Search

Hollow hamburger-like and other coupled-layered ZnO microstructures have been fabricated by a facile solvothermal process using the mixture of water and alcohol as solvents. The volume ratios of water/glycerol play an important role for the morphologies of the microstructures. In the case of a volume ratio of 1/2, the hamburger-like ZnO microstructures are created by employing zinc glycerolate (C3H6O3Zn) as a sacrificial template. A possible formation process from precursor C3H6O3Zn to ZnO is proposed by arresting a series of intermediate phases and the formation mechanism of the microstructures is proposed accordingly. The volume ratios of water/glycerol, such as 1/10, 1/6, 1/4, 1/2 and 1/1, were adjusted to create microstructures with various morphologies. The results indicated that the morphologies of the resulting samples changed from quasi-rhombic C3H6O3Zn plates to various coupled-layered ZnO microstructures, suggesting that water is responsible for the formation of coupled-layered structures. In addition, investigations into the formation of ZnO microstructures in mixtures of water and various alcohols, including water/ethanol, water/isopropyl alcohol, water/n-butyl alcohol, water/ethylene glycol and water/glycerol, reveal that alcohols are crucial for control of the morphologies of the microstructures. The multi-hydroxyl alcohols, e.g. ethylene glycol and glycerol, favour the formation of hollow structures compared with the case of single-hydroxyl alcohols. [ABSTRACT FROM AUTHOR]

Micro- and nano-structures of iron oxide with tunable morphologies were fabricated through a solvothermal process by adjusting experimental parameters. In this route, the ethylene glycol (EG) solution of ferric chloride hexahydrate (FeCl3·6H2O), sodium bicarbonate (NaHCO3), and ethylenediamine (EDA) was heat-treated to create the micro- and nano-structures of Fe3O4, where EG acted as both solvent and reducing agent. NaHCO3 and EDA were crucial for the morphology and size of these micro- and nano-structures. Fe3O4 micro- and nano-structures revealed solid, porous and hollow morphologies by changing the reaction time, the type of solvent, and the amount of EDA and NaHCO3. Fe3O4 nanoparticles were created by controlling experimental parameters. As the reaction progressed, nanoparticles aggregated together to form solid Fe3O4 spheres, and then inner nanoparticles dissolved and recrystallized onto the outer shell of Fe3O4 spheres having been obtained through agglomerating together and then gradually developing into hollow micro- and nano-spheres due to an Ostwald ripening mechanism. Hematite (α-Fe2O3) was synthesized using ethyl alcohol instead of EG. These magnetic micro- and nano-structures revealed excellent magnetic properties. [ABSTRACT FROM AUTHOR]

Some of the metal vanadates have special self-activated luminescence. In order to further enrich its luminous color, luminescent impurity ions can be introduced into its lattice. The interaction between the self-activated emission and the impurity-related emission remains to be studied. In this work, the synergism between the two kinds of emission in LiCa 3 ZnV 3 O 12 was explored from these three aspects: lattice distortion, energy transfer and temperature effect. Eu 3+ ions replace Ca 2+ ions in the lattice of LiCa 3 ZnV 3 O 12 , leading to a lattice contraction of the LCZV host, which depresses the self-activating emission around 500 nm. The characteristic linear emissions of Eu 3+ ions are also observed benefiting from the energy transfer from [VO 4 ] 3- to Eu 3+ . Since the temperature quenching effect is more sensitive for the self-activated emission than that for the Eu 3+ -related ones, the phosphor can be applied as a luminescent temperature sensor, with the absolute and relative temperature sensitivities of 0.012 K -1 and 1.56% K -1 , respectively., Competing Interests: There are no conflicts to declare., (This journal is © The Royal Society of Chemistry.)