Search

In this study, different weight percentages of Mg(NO3)2 were added to a polymer blend composed of chitosan (CS) and methylcellulose (MC). The solution casting method was adopted to prepare the polymer electrolyte films. As the host matrix, the polymer blend consists of 70 wt.% of CS and 30 wt.% of MC. The interactions between the blend and the Mg(NO3)2 salt were revealed by FTIR analysis. The deconvolution of XRD peaks followed by the calculation of crystallinity indicates that the electrolyte samples were amorphous. The bulk resistance decreased with increasing salt content, according to the results of electrical impedance spectroscopy (EIS), and this was caused by the influence of carrier concentration. The sample containing 30 wt.% of Mg(NO3)2 was determined to have a maximum value of DC conductivity of 2.12 × 10–5 Scm−1 at room temperature by EIS analysis. The highest conducting film's potential stability was found to be 3.65 V. It was found that the ion transference number was 0.86. The performance of the magnesium ion battery was then evaluated after it was built using the highest conducting polymer electrolyte. Considering this, the current work proposes an eco-friendly, practical, and affordable electrolyte appropriate for making electrochemical devices. [ABSTRACT FROM AUTHOR]

Solid polymer blend electrolyte (SPE) films of Polyethylene oxide(PEO)/Carboxymethyl cellulose (NaCMC) doped with Sodium iodide (NaI), were prepared by solution cast method and their structural, optical and electrical properties were investigated using X-Ray diffraction, Fourier transform infrared spectroscopy, UV–Vis spectrophotometer and Electrical impedance analyser respectively. X-Ray diffraction spectra indicate that, deformation occurred in the structure of the blend followed by doping with NaI salt. The variation in intensity and shifting of characteristic bands in FTIR spectra provides the evidence for formation of complex due to the interaction occurred in the blend with the dopant. Optical energy band gap decreases in the blend samples upon doping and is confirmed by UV–Vis spectrophotometer analysis. Increase of dielectric constant and loss upon doping, exhibits usual behaviour of the polymer electrolytes. An increase in AC conductivity is observed upon doping and maximum conductivity of 9.41 × 10−3 Scm−1 is obtained for 10/90 sample doped with 0.03% Sodium iodide and DC conductivity for the same sample at room temperature is 1.05 × 10–2 Scm−1. In addition, I-T studies confirm the conductivity exhibited by the sample as due to ions and I-V studies show electrochemical stability in the range of good working potential. From the results obtained, it can be inferred that, the prepared sample can be used as polymer electrolytes in the manufacturing of energy storage devices. [ABSTRACT FROM AUTHOR]

In this paper, we report the effect of doping sodium iodide (NaI) salt into a polymer blend matrix of sodium carboxymethyl cellulose (NaCMC) and poly(vinyl alcohol) (PVA). Solution casting approach was used to prepare solid polymer electrolyte (SPE) films. The films were characterized by Fourier-transform infrared spectroscopy (FTIR), X-Ray diffraction (XRD), electrical impedance spectroscopy, thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). XRD showed that NaI incorporation decreased the crystallinity of NaCMC/PVA-based SPE. FTIR technique confirmed the complexation of salt with polymer matrix due to the formation of the coordination bond between Na+ and –OH group and hydrogen bond between I− and –CH group. The sample with 30 wt% NaI showed the highest conductivity of 2.52 × 10–3 S cm−1, strongly influenced by the highest charge concentration (n) , not its mobility (μ). DSC analysis revealed an increase in glass transition temperature (T g) with increasing salt content. TGA studies showed a decrease in thermal stability with salt inclusion. The transference number was found to be 0.99 for the highest conducting sample showing the primary charge carriers are ions. The highest conducting sample exhibited a mechanical strength of 15.42 MPa at room temperature, and it has been used to fabricate a battery to evaluate its suitability in energy storage devices. Graphical abstract created with https://biorender.com. [ABSTRACT FROM AUTHOR]