This paper presents a simple experimental validation of a method for finding optimal application patterns in adhesive bonding, as previously introduced by Flaig et al. (2023). The study uses two examples to demonstrate that the patterns found in theory effectively fill the target gaps after pressing in practice. The results confirm that the identified application patterns fill the target gaps almost perfectly, ensuring excellent joint integrity after the pressing process. In particular, the applicability of the star pattern to fill square gaps is experimentally validated. In addition, the method of creating a rectangle by pressing a cut star connected by a straight beam is also effective. While the theoretical results in Flaig et al. (2023) were already promising, this research now provides experimental evidence of their practical applicability. [ABSTRACT FROM AUTHOR]

Mit den hier vorgestellten Ergebnissen an geklebten Holz‐Glas‐Proben aus Experimenten unter Kurz‐ und Langzeitbeanspruchung mit vielen Parametern (Holzsorte, Klebstoff, Temperaturen und Luftfeuchtigkeit) konnten neue Erkenntnisse gewonnen werden. Bei Zug‐ und Durckscherproben hat der Klebstoff den größeren Einfluss auf die Festigkeit. Die Temperatur bei 1K‐PU, Silanen und Acrylaten hat bis 60 °C einen signifikanten Einfluss auf die Festigkeit, bei 2K‐Epoxiden bis 80 °C keinen. In Verbundversuchen unter dauerhafter zyklischer Klimalagerung wurde deutlich, dass durch das Holzquellen Zugspannungen an der Glasaußenseite auftreten. Dies stellt eine ungünstige Belastungssituation für großflächig verklebte Glasscheiben dar, die bei Klebstoffen mit hoher Steifigkeit zu Rissen im Glas führen. Structural wood‐glass‐bonds under short‐ and long‐term loading. The results presented here on bonded wood‐glass specimens from experiments under short‐ and long‐term stress with many parameters (wood type, adhesive, temperatures, and humidity) provided new insights. In tensile and compression tests, the adhesive has the greater influence on the strength. The temperature has a significant influence on the strength of 1K PU, silanes and acrylates up to 60 °C, and none up to 80 °C for 2K epoxies. In composite tests under permanent cyclic climate storage, it became clear that tensile stresses occur on the outside of the glass due to wood swelling. This is an unfavourable load situation for glass panes bonded over a large area, which leads to cracks in the glass in the case of adhesives with high stiffness. [ABSTRACT FROM AUTHOR]