Metal–organic frameworks (MOFs) have been observed to exclusively eliminate dyes confined within their respective pores. In this investigation, the synthesis of a breathable MOF structure, MIL-88B(Fe), was pursued with the objective of circumventing restrictions on pore size to enhance its adsorption capabilities. The synthesis of MIL-88B(Fe) was carried out via the assisted solvothermal method at 373 K using inexpensive yet environmentally benign FeCl3·6H2O, 1,4-benzenedicarboxylic acid, and DMF as a metal precursor, linker, and solvent, respectively. Furthermore, the MOF was subjected to extensive analytical characterisation using XRD, FT-IR spectroscopy, N2 gas sorption, TGA, and SEM. The experimental data showed that the utilisation of MIL-88B(Fe) with a dose level of 5 mg for 180 min at a pH of 9 led to the highest levels of adsorption for both dyes, with 162.82 mg g−1 for methylene blue (MB) and 144.65 mg g−1 for rhodamine B (RhB), as a result of the contrast in the molecular size between each dye. The Langmuir and Freundlich models demonstrated a correlation with isotherms, while the thermodynamic analysis demonstrated that MIL-88B(Fe) exhibits distinct endothermic and breathable properties. The efficacy of MIL-88B(Fe) adsorbent for MB and RhB in aqueous solutions indicated exceptional performance, stability, and noteworthy reusability performance.

Crystalline sodium Y (NaY) zeolite has been synthesized using alternative natural source of aluminate and silicate, extracted from natural Belitung kaolin. Prior to use, the natural kaolin was pretreated to obtain fragmented metakaolin and extracted silica. Synthesis was conducted with the addition of NaY gel (two types of NaY seeds were used, prepared from colloidal sillica or sodium silica water) using hydrothermal method for 21 h at 100 °C. The characterization on the as-synthesized zeolites confirmed that the one prepared using colloidal silica-seed has closer structure similarity to NaY zeolite that was synthesized using pro analysis silicate and aluminate sources. Thus, the rest of the synthesis of NaY was carried out using colloidal silica-NaY seed. The NaY zeolites then were converted to HY, through ammonium-exchange followed by calcination, to be tested as cracking catalysts using n-hexadecane as a probe molecule. It shows that HY from metakaolin and extracted silica gives high performance, i.e., n-hexadecane conversion of 58%−64%, also C5-C12 percentage yield and selectivity of 56%−62% and 98%. This work has shown the potential to utilize kaolin as alternative silicate aluminate sources for crystalline zeolite synthesis and to obtain inexpensive and environmentally friendly catalyst materials.