Search

As recently explored lithium-ion battery (LIB) anode materials, transition metal vanadates have attracted much attention due to their excellent electrochemical performance. In this work, we successfully synthesized solid Co3V2O8 microspheres (sCVO MSs) via a facile and controllable hydrothermal reaction, and the magical formation mechanism was also revealed by the different morphologies of sCVO MSs at different reaction times. When tested as LIB anode materials, sCVO MSs showed superior reversible capacities (∼780 mA h g−1 after 250 cycles at 1000 mA g−1 and as high as 550 mA h g−1 even after 400 cycles at 5000 mA g−1) and excellent rate performance (a capacity of ∼500 mA h g−1 at a current density of 2000 mA g−1). It is accordingly demonstrated that uniform sCVO MSs have great potential to be used as high-performance LIB anodes. [ABSTRACT FROM AUTHOR]

Transition metal vanadates have attracted much attention for high capacity anodes of lithium ion batteries (LIBs). However, they have obvious drawbacks (short cycle-lives and low rate performance) because of the intrinsically low electronic conductivity and serious volume variation during Li-ion desorption and insertion. In particular, pure Co3V2O8 micro-pencils (pCVO MPs) have a stable and regular crystal structure, large tap density and uniform grain size, but, unfortunately, they have not exhibited expected electrochemical performance. Herein, we report the successful preparation of reduced graphene oxide coated Co3V2O8 micro-pencils (rGO@CVO MPs) through a facile approach combining hydrothermal synthesis with thermal reduction. When tested as anodes for LIBs, rGO@CVO MPs exhibit superior electrochemical performance compared to that of pure Co3V2O8 micro-pencils (pCVO MPs). The anodes of rGO@CVO MPs show a high reversible capacity of 760 mA h g−1 over 200 cycles at 200 mA g−1, and 500 mA h g−1 can remain after 500 cycles at 1000 mA g−1, with an increase in 200 mA h g−1 in contrast to the pCVO MPs. It is consequently demonstrated that the composite material (rGO@CVO MPs) is a promising anode material for LIBs. [ABSTRACT FROM AUTHOR]

In this study, we used lead zirconate titanate (PZT) aerogels prepared by a solvothermal assisted sol-gel method as raw materials to synthesize PZT aerogel/PVDF composite coatings and PZT aerogel sintered sheets through natural annealing and PVDF composite and hot pressing, respectively, and then combined them with the design principle of a biomimetic shell structure to prepare an alternate coating/sheet structured PZT aerogel piezoelectric composite with natural distinguished mechanical properties. It had excellent piezoelectric properties with a piezoelectric coefficient d 33 of 435.15 pC N -1 and d 31 of -144.55 pC N -1 , excellent electromechanical coupling properties with a planar electromechanical coupling coefficient of 60.14%, low dielectric loss of 0.76% at 40 Hz and low density of 3.04 g cm -3 . When used as the piezoelectric material in underwater acoustic transducers (UATs), compared with all kinds of piezoelectric ceramics, it achieved higher piezoelectric and comprehensive mechanical properties, lower dielectric loss, lower density, and electromechanical coupling properties similar to that of Pb-containing piezoelectric ceramics, thus showing extremely promising application prospects in UATs.

Layered, Li-rich Mn-based oxides (LLMOs) are the most promising next-generation, high-energy batteries due to their relatively high specific capacities and high voltages. However, the practical application of LLMO cathodes is limited by low initial coulombic efficiencies (CEs) and poor cycling performance. Herein, we used the reaction of KMnO 4 and MnSO 4 under hydrothermal conditions to grow a nano-SCMO shell on the LLMO material surface (SCMO@LLMO). The unique particle/sheet compound structure of the SCMO shell is beneficial to the electrochemical reaction. SCMO has good Li storage characteristics and excellent surface structure stability in the single-crystal phase which further improves the reversible capacity, CE, and cyclic stability of the LLMO cathode. Therefore, the optimal coated sample (feedstock: 2 M KMnO 4 , SCMO@LLMO-2.0) exhibits a good initial discharge capacity (238.2 mA h g -1 at 1C and 173.8 mA h g -1 at 5C), initial CE (89.6% at 1C and 86.5% at 5C), and cycling performance (capacity retention of 84.67% at 1C and 62.72% at 5C after 200 cycles). This work adopts a hydrothermal method to synthesize a nano-single crystal composite material, laying a foundation for the preparation of the SCMO@LLMO cathodes for LLMO primary battery cathodes with high electrochemical performance., Competing Interests: There are no conflicts to declare., (This journal is © The Royal Society of Chemistry.)