The aim of this study was to determine the changes occurring in the wood cellulose of the fast-growing poplar (Populus deltoides × maximowiczii) under the influence of steam explosion (SE) pretreatment. Cellulose from native wood and after pretreatment at 160 and 205 °C was isolated. Cellulose polymerization degree by size exclusion chromatography (SEC) and cellulose crystallinity index by Fourier transform infrared spectroscopy-attenuated total reflectance (FTIR-ATR) were determined. The profiles of sugars in the native wood and in the solid fraction after pretreatment (using the acid hydrolysis method) were also determined. In addition, the profile of monosaccharides in the liquid fraction obtained after steam explosion and in the liquid fraction after acid hydrolysis of the oligosaccharides were investigated using high-performance liquid chromatography (HPLC). This allowed to determine the change in the yield of hexoses and pentoses in the studied material. The behavior of cellulose in wood subjected to steam explosion at 160 and 205 °C and isolated by the Kürschner–Hoffer method was studied by determining the absorption bands of FTIR-ATR spectra. The lateral order index (LOI) of cellulose was calculated from the ratio of the intensity of the corresponding absorption bands A1422/A896 cm−1. Total crystallinity index (TCI) of cellulose was calculated from the ratio of the intensity of absorption bands A1372/A2900 cm−1. TCI of Kürschner-Hoffer cellulose isolated from wood subjected to steam explosion at 160 and 205 °C decreased by 5.6 and 5.0%, respectively, with regard to the applied temperature. LOI increased in cellulose isolated from wood subjected to steam explosion at 160 °C (by 0.7%) and at 205 °C (by 19.2%) in relation to the index of cellulose isolated from native wood. Kürschner–Hoffer cellulose isolated from wood subjected to steam explosion at 160 and 205 °C exhibited, respectively, a reduced degree of polymerization of about 11% and about 8%. Polydispersity index in Kürschner–Hoffer cellulose was 1% lower after both pretreatments than native sample. [ABSTRACT FROM AUTHOR]

Attenuated total reflectance (ATR) infrared (IR) spectroscopy analyses were performed with silver/white birch (Betula pendula/B. pubescens) and Scots pine (Pinus sylvestris) chips pretreated under alkaline (from 1 to 8% NaOH charge on wood dry solids) conditions to determine the suitability of this method in quickly determining chemical changes caused by varying treatment conditions on wood chemical structure. In addition to the alkali charge, pretreatment conditions varied with respect to temperature (130 and 150 °C) and treatment time (from 30 to 120 min). The spectral data of pretreated wood samples were compared to those of untreated reference samples, and the effects of the pretreatments conducted were determined based on these data. Results indicated that the most essential phenomena taking place during alkaline pretreatments could be detected by applying this simple and rapid spectral method requiring only a small sample amount. Such information included, for example, the cleavage of common lignin and carbohydrate bonds together with the significant removal of organics, especially hemicelluloses during pretreatments. [ABSTRACT FROM AUTHOR]