Search

In the direct iron ore smelting reduction process, molten iron near the bottom blowing gas tuyere is cooled by low temperature/endothermic gas and forms a mushroom shaped solid on top of the tuyere. The formation of an appropriate solid mushroom, which covers the tuyere, can protect the tuyere and the surrounding refractory. In the present study, a water model with a low temperature gas system was established to investigate formation of the solid mushroom and the effects of operating conditions on its shape and dimensions. Transparent acrylic was used to construct the water model, which was 40% of the size of the actual furnace. Water was used to simulate the molten iron. Low temperature air, obtained by passing air through a heat exchanger cooled by liquid nitrogen, was blown into the water bath through a bottom tuyere. The air temperature was able to reach-188±1°C. In the water model experiments, water near the tuyere was cooled, and formed an ice mushroom surrounding the tuyere. The effects of operating conditions, mainly gas flowrate and mould material surrounding the tuyere, on the parameters of the solid mushroom were investigated. The parameters of the solid mushroom included whether it could be formed and duration of the solid mushroom, as well as the shape, dimensions, and weight of the solid mushroom. Attempts were also made to relate the temperature-time and pressure-time relationships of the blown gas to the parameters of the solid mushroom. With copper used as mould material surrounding the tuyere, the water model experiments were conducted with flowrate of the bottom blown gas set in the range 30-90 NL min[sup -1]. The results show that as the gas flowrate was increased, the highest water temperature which allowed the solid mushroom to form in the water model was increased. Three different types of pressure-time curve were obtained under different gas flowrates in the present study. They also corresponded to different forms of solid mushroom. As peaks appeared in the pressure-time curve, they revealed ice capsulation and subsequent bursting to release the pressure. A gas flowrate of 80 NL min[sup -1] and water temperature of 19·2°C with copper plate as the bottom material are considered to be optimal conditions of the water model for growth of the appropriate ice mushroom. These data are rather consistent with the gas flowrate and superheat for the actual direct iron ore smelting reduction unit, which are 2700 NL min[sup -1] and 120°C (equivalent to 70 NL min[sup -1] and 22·7°C in the water model). [ABSTRACT FROM AUTHOR]

The present study has been conducted to investigate the effects of operating conditions, which include gas flowrate, tuyere size, tuyere number, and height of iron phase, on the extent of mixing between molten iron and molten slag in the direct iron ore smelting reduction process. A transparent acrylic water model, 30% of the size of the actual smelter, was constructed to study the mass transfer phenomena. In the water model, water and spindle oil were used to simulate molten iron and molten slag, respectively, while air was used to replace the bottom blown nitrogen gas. In addition, thymol (C[sub 10]H[sub 14]O[sub 6]) was used as a tracer material in the water model, added to the water at the beginning of the experiment. As mixing between water and spindle oil proceeded owing to stirring by the bottom blown gas, the concentration of thymol in the water decreased and that in the spindle oil increased. Water samples were taken from the bottom and 12 cm above the bottom of the water model at various operating times. Concentrations of thymol were then measured using a diode array ultraviolet visible spectrophotometer. By analysing the concentration data, the mass transfer rate k[sub w]A, which is a direct index for evaluating the mixing efficiency, could be derived. The process conditions under investigation included 40-500 L min[sup -1] gas flowrate, 0·3[sup -1] cm tuyere size, four or five tuyeres, and 20-30 cm height of the water phase. The test results indicate that when the gas flowrate increases, the value of k[sub w]A increases, which indicates better mixing between oil and water phases. However, as the gas flowrate approaches 40 L min[sup -1], the improvement becomes less obvious. The smaller tuyere gives better mixing, and the design of five tuyeres results in better mixing compared with four tuyeres when they are blown with the same total gas flowrate. However, mixing efficiency decreases with increased height of the water phase. Also, as the gas flowrate of bottom blowing approaches 40 L min[sup -1], gas blowing from the top has little effect on the mixing behaviour in the liquid bath. For a four tuyere system, the process conditions of height of oil phase 5 cm, height of water phase 25 cm, diameter of tuyere 0·75 cm, and gas flowrate for each tuyere 40 L min[sup -1], appear to be the optimal design. [ABSTRACT FROM AUTHOR]

The article reports on research that examined the growth capacity of the cellular components of young mouse incisors and attempted to determine their migration rate. The author were interested in this examination due the fact that rodent incisors undergo continuous growth. The findings indicated that the average daily eruption rate of the incisor correlated with the migration rate of ameloblasts.