The focus is on the oxidation resistance and tribological performance of ta-C and Al2O3/ta-C coatings. The wear tests were carried out on the ball on disc tribometer at room (25 °C) and high (400, 450 and 500 °C) temperatures in ambient air with Si3N4 balls as counterbodies. Scanning electron microscopy and Raman spectroscopy were used to analyze the surface morphology and chemical bonding, respectively. The Al2O3/ta-C coating exhibited better oxidation resistance and tribological performance at elevated temperatures than the ta-C coating. The Raman analysis revealed that a thin alumina layer suppresses structural changes in the ta-C coating at elevated temperatures, thus preserving the sp3 content.

Mechanical and tribological properties of the hard-multilayer TiN-AlTiN/nACo-CrN/AlCrN-AlCrO-AlTiCrN coating deposited on WC-Co substrate were investigated. The sliding tests were carried out using ball-on-disc tribometer at room (25 &deg, C) and high temperatures (600 and 800 &deg, C) with Al2O3 balls as counterpart. Nano-scratch tests were performed at room temperature with a sphero-conical diamond indenter. The surface morphology and chemical composition were investigated with scanning electron microscopy (SEM), energy-dispersive spectrometry (EDS) and in-situ high-temperature X-ray diffraction (HT-XRD). The phase transition from fcc-(Al,Cr)2O3 into &alpha, (Al,Cr)2O3 was observed at about 800 &deg, C. The results of the tribological tests depends on the temperature, the lowest apparent and real wear volumes were observed on the coating after the test at 800 &deg, C along with the smallest coefficient of friction (COF). The plastic deformation of the coating was confirmed in sliding and nano-scratch tests. The nano-scratch tests revealed the dependence of COF value on the temperature of the sliding tests.

The study deals with tribological properties of diamond films that were tested under reciprocal sliding conditions against Si3N4 balls. Adhesive and abrasive wear are explained in terms of nonequilibrium thermodynamic model of friction and wear. Surface roughness alteration and film deformation induce instabilities in the tribological system, therefore self-organization can occur. Instabilities can lead to an increase of the real contact area between the ball and film, resulting in the seizure between the sliding counterparts (degenerative case of self-organization). However, the material cannot withstand the stress and collapses due to high friction forces, thus this regime of sliding corresponds to the adhesive wear. In contrast, a decrease of the real contact area leads to the decrease of the coefficient of friction (constructive self-organization). However, it results in a contact pressure increase on the top of asperities within the contact zone, followed by material collapse, i.e., abrasive wear. Mentioned wear mechanisms should be distinguished from the self-lubricating properties of diamond due to the formation of a carbonaceous layer.