Search

UV-visible absorption spectroscopy and Raman spectroscopy were used to study damage production in cerium dioxide epitaxial films and polycrystalline sintered samples after irradiation with electrons for three energies to span the threshold displacement energies of cerium and oxygen atoms, and 2.4-MeV Cu ions. Neither amorphization nor specific colour-centre bands were detected. Evolutions of the refractive index were derived from the interference fringes in the optical transmission spectra of epilayers after irradiation. No significant change of the refractive index occurred for the 1.0-MeV electron irradiation, whereas a maximum decrease by 28 ± 8% was deduced for the 1.4-MeV and 2.5-MeV energies. These modifications are consistent with ballistic damage on the cerium sublattice for high electron energies producing Ce3+ ions. However, no significant change of refractive index was found for the Cu ion irradiation. This likely stems from the high rate of Frenkel pair recombination in the collision cascades induced by more energetic recoils than for the electron irradiations, combined with electronic excitations and hole capture on Ce3+ ions. This study reveals modifications of the electronic structure upon irradiation that could take place in other non-amorphizable oxide systems. [ABSTRACT FROM AUTHOR]

The photo-annealing of colour centres in yttria-stabilised zirconia (YSZ) was studied by electron paramagnetic resonance spectroscopy upon UV-ray or laser light illumination, and compared to thermal annealing. Stable hole centres (HCs) were produced in as-grown YSZ single crystals by UV-ray irradiation at room temperature (RT). The HCs produced by 200-MeV Au ion irradiation, as well as the F+-type centres ( centres involving oxygen vacancies) were left unchanged upon UV illumination. In contrast, a significant photo-annealing of the latter point defects was achieved in 1.4-MeV electron-irradiated YSZ by 553-nm laser light irradiation at RT. Almost complete photo-bleaching was achieved by laser irradiation inside the absorption band of centres centred at a wavelength ~550 nm. Thermal annealing of these colour centres was also followed by UV-visible absorption spectroscopy showing full bleaching at 523 K. Colour-centre evolutions by photo-induced and thermally activated processes are discussed on the basis of charge exchange processes between point defects. [ABSTRACT FROM AUTHOR]

The damage induced by heavy-ion irradiation has been studied in yttrium iron garnet (Y3Fe5O12or YIG) films, doped with Ca, Tb and Tm, grown by liquid-phase epitaxy on gadolinium gallium garnet (Gd3Ga5O12or GGG) substrates. Irradiations of doped-YIG epitaxial films and GGG substrates with 36-MeV183W and 12-MeV197Au ions were applied for fluences between 1 × 1013and 3 × 1015 cm–2near room temperature. The radiation damage was monitored by micro-Raman spectroscopy and UV–visible optical absorption spectroscopy. Raman spectra revealed that amorphisation was achieved in YIG for both ions, whereas a high lattice disorder was induced in GGG without reaching amorphisation for the Au ion irradiation. Raman spectra also showed that a major damage of the tetrahedral sites was induced in GGG, as previously found for YIG. It is concluded that with such ions reaching the stopping power threshold of track formation in YIG and GGG the observed rate of amorphisation may result from a combination of electronic and nuclear energy losses as calculated using the unified thermal spike model. [ABSTRACT FROM PUBLISHER]