Search

The activation of molecular oxygen is a fundamental step in almost all catalytic oxidation reactions. We have studied this topic and the role of surface vacancies for Co 3 O 4 (100) films with a synergistic combination of experimental and theoretical methods. We show that the as-prepared surface is B-layer terminated and that mild reduction produces oxygen single and double vacancies in this layer. Oxygen adsorption experiments clearly reveal different superoxide species below room temperature. The superoxide desorbs below ca. 120 K from a vacancy-free surface and is not active for CO oxidