Search

Submitted by LEANDRO BENETTI DE OLIVEIRA null (le_benetti@yahoo.com.br) on 2016-08-30T13:45:31Z No. of bitstreams: 1 TESE - Leandro Benetti de Oliveira.pdf: 2195790 bytes, checksum: 21bf2ac77d2bdf1976aedf77850b0e7f (MD5) Approved for entry into archive by Ana Paula Grisoto (grisotoana@reitoria.unesp.br) on 2016-08-31T13:10:40Z (GMT) No. of bitstreams: 1 oliveira_lb_dr_arafo.pdf: 2195790 bytes, checksum: 21bf2ac77d2bdf1976aedf77850b0e7f (MD5) Made available in DSpace on 2016-08-31T13:10:40Z (GMT). No. of bitstreams: 1 oliveira_lb_dr_arafo.pdf: 2195790 bytes, checksum: 21bf2ac77d2bdf1976aedf77850b0e7f (MD5) Previous issue date: 2016-07-29 Este estudo avaliou a resistência ao deslocamento vertical de seis métodos de fixação interna estáveis utilizados na osteotomia sagital do ramo mandibular (OSRM) no movimento de avanço mandibular com rotação anti-horária. Foram utilizadas sessenta hemimandíbulas sintéticas, divididas em seis grupos de 10 hemimandíbulas, todas fixadas com sistema de fixação 2,0 mm da seguinte forma: Grupo I - 1 miniplaca reta de quatro furos e quatro parafusos monocorticais de 6,0 mm; Grupo II – 1 miniplaca reta de seis furos e seis parafusos monocorticais de 6,0 mm; Grupo III - 2 miniplacas retas de quatro furos e oito parafusos monocorticais de 6,0 mm; Grupo IV - 1 placa grade de oito furos e oito parafusos monocorticais de 6,0 mm; Grupo V - 1 miniplaca reta de quatro furos com quatro parafusos monocorticais de 6,0 mm e um parafuso bicortical 2,0 x 12 mm; Grupo VI – 1 miniplaca reta de quatro furos, locking e quatro parafusos monocorticais de 6,0 mm locking. O teste mecânico foi realizado por meio da aplicação de uma força linear na região entre o primeiro pré-molar e canino, em uma máquina de ensaios mecânicos (EMIC- DL2000) com célula de carga de 10 kilogramas Newton (kN). As cargas para o deslocamento de 1, 3 e 5 mm foram registados em Newton (N) e os dados foram transmitidos para um computador. Os resultados foram avaliados utilizando a análise de variância ANOVA (p

Made available in DSpace on 2016-07-01T13:10:25Z (GMT). No. of bitstreams: 0 Previous issue date: 2015-07-03. Added 1 bitstream(s) on 2016-07-01T13:14:09Z : No. of bitstreams: 1 000864064_20170803.pdf: 144226 bytes, checksum: 6db435f9c14d2caa7d0fbe3b85819efe (MD5) Bitstreams deleted on 2017-08-07T14:09:15Z: 000864064_20170803.pdf,. Added 1 bitstream(s) on 2017-08-07T14:10:18Z : No. of bitstreams: 1 000864064.pdf: 839342 bytes, checksum: 9a89eab66a535ba6ef6d68f443f111d4 (MD5) Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) O objetivo do estudo foi desenvolver uma placa óssea bloqueada em formato de T, com o intuito de ser utilizada em fraturas distais de rádio, e avaliar a resistência da montagem, por meio de ensaios mecânicos. A placa de 2,7 mm foi confeccionada em titânio, contendo eixo com três orifícios para parafusos bloqueados e um orifício para compressão dinâmica, e uma cabeça com dois orifícios para parafusos bloqueados. A cabeça da placa possuía uma chanfradura localizada na porção médio-distal e a extremidade proximal da haste da placa apresentava formato afunilado. Para os ensaios mecânicos foram usados 40 corpos de prova sintéticos em formato de T e 20 placas em T. A placa óssea foi posicionada sobre os corpos de prova, com a falha óssea segmentar de 2 mm localizada entre a cabeça e a haste da placa. Para a determinação das cargas para os ensaios de fadiga, seis montagens foram testadas até a falha, sendo três em flexão engastada e três em compressão. Para o ensaio de fadiga foram utilizadas 14 montagens, sendo sete testadas em compressão axial e sete em flexão engastada. Em ambos os ensaios foram observados valores mais altos, em todas as variáveis avaliadas, na configuração sob carga axial do que na flexão engastada. Além disso, no ensaio em fadiga em compressão axial as montagens suportaram um maior número de ciclos. Foi possível concluir que pelos testes mecânicos, o modelo oferece suficiente estabilidade para resistir as cargas axiais no tratamento de fratura radial distal The aim of this study was to develop a locked T-plate to be used in distal radial fractures and evaluate the mechanical properties. A titanium 2.7 mm T-plate was designed with a shaft containing three locked screw holes and one dynamic compression hole, and a head with two locked screw holes. The head of the plate had an indentation and shaft had tapered-shaped end. Forty polyurethane blocks having a T-shaped and 20 titanium T-plates were used for mechanical testing. The bone plate was positioned over the polyurethane blocks with 2 mm fracture gap between the head and shaft of the plate. Six bone-plate constructs were tested until failure, three in axial compression and three in cantilever bending, to determine the loads for fatigue testing. Fourteen bone-plate constructs were tested for failure in fatigue, seven in axial compression and seven in cantilever bending. Fatigue failure was defined as polyurethane block breakage or pullout of the screws in the polyurethane block. Tests were discontinued after one million cycles if the construct had not already failed. In both static and fatigue testing, higher values of axial compression test than cantilever bending test were observed for all variables. Moreover, the constructs under fatigue axial compression test supported a larger number of cycles to failure. The locking Tplate tested has biomechanical properties that may offer sufficient stability to resist axial loads in the treatment of a distal radius fracture

