Magnetic iron oxide-silica shell nanocomposites (IONP@SiO2) have been prepared in a two-step procedure. IONPs were obtained by coprecipitation of iron salts, and coated by silica in sol-gel method under sonication. Two IONP/silica ratios and two drying methods, heating in oven and supercritical CO2 drying, were used. The samples were analyzed using X-ray diffraction (XRD), infrared spectroscopy, magnetic measurements, small-angle neutron scattering (SANS), nitrogen sorption, and scanning electron microscopy (SEM) coupled with energy-dispersive X-ray analysis (EDX). The iron oxide silica nanocomposites obtained via supercritical drying exhibited higher values of the specific surface area and of saturation magnetization compared to the samples synthesized with the same iron oxide content but obtained after drying at 60 °C. Pd(II) adsorption experiments were performed on the materials prepared by supercritical drying. The maximum adsorption capacity 6.5 mg/g showed that the materials can be used as good and cheap adsorbent for palladium ions from aquatic environment. [ABSTRACT FROM AUTHOR]

Mesoporous silica particles have been prepared with functionalized precursors, used either in situ co-condensation process or as post-synthesis grafting agents, in order to deliver surface functionalisation. Aminopropyl, mercaptopropyl, vinyl and hexyl organosilanes were used as funtionalized precursors, tetraethyl orthosilicate as the base silica precursor material, hexadecyl-trimethylammonium bromide (CTAB) as directing agent and water-ethanol mixture as solvent, with ammonia catalyst. The aim was to explore the effect of various recipes on the structural properties of the composite materials. The samples' microstructures have been evaluated using nitrogen sorption and small angle neutron scattering. Ordered mesoporous structures were obtained, for almost all synthesis conditions, after the solvent-extraction of the template agent. Only in one case, for the materials functionalized by mercaptopropyl groups in co-condensation route, disordered amorphous structure was obtained. All samples functionalized by post-grafting presented well-ordered mesoporous structures. The results have potential use for easy design of sorbent materials for drug loading or pollutant adsorption applications. [ABSTRACT FROM AUTHOR]