Search

Pengaruh penambahan karbon aktif tanah gambut terhadap kinerja superkapasitor berbahan dasar cangkang kelapa sawit telah dipelajari. Karbon aktif dari tanah gambut dibuat dengan menambahkan KOH 10 M dan dilakukan perendaman pada perbandingan massa 1: 4 antara karbon dengan KOH. Karbon aktif yang dihasilkan dikarakterisasi dengan XRD (X-Ray Difraksi), SEM-EDX (Scanning Elektron Microscopy-Energi Dispersive X - Ray), dan FTIR (Fourier Transform infrared Spektroscopy). Penambahan karbon aktif dari tanah gambut memberikan nilai kapasitansi meningkat menjadi 8063 kali lebih besar pada perbandingan masaa 1: 2 dengan luas luas pelat elektroda 3x3 cm2, konsentrasi elektrolit H3PO4 0,3 N dan waktu pengisian 15 menit. Pencampuran Karbon aktif dari tanah gambut dan cangkang kelapa sawit memiliki kinerja yang baik sebagai bahan elektroda superkapasitor.

Pengaruh aktivasi dengan KOH dan NaOH terhadap performance TiO2/C berpendukung keramik sebagai elektroda superkapasitor telah diteliti. Sintesis sol TiO2 dilakukan dengan menggunakan metode sol-gel. Membran keramik sebagai template penumbuhan TiO2/C yang diaktivasi dengan KOH dan NaOH disiapkan sebagai bahan elektroda superkapasitor dengan menggunakan elektrolit hidrogel polimer yaitu polivinil alkohol sebagai separator dan asam fosfat (H3PO4) sebagai elektrolit. Pengaruh aktivator NaOH memberikan peningkatan kapasitansi 1,5 kali lebih besar dibandingkan dengan aktivasi KOH. Nilai kapasitansi dengan aktivator NaOH adalah 14540 nF menggunakan konsentrasi elektrolit H3PO4 0,5 M dan waktu pengisian 30 menit dengan nilai konduktivitas sebesar 45,4 x 10-5 S/cm

The performance of palm kernel shells as a supercapasitor electrode material has been studied. The supercapasitor was assembled by plate/sandwich methods. Both electrodes were separated by using a PVA (Polyvinil Alcohol) as a separator. Potassium hydroxide, KOH 10 M was used as activator in order to increase the capacitancy value. Prepared activated carbon as electrode material was characterized by XRD, FTIR, SEM-EDX and SAA methods. The activated carbon has 15 times more larger surface area is 27.2253 m2/g than carbon without activated which is 1.829 m2/g. Supercapasitor was fabricated by variation of particle size, plat area, electrolyte concentration and charging time to obtain the maximum capacitancy value that is 48.2516 µF with 3x11 cm2 plat area, charging time is 35 min, and H3PO4 electrolyte concentration as 0.3 N. Keywords: EDLCs, electrode, supercapasitor, method of plate/sandwich, PVA, separator

Activated carbon from palm kernel shell can be used as supercapacitor electrodes. In this research studied the effect of delipidation treatment by using soxhletation methode to activated carbon and the effect of KOH as activator. The effect of delipidation and activation makes the preparation process of carbon from palm kernel shell becomes easily than without delipidation and activation treatment. The effect of delipidation on the performance of carbon from palm kernel shell as supercapacitor electrodes seen from the increase in specific surface area 7 times larger that is from 1,829 m2/g to 13,136 m2/g and a capacitance value increased 236,82 times that is 46,89 µF and conductivity as 9,016 x 10-5 Ω-1cm-1. Keywords : Aktivation, Capacitance, Carbon palm kernel shell, Delipidation, Supercapacitor.