Two metal-organic frameworks, Ca(2,6-NDC)(DMF) (1) and Mn3(2,6-NDC)3(DMF)4 (2) (where 2,6-NDC = 2,6-naphthalene dicarboxylate and DMF = N,N′-dimethylformamide) have been solvothermally synthesized under optimized conditions and characterized by X-ray powder diffraction, elemental analysis, FT-IR spectroscopy, and TG analysis. The thermal decomposition characteristics were investigated under air atmosphere from 300 to 1,170 K (for 1) and from 300 to 971 K (for 2). The molar heat capacities were measured from 198 to 548 K (for 1) and from 198 to 448 K (for 2) by temperature modulated differential scanning calorimetry (TMDSC) for the first time. The fundamental thermodynamic parameters such as entropy and enthalpy variations with temperature were calculated based on the experimentally determined molar heat capacities.

Nanometric Fe2O3 particles could be inserted inside the internal pore volume of SBA-15 mesoporous silica and mesoporous alumina supports, when Fe(III) chelates (EDTA, gluconate or citrate) were used as impregnating precursors. The oxidative degradation of the chelating anions was followed by combined TG-DTA. Strong chelate-SiOH interactions (case of bulky EDTA), favored by the mesopore curvature, yield sub-nanometric extremely well dispersed Fe2O3 particles preferentially located at the micropore mouths (confinement effect). Fe2O3 even more strongly interacts with alumina walls, generating either (Fe,Al)2O3 mixed phases or Fe-aluminate micro domains. These iron-based mesoporous alumina composites proved very active catalysts in total oxidation of phenol at ambient conditions, with extremely low iron leaching (0.2%).

The dehydration of a series of VPI-5 and H3 samples, synthesized under various conditions, as well as the solid state transformation of VPI-5 to AlPO4-8 have been investigated using combined TG-DTG-DSC and high-resolution solid state31P-NMR. The TG curves show a quasi-continuous release of water, the total loss being characteristic for each sample. Complete dehydration is achieved when the samples are heated from 20°C to about 150°C at various beating rates. Besides the main dehydration effect, several weak endothermic peaks are observed. These generally non-reproducible modulated peaks, recorded at high heating rates, are presumably due to the interactions of the water molecules leaving the channels of VPI-5 with the randomly positioned fragments stemming from the destruction of the water triple helix assemblage. The non-isothermal kinetic parameters of the dehydration have been evaluated from the TG and DTG curves recorded at low heating rates.