Two critical issues associated with semi-transparent, n–i–p perovskite solar cells for 2-terminal tandem devices are parasitic absorption and long-term instability associated with the widely used spiro-OMeTAD and MoOx hole transport and buffer layers, respectively. In this work, we present an alternative hole contact bilayer that consists of a 30 nm undoped layer of spiro-TTB in conjunction with 9 nm of air-stable vanadium oxide (VOx) deposited via atomic layer deposition. The low absorption of UV and visible light in this bilayer results in the fabrication of a semi-transparent perovskite cell with 18.9 mA cm−2 of photocurrent, a 14% increase compared to the 16.6 mA cm−2 generated in a control device with 150 nm of doped spiro-OMeTAD. The ALD VOx buffer layer shows promise as a stable alternative to MoOx; an unencapsulated Cs0.17FA0.83Pb(Br0.17I0.83)3 device with ALD VOx and ITO as the top contact maintains its efficiency following 1000 hours at 85 °C in a N2 environment. Lastly, we use transfer matrix modeling of the optimized perovskite stack to predict its optical performance in a monolithic tandem cell with heterojunction silicon.

In Methyl Ammonium Lead Iodide (MAPI) perovskite solar cells, screening of the built in field by mobile ions has been proposed as part of the cause of the large hysteresis observed in the current/voltage scans in many cells. We show that photocurrent transients measured immediately (e.g. 100 μs) after a voltage step can provide direct evidence that this field screening exists. Just after a step to forward bias, the photocurrent transients are reversed in sign (i.e. inverted), and the magnitude of the inverted transients can be used to find an upper bound on the width of the space charge layers adjacent to the electrodes. This in turn provides a lower bound on the mobile charge concentration, which we find to be 1 x 10 17 /cm 3 . Using a new photocurrent transient experiment, we show that the space charge layer thickness remains approximately constant as a function of bias, as expected for mobile ions in a solid electrolyte. We also discuss additional characteristics of the inverted photocurrent transients that imply either an unusually stable deep trapping, or a photo effect on the mobile ion conductivity.