The influence of the substrate electrochemical pre-treatment in 0.5 mol L-1 H2SO4 on the Pt electrodeposition on boron-doped diamond, BDD, film electrodes was investigated. Platinum cannot be electrodeposited on a freshly prepared BDD electrode; however, potentiodynamic cycling or anodic potential steps at short times does activate the electrode. Anodic pre-treatment plays a dual role in the behavior of Pt deposition on BDD surfaces: Pt deposition is increased at short-term anodic pre-treatments, whereas at longer pre-treatment times Pt deposition was inhibited. These facts are explained in terms of wettability changes and passivation of the surface. Conversely, the oxide layer formed in these treatments increases the dispersion level of the catalyst. Este trabalho trata da influência do pré-tratamento eletroquímico de eletrodos de diamante dopado com boro (DDB) em meio ácido, na eletrodeposição de platina. Pt não pôde ser eletrodepositada em eletrodos de DDB recém-preparados. Entretanto, pré-tratamentos baseados em varreduras de potenciais ou em polarizações anódicas a potencial constante em curtos intervalos de tempo ativaram o eletrodo para a deposição de Pt. O tratamento anódico desempenha diferentes papéis, de acordo com o tempo de tratamento: em tempos curtos, a deposição de Pt é aumentada, ao passo que tempos de polarização mais longos inibem o processo de eletrodeposição de Pt, originando, entretanto, depósitos com maior área superficial. Tais resultados são discutidos em termos de mudanças na hidrofilicidade da superfície do DDB, bem como na apassivação da superfície, provavelmente representada pela oxidação da mesma.