Search

Three‐dimensional ceramic nanofiber‐assembled materials with large specific surface area and excellent thermal insulation properties are attracting increasing interests for their unique structure and promising applications. In this paper, we propose a facile methodology to fabricate three‐dimensional silicon nitride nanofiber‐knitted ceramic foams via in situ reactive synthesis from silicon foams. Silicon particle‐stabilized foams are fabricated for the first time using long‐chain surfactant cetyltrimethyl ammonium bromide as a hydrophobic modifier. First, the fabrication and stability of silicon foams are investigated. Based on the stable silicon foams, silicon nitride‐based nanofiber‐knitted ceramic foams are synthesized via in situ reactive sintering in nitrogen atmosphere. The novel ceramic foam materials consist of three‐dimensional nanofiber‐assembled strut wall and nanofiber‐spheres in the pores. The diameter of obtained silicon nitride nanofibers ranges from 15 to 100 nm. The unique nanofiber‐knitted foams may have potential applications in specific fields, including catalysis, adsorption, separation, and thermal insulation. [ABSTRACT FROM AUTHOR]

Abstract: A novel method for fabrication of highly porous barium strontium titanate (BST) ceramic foams based on particle‐stabilized foaming method was developed for the first time, in which propyl gallate (PG) was employed as BST particle modifier. The results showed that the stability of wet BST foams closely depends on the pH value and PG concentration, which could be explained by the adsorption behavior of PG on BST particle surface. BST ceramic foams with dense, uniform, and closed pore and defect‐free wall were obtained. The pore size and porosity can be well controlled by adjusting solid loading and sintering temperature. It was revealed that not only sintering temperature but also solid loading significantly influenced the growth of BST grain. The BST ceramic foams exhibited high porosity in the range of 81%‐95%, low dielectric constant in the range of 47‐150, and low dielectric loss below 0.0025. The BST ceramic foams with higher porosity presented a tendency of lower dielectric constant and the fitting results indicated that the natural logarithm of dielectric constant was linear correlated with porosity. [ABSTRACT FROM AUTHOR]

The weak compressive strength of dried ceramic foams is a disadvantage of fabricating ultralight ceramic foams, especially for the ceramic foams with porosity exceeding 95%. In this study, dried alumina foams were enhanced by agar and PVA-freezing-thawing using sodium dodecyl sulfate as surfactant. It is found that the two additives have no negative influence on adsorption of sodium dodecyl sulfate on alumina particles as well as the hydrophobic character of alumina particles. Stable alumina particle-stabilized foams were prepared with less than 0.5 wt% agar and 1.0 wt% PVA. High additive concentration above the critical values weakens stability of wet foams, which is probably due to the aggregate of alumina particles caused by long-chain molecules connecting. The compressive strength of dried alumina foams has a significant improvement with the employment of agar and PVA-freezing-thawing. The dried foams prepared with 1wt% PVA assisted by freezing-thawing has porosity of 97.1% and compressive strength of 0.16 MPa, which could maintain integrity of dried foams without destruction in the fabricating process. [ABSTRACT FROM AUTHOR]