spectrometry (RBS). The results of XRD showed that the PbS thin film was crystalline in nature at room temperature with cubic crystal structure (galena) and preferential (111) and orientation (022). The morphology of the thin films was studied by FESEM, which also showed uniform and continuous deposition without any peel-off and patches. EDS analysis was performed to confirm the presence of lead and sulfur in as-deposited and annealed films. The thickness of the PbS film was found to be 172 nm, which is slightly greater than the intended thickness of 150 nm, determined by RBS. Ultraviolet-Visible-Near-Infrared (UV-Vis-NIR) spectroscopy revealed the maximum transmittance of ~25% for as-deposited films, with an increase of 74% in annealed films. The band gap of PbS was found in the range of 2.12–2.78 eV for as-deposited and annealed films. Hall measurement confirmed the carriers are p-type in nature. Carrier concentration, mobility of the carriers, conductivity, and sheet resistance are directly determined by Hall-effect measurement. The as-deposited sample showed a conductivity of 5.45 × 10−4 S/m, which gradually reduced to 1.21 × 10−5 S/m due to the composite nature of films (lead sulfide along with lead oxide). Furthermore, the present work also reflects the control of properties by controlling the amount of PbO present in the PbS films which are suitable for various applications (such as IR sensors).

Comparative studies were performed on variations in the ABO3 perovskite structure, chemical stability in a CO2-H2 gas atmosphere, and electrical conductivity measurements in air, hydrogen, and humidity-involving gas atmospheres of monophase orthorhombic Ba1−xSrxCe0.9Y0.1O3−δ samples, where 0 < x < 0.1. The substitution of strontium with barium resulting in Ba1−xSrxCe0.9Y0.1O3−δ led to an increase in the specific free volume and global instability index when compared to BaCe0.9Y0.1O3−δ. Reductions in the tolerance factor and cell volume were found with increases in the value of x in Ba1−xSrxCe0.9Y0.1O3−δ. Based on the thermogravimetric studies performed for Ba1−xSrxCe0.9Y0.1O3−δ, where 0 < x < 0.1, it was found that modified samples of this type exhibited superior chemical resistance in a CO2 gas atmosphere when compared to BaCe0.9Y0.1O3−δ. The application of broadband impedance spectroscopy enabled the determination of the bulk and grain boundary conductivity of Ba1−xSrxCe0.9Y0.1O3−δ samples within the temperature range 25–730 °C. It was found that Ba0.98Sr0.02Ce0.9Y0.1O3−δ exhibited a slightly higher grain interior and grain boundary conductivity when compared to BaCe0.9Y0.1O3−δ. The Ba0.95Sr0.05Ce0.9Y0.1O3−δ sample also exhibited improved electrical conductivity in hydrogen gas atmospheres or atmospheres involving humidity. The greater chemical resistance of Ba1−xSrxCe0.9Y0.1O3−δ, where x = 0.02 or 0.05, in a CO2 gas atmosphere is desirable for application in proton ceramic fuel cells supplied by rich hydrogen processing gases.

The high efficiency of solid oxide fuel cells with La0.8Sr0.2MnO3−δ (LSM) cathodes working in the range of 800–1000 °C, rapidly decreases below 800 °C. The goal of this study is to improve the properties of LSM cathodes working in the range of 500–800 °C by the addition of YFe0.5Co0.5O3 (YFC). Monophasic YFC is synthesized and sintered at 950 °C. Composite cathodes are prepared on Ce0.8Sm0.2O1.9 electrolyte disks using pastes containing YFC and LSM powders mixed in 0:1, 1:19, and 1:1 weight ratios denoted LSM, LSM1, and LSM1, respectively. X-ray diffraction patterns of tested composites reveal the presence of pure perovskite phases in samples sintered at 950 °C and the presence of Sr4Fe4O11, YMnO3, and La0.775Sr0.225MnO3.047 phases in samples sintered at 1100 °C. Electrochemical impedance spectroscopy reveals that polarization resistance increases from LSM1, by LSM, to LSM2. Differences in polarization resistance increase with decreasing operating temperatures because activation energy rises in the same order and equals to 1.33, 1.34, and 1.58 eV for LSM1, LSM, and LSM2, respectively. The lower polarization resistance of LSM1 electrodes is caused by the lower resistance associated with the charge transfer process.

Comparative studies were performed on variations in the ABO3 perovskite structure, chemical stability in a CO2-H2 gas atmosphere, and electrical conductivity measurements in air, hydrogen, and humidity-involving gas atmospheres of monophase orthorhombic Ba1−xSrxCe0.9Y0.1O3−δ samples, where 0 < x < 0.1. The substitution of strontium with barium resulting in Ba1−xSrxCe0.9Y0.1O3−δ led to an increase in the specific free volume and global instability index when compared to BaCe0.9Y0.1O3−δ. Reductions in the tolerance factor and cell volume were found with increases in the value of x in Ba1−xSrxCe0.9Y0.1O3−δ. Based on the thermogravimetric studies performed for Ba1−xSrxCe0.9Y0.1O3−δ, where 0 < x < 0.1, it was found that modified samples of this type exhibited superior chemical resistance in a CO2 gas atmosphere when compared to BaCe0.9Y0.1O3−δ. The application of broadband impedance spectroscopy enabled the determination of the bulk and grain boundary conductivity of Ba1−xSrxCe0.9Y0.1O3−δ samples within the temperature range 25–730 °C. It was found that Ba0.98Sr0.02Ce0.9Y0.1O3−δ exhibited a slightly higher grain interior and grain boundary conductivity when compared to BaCe0.9Y0.1O3−δ. The Ba0.95Sr0.05Ce0.9Y0.1O3−δ sample also exhibited improved electrical conductivity in hydrogen gas atmospheres or atmospheres involving humidity. The greater chemical resistance of Ba1−xSrxCe0.9Y0.1O3−δ, where x = 0.02 or 0.05, in a CO2 gas atmosphere is desirable for application in proton ceramic fuel cells supplied by rich hydrogen processing gases.