Simultaneous reverse and normal initiation technique for atom transfer radical copolymerization (SR&NI ATRP) of styrene and methyl methacrylate in the presence of hexamethyldisilazane (HMDS)-modified silica aerogel nanoparticles (H-SAN) and investigating the effect of addition of H-SAN on the copolymerization and thermal properties of the products are discussed. Some unique features of the H-SAN are evaluated using nitrogen adsorption/desorption isotherm, SEM and TEM. Conversion and molecular weight determinations were carried out using GC and SEC respectively. Adding of H-SAN by 3 wt% results in decrement of conversion from 94 to 73%. In addition, molecular weight of copolymer chains decreases from 19500 to 16000 g.mol-1. However, polydispersity index values increases from 1.29 to 1.65. Linear increase of ln(M0/M) with time for all the samples shows that copolymerization proceeds in a living manner. Increasing thermal stability of the nanocomposites is demonstrated by TGA. DSC results show a decrease in glass transition temperature from 70.3 to 63.5 °C by addition of 3 wt% H-SAN.

Mesoporous diatomite platelets were employed to prepare various random poly (styrene-co-methyl methacrylate)/diatomite composites by in situ simultaneous reverse and normal initiation technique for atom transfer radical random copolymerization (SR&NI ATRP) technique. Nitrogen adsorption/desorption isotherm, SEM and TEM were employed for evaluating some inherent properties of the pristine diatomite platelets. Conversion and molecular weight determinations were carried out using GC and SEC respectively. Addition of 3 wt% diatomite platelets leads to increase of conversion from 76 to 92%. Molecular weight of poly (styrene-co-methyl methacrylate) chains increases from 12893 to 14907 g mol-1 by addition of 3 wt% mesoporous diatomite; however, polydispersity index values increases from 1.18 to 1.44. Copolymers composition was evaluated using 1H NMR spectroscopy. Increasing thermal stability of the nanocomposites is demonstrated by TGA. Differential scanning calorimetry shows an increase in glass transition temperature from 67.6 to 73.4 °C by adding 3 wt% of mesoporous diatomite platelets.