Statement of Problem: It is unclear whether an extended glaze firing could improve the long-term mechanical performance of densely sintered CAD-CAM ceramics., Purpose: The purpose of this in vitro study was to analyze the effect of an extended glaze firing on the flexural fatigue strength (FFS) of densely sintered milled (hard-machined) leucite-based (LEU) and lithium disilicate-based (DIS) ceramics., Material and Methods: Disks were machined from ceramic blocks and divided into 6 groups (n=20) according to the material, LEU or DIS, and to the applied glaze firing: manufacturer-recommended glaze (G group), extended glaze (EG group), and control/no firing (C group). The surface roughness of the disks was measured before and after firing by using a contact profilometer, and data were compared by paired sample tests. Specimens were submitted to fatigue by using the staircase test design in water (piston-on-3 balls; 500 000 cycles, 20 Hz, and sinusoidal loading). Mean (±SD) FFS values were then calculated and analyzed by using 1-way analysis of variance and post hoc Tukey test (α=.05)., Results: Surface roughness did not change after the firing (P>.05). The highest FFS value in both ceramics was obtained after EG firing (LEU-EG=80.52 ±6.3 MPa; DIS-EG=147.25 ±10.5 MPa), which was statistically superior to G firing (LEU-G=73 ±6.8 MPa, P=.003; DIS-G=134.34 ±15.6 MPa; P=.023) and C group (LEU-C=61.94 ±6.3 MPa; P<.001; DIS-C=134.13 ±17.3 MPa; P=.023)., Conclusions: EG firing optimized the biaxial flexural fatigue strength of hard-machined leucite and lithium disilicate ceramics compared with conventional glaze firing., (Copyright © 2018 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.)