Introduction Recurrent dislocations are still the most frequent reason for revision in total hip arthroplasty (THA). The impact of bearing surfaces on dislocations is still controversial. We hypothesized that: (1) bearing surfaces influence the revisions due to dislocations; (2) ceramic-on-ceramic reduced the revisions for dislocations in adjusted models; (3) Delta-on-Delta bearings reduced the revisions for dislocations in comparison to surfaces with cross-linked polyethylene. Materials and methods The regional arthroplasty registry was enquired about bearing surfaces and revisions for dislocations and instability. Unadjusted and adjusted rates were provided, including sex, age (28 mm; Results The rate of revisions for dislocations was significantly lower in ceramic-on-ceramic and metal-on-metal bearings (unadjusted rates). After adjusting for age, sex, and head size (36 and 28 mm), hard-on-hard bearings were protective (p p = 0.0009). The rate of revisions for dislocation was similar in bearings with cross-linked polyethylene and Delta-on-Delta articulations, in unadjusted and adjusted models. Conclusion Bearings with conventional polyethylene were more predisposed to dislocations. Currently adopted bearings exerted no significant influence on revisions due to dislocations. These findings could be primarily related to wear, but due to the time distribution, soft tissue envelopes and surface tension may also play a role. Pre-clinical biomechanical evaluations and prospective matched cohort studies are required to draw definitive conclusions.

Evaluation of medical devices retrieved after in vivo service provides unique evidence related to the physiological environment in which the biomaterials performed. This study implements a training procedure for evaluating polyethylene bearings of joint prostheses obtained after pre-clinical tests or explanted after in vivo function. A total of 161 damage regions on 45 bearings were evaluated by four observers. An illustrated Damage Mode Atlas was developed as a reference guide, inclusive of both photographs and concise written descriptions of 16 specific damage modes that are typical for polyethylene bearings. Utilizing the Damage Mode Atlas to train new researchers improved the damage pattern analysis, including more accurate identification of damage modes and improved inter-rater reliability. This Damage Mode Atlas is a useful supplementary tool for conducting Stage II non-destructive analysis of explanted polyethylene bearings used for joint replacement, in accordance with international guidelines for evaluating explanted medical devices.