Search

Svrha: Ispitati utjecaj protokola starenja na kemijski i fazni sastav te na kvalitetu površine monolitne translucentne cirkonij-oksidne keramike. Materijali i postupci: Translucentna cirkonij-oksidna keramika KATANA-Zirconia STML s različitom završnom obradom površine (bez obrade, K1, K2; glazirana, G1 – G8; polirana, P1 – P8) podvrgnuta je eksperimentalnim protokolima starenja (hidrotermalna degradacija u autoklavu na 134 °C, pri tlaku od 2 bara tijekom 3 sata: G1 – G4, P1 – P4 te kemijskoj degradaciji u 4-postotnoj octenoj kiselini na 80 °C tijekom 16 sati (ISO 6872): G5 – G8, P5 – P8) kako bi se utvrdio njihov utjecaj na kemijski sastav, osobito udio stabilizatora itrijeva oksida (energetsko disperzivna flourescencija X-zraka – EDXRF), fazni sastav (rendgenska difraktometrija – XRD) te stanje površine izraženo hrapavošću i sjajem. Rezultati: Protokoli starenja nisu utjecali na stabilnost kemijskog sastava testiranih uzoraka i visok udio stabilizatora itrijeva oksida (≥ 10 % ukupnog udjela) koji je u korelaciji s odsutnošću monoklinske faze. Statistički je značajno smanjenje sjaja površine svih uzoraka. Kemijska degradacija u korozivnom mediju značajno je povećala površinsku hrapavost testiranih uzoraka. Zaključak: Monolitna translucentna cirkonij-oksidna keramika pokazala je stabilnost kemijskog sastava i otpornost na tetragonsko-monoklinsku transformaciju. Sjaj površine značajno je smanjen, osobito na poliranim uzorcima. Suprotno testiranim glaziranim uzorcima, na testiranim poliranim uzorcima uočeno je povećanje hrapavosti površine. Glaziranje površine translucentne monolitne cirkonijeve keramike osigurava bolji estetski, tribološki i higijenski učinak u usporedbi s poliranjem., Objectives: To examine the effect of two aging protocols on the chemical and phase composition as well as the surface state of monolithic translucent zirconia ceramics. Material and Methods: Trans-lucent zirconia ceramics KATANA-Zirconia STML with different surface treatments (no treatment, K1, K2; glazed, G1-G8; polished, P1-P8) underwent testing in order to examine how the two aging protocols (three-hour hydrothermal degradation in an autoclave at 134 °C and 2 bars: G1-G4, P1-P4, and sixteen-hour chemical degradation in four-percent acetic acid at 80 °C (ISO 6872): G5-G8, P5-P8) affect chemical composition, particularly the share of stabilizing yttrium oxide (Energy Dispersive X-Ray Fluorescence – EDXRF), phase composition (X-ray diffraction – XRD) and surface state in terms of roughness and gloss. Results: Aging protocols did not affect the tested chemical composition stability of specimens and a high share of stabilizing yttrium-oxide (≥10% of total content), which correlates with the absence of monoclinic phase. A decrease in gloss on all specimens is statistically significant. Chemical degradation substantially increased the surface roughness of tested specimens. Conclusions: Translucent monolithic zirconia demonstrated a stable chemical composition and resistance to tetragonal-to-monoclinic transformation. Surface gloss was significantly reduced, especially in polished specimens. Contrary to glazed specimens, the tested polished specimens manifested an increase in surface roughness. Glazing the surface of translucent monolithic zirconia produces better esthetic, tribological and hygienic effects than polishing.