Made available in DSpace on 2014-06-11T19:31:06Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-05-06Bitstream added on 2014-06-13T19:20:06Z : No. of bitstreams: 1 ribeirojunior_pd_dr_araca.pdf: 475855 bytes, checksum: 25027ddf9644c9757d0a760d4ed4ca58 (MD5) Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) Este estudo avaliou in vitro a influência do tipo de miniplaca (convencional ou locking) e do número de parafusos instalados no segmento ósseo distal e proximal para a promoção da estabilidade óssea e resistência da osteossínteses pelo método Champy, utilizada para o tratamento de fraturas de ângulo mandibular. Sessenta hemi-mandíbulas de poliuretano, com consistência similar ao osso mandibular, foram divididas em 4 grupos (n=15) e seccionadas na região de ângulo mandibular simulando uma fratura. Os segmentos ósseos foram fixados por diferentes tipos de miniplacas usando sistema 2.0- mm e parafusos monocorticais de 2.0 x 6.0mm. Nos grupos 1 e 2, dois parafusos convencionais (G1) ou locking (G2) foram instalados em cada segmento ósseo usando respectivamente miniplacas retas convencionais e locking; Nos grupos 3 e 4, três parafusos convencionais (G3) ou locking (G4) foram instados no segmento ósseo proximal e quatro parafusos convencionais (G3) ou locking (G4) foram instalados no segmento distal, usando uma miniplaca convencional (G3) e locking (G4) de sete furos, reta. As hemi-mandíbulas foram submetidas a um teste de compressão utilizando uma máquina universal de ensaio INSTRON até que houvesse um distanciamento entre os segmentos ósseos de 4 mm, seja no sentido horizontal ou vertical. Os dados registrados foram submetidos à avaliação estatística pelo método ANOVA e teste de Tukey utilizando um nível de significância de 1%. As miniplacas locking ofereceram maior resistência ao teste de compressão do que as miniplacas convencionais (p0.01). Apesar de não estatisticamente significante os resultados numéricos sugeriram que as miniplacas locking longas oferecem maior resistência ao teste de compressão que as miniplacas locking curtas. This study evaluated in vitro the influence of the type of miniplate (conventional or locking) and the number of screws installed in the proximal and distal segments on the stability and resistance of Champy’s osteosynthesis in mandibular angle fractures. Sixty polyurethane hemimandibles with bone-like consistency were randomly assigned to 4 groups (n=15) and sectioned in the mandibular angle region to simulate fracture. The bone segments were fixed by different osteosynthesis methods using 2.0-mm miniplates and 2.0 x 6 mm monocortical screws: Groups 1 and 2- Two conventional (G1) or locking (G2) screws were installed in each bone segment using either a conventional (G1) or a locking (G2) straight miniplate; Groups 3 and 4- Three conventional (G3) or locking (G4) screws were installed in the proximal segment and four conventional (G3) or locking (G4) screws were installed in the distal segment using a either a conventional (G3) or a locking (G4) 7-hole straight miniplate. The hemimandibles were loaded in compressive strength in an Instron machine until a 4-mm displacement occurred between the segments either vertically or horizontally. Data were analyzed statistically by ANOVA and Tukey’s test at 1% significance level. The locking plate/screw systems provided significantly greater resistance to displacement under compressive load than the conventional plate/screw systems (p0.01). In conclusion, the locking miniplates offered more resistance than conventional miniplates and long locking miniplates provided greater (number results) bone stability compared to short ones.