Search

The global drive to eliminate mercury is stimulating the development of LED lamps for UV curing of coatings. Despite its many advantages, the transition to this system in the furniture industry presents technological issues. This paper aimed to determine the impact of the paint line’s individual technological and process parameters on the coating’s optical properties, such as colour and gloss of furniture components made of white-coloured light-weight boards. Samples were prepared under the conditions of an industrial paint line using LED and traditional mercury lamps at the rate of 50 m/min. The colour was tested using the CIELAB system on a BYK GARDNER spectrophotometer, while the gloss was measured using the PICO GLOSS meter. Based on the data obtained, the optical parameters were found to be highly stable irrespective of the power drop in the LED lamps. The coordinates L*, b* and gloss G were affected by the amount of topcoat and basecoat, the number of coats, the mercury lamps’ power and the panel grinding programs used. The results of the tests showed that high L* and b* values could be achieved by increasing the number of overlays. This solution also ensures less basecoat and topcoat consumption, contributing to large material savings.

The furniture industry constantly strives to search for ecological and cost-effective solutions in the production of wood-based composites. It is anticipated that furniture with a honeycomb core and HDF-facing will gain market share. Understanding how specific technical and procedural factors on the finishing line affect the resistance of coatings on furniture elements made of honeycomb boards was the main goal of the study. With the use of a digital microscope, the roughness of two different types of HDF was tested. On the industrial UV LED+Hg finishing line, 198 different surface coating variations were produced by applying five or six layers of varnish applied, ranging from 3 to 30 g/m2 and hardening them with various surface power densities. On the basis of statistical tests, the influence of individual factors on abrasion, impact, and scratch resistance was determined. The nanointendence test of the coatings was used to measure the hardness and elasticity modulus. The coloring caused by coffee traces was checked using a colorimeter. The findings confirm the conception that LED+Hg lamp modules can replace mercury and gallium-doped mercury lamps.

In the upcoming years, it is expected that more furniture will be built from honeycomb panels due to the growing demand for lightweight, long-lasting furnishings. High-density fiberboard (HDF), previously used in the furniture industry as back walls in box furniture or drawer components, has become a popular facing material used in the production of honeycomb core panels. Varnishing the facing sheets of lightweight honeycomb core boards with the use of analog printing technology and UV lamps is a challenge for the industry. The aim of this study was to determine the effect of selected varnishing parameters on coating resistance by experimentally testing 48 coating variants. It was found that the interactions between the following variables were crucial in achieving adequate resistance: lamp power, the amounts of varnish applied, and the number of layers. The highest scratch, impact, and abrasion resistance values were observed for samples with optimal curing provided by more layers and maximum curing with 90 W/cm lamps. Based on the pareto chart, a model was generated that predicted the optimal settings for the highest scratch resistance. Resistance to cold liquids made with a colorimeter increases with lamp power.

One of the most important properties of the surface of wood-based panels is their roughness. This property determines the way of working with the material in the processes of gluing and surface varnishing. The aim of this study was to determine the effect of various sanding belt configurations and the feeding speed of the conveyor belt during grinding on the surface roughness of high-density fiberboards (HDF). The research material was prepared under industrial conditions. Three types of boards were selected for the tests. After grinding, the roughness parameters were measured both transversely and longitudinally relative to the grinding direction, using a Mitutoyo SJ-210 profilometer and the optical method. Based on ANOVA analysis of the data, it was found that the type of HDF boards used and the configuration of the abrasive belts had a statistically significant impact on the roughness. The samples for which the grinding process was performed with sanding belts of the highest grain size had the lowest roughness. For the amplitude roughness parameters, the direction of roughness measurement had a significant influence. These results may provide valuable guidance for the furniture industry in the preparation of HDF for furniture production.