The aim of achieving integration of lightweight, high strength, high‐temperature resistant, and satisfactory electromagnetic (EM) wave absorption was successfully accomplished in the present study by synthesizing TiC–TiB2 fibers reinforced Si3N4 composites, which were pressureless sintered at 1650°C for 2 h. The preparation of TiC–TiB2 fibers was conducted through a chloride‐assisted carbothermic method. This work focused on investigating the effects of incorporating TiC–TiB2 fibers on the mechanical properties and EM wave absorption characteristics of the composites. The 30 wt% TiC–TiB2/Si3N4 composite displayed the bulk density of 1.89 g/cm3, bending strength of 93.11 ± 3.91 MPa, fracture toughness of 1.81 ± 0.10 MPa m1/2, minimum reflection loss of −38.87 dB, and effective absorption bandwidth of 1.43 GHz in the Ku‐band, respectively. The as‐synthesized TiC–TiB2/Si3N4 composites are promising candidates for EM wave absorbing load‐bearing materials due to their outstanding mechanical properties and microwave absorption properties. [ABSTRACT FROM AUTHOR]

The boron nitride nanosheets (BNNSs)/aluminum nitride (AlN) composites were prepared by hot press sintering at 1600°C. The microstructure, mechanical properties, and thermal conductivity of the samples were measured, and the effect of adding BNNSs to AlN ceramics on the properties was studied. It is found that the addition of BNNSs can effectively improve the mechanical properties of AlN. When the additional amount is 1 wt%, the bending strength of the sample reaches the maximum value of 456.6 MPa, which is 23.1% higher than that of the AlN sample without BNNSs. The fracture toughness of the sample is 4.47 MPa m1/2, a 68.7% improvement over the sample without BNNSs. The composites obtained in the experiment have brilliant mechanical properties. [ABSTRACT FROM AUTHOR]