In this work, we fabricated a polycrystalline Tb2FeCrO6 double perovskite (DP) oxide by a solid-state reaction method and determined its structural, magnetic, and magnetocaloric (MC) properties. The Tb2FeCrO6 DP oxide was found to crystallize in a DP-type structure with the Pbnm space group and to undergo a paramagnetic-to-antiferromagnetic transition at a temperature of ~ 8.5 K. A large low-temperature MC effect was observed in the Tb2FeCrO6 DP oxide. The MC parameters in terms of maximum magnetic entropy changes, temperature-averaged entropy change (5 K), and relative cooling power for Tb2FeCrO6 DP oxide under a magnetic field change of 0–7 T were 12.9 J/kg K, 12.7 J/kg K, and 341.4 J/kg, respectively. These parameters were consistent with similarly high levels in recently updated MC materials, making the material a suitable candidate for low-temperature magnetic cooling applications. [ABSTRACT FROM AUTHOR]

The magnetic properties and magnetocaloric effect (MCE) in the ternary intermetallic compound of EuAuGe have been investigated. The compound undergoes a second-order magnetic phase transition at its own Curie temperatures T∼33 K. A large reversible table-like MCE has been observed from 1 to 40 K, which is related to the magnetic field-sensitive magnetic phase transition. For the magnetic field changes of 0-5 and 0-7 T, the maximum values of magnetic entropy change ( $-{\Delta } S_{\mathrm {M}}^{\max }$) are evaluated to be 7.6 and 10.1 J kg K, respectively; the corresponding relative cooling power ( RCP) are 358 and 499 J kg. The present results indicate that the EuAuGe compound is a considerable candidate for low-temperature refrigeration. [ABSTRACT FROM AUTHOR]