The magnetic properties and magnetocaloric effect (MCE) in the ternary intermetallic compound of EuAuGe have been investigated. The compound undergoes a second-order magnetic phase transition at its own Curie temperatures T∼33 K. A large reversible table-like MCE has been observed from 1 to 40 K, which is related to the magnetic field-sensitive magnetic phase transition. For the magnetic field changes of 0-5 and 0-7 T, the maximum values of magnetic entropy change ( $-{\Delta } S_{\mathrm {M}}^{\max }$) are evaluated to be 7.6 and 10.1 J kg K, respectively; the corresponding relative cooling power ( RCP) are 358 and 499 J kg. The present results indicate that the EuAuGe compound is a considerable candidate for low-temperature refrigeration. [ABSTRACT FROM AUTHOR]

The rare-earth (RE)-based magnetic solids with large magneto-caloric effect (MCE) have been well investigated recently due to their potential applications in the field of environmentally friendly cryogenic magnetic refrigeration (MR). Herein, two polycrystalline RE-based REFe2Si2 (RE = Dy and Tb) intermetallic compounds have been prepared by an arc-melting way and determined with regard to the structural and magnetic phase transition (MPT) properties as well as the MCE and magneto-caloric performance. Both of the present REFe2Si2 compounds at room temperature are crystallized in a ThCr2Si2-type structure and undergo a first-ordered MPT from antiferromagnetic to paramagnetic state around the Néel temperature (TN) of ~ 4.05 K for DyFe2Si2 and ~ 6.25 K for TbFe2Si2, respectively. Large cryogenic MC effect together with excellent MC performance have been realized in DyFe2Si2 compound. The MC parameters with magnetic field change at 0–5 T of the maximum magnetic entropy changes and the refrigerant capacity/relative cooling power were found to be 16.08 J/kgK and 318.5/403.3 J/kg for DyFe2Si2 and to be 9.88 J/kgK and 105.9/140.8 J/kg for TbFe2Si2, respectively. [ABSTRACT FROM AUTHOR]