Hydrogels constitute an important class of polymeric materials, mainly due to their promising applications in the biomedical field. Particularly, mechanical properties are a limiting factor for applications, and reinforcement and improved wear resistance are major directions in current research. In here, graphitic carbon nitride (g-CN)-based hydrogels are presented. The hydrogels are formed in a two-step procedure. In the first step, a prepolymer is synthesized that leads to a significantly improved g-CN dispersibility and stability of g-CN dispersions. Hence, the g-CN content in the final hydrogels can be increased to obtain tough hydrogels. More importantly, hydrogels from charged monomers can be formed as well, which leads to lubricant properties. As such, the investigated route opens up new opportunities to fabricate functional hydrogels with significant toughness, compressibility and lubricity.

Molybdenum carbide and molybdenum nitride nanoparticles have been developed for catalyzing the hydrogen evolution reaction (HER). These nanocatalysts were synthesized by the ‘urea glass’ route. By simply changing the molar ratio of the urea/metal precursor, α-Mo2C and γ-Mo2N nanoparticles, both of which are crystalline, phase pure and monodisperse in size, were obtained. Hydrogen evolution was performed in both 1 M KOH and 0.5 M H2SO4 electrolytes, and characterized by linear sweep voltammetry and electrochemical impedance spectroscopy. The as-synthesized Mo2C showed excellent HER performance especially in KOH. At a catalyst loading of 102 μg cm−2, a low overpotential of 176 mV was needed to produce 10 mA cm−2 of H2. Its measured currents and turnover frequencies for hydrogen evolution at different overpotentials compare favorably against many other recently reported non-precious metal HER catalysts. Online gas chromatography demonstrated that the current efficiency for H2 production is ∼100%. Both Mo2C and Mo2N showed negligible overpotential losses after acceleration degradation tests in acid and alkali. This is noteworthy since very few catalysts are active in these two extreme pHs. An attractive aspect of the α-Mo2C and γ-Mo2N nanoparticles for electrochemical hydrogen evolution is that they are simple and well-characterized in chemical and physical composition. The excellent catalytic activity of the α-Mo2C catalysts can be attributed to their small particle size, which will facilitate a rapid electron transfer for the hydrogen evolution reaction. Our study has placed the as-synthesized α-Mo2C nanoparticles as highly promising alternatives to platinum in the alkaline water electrolyzer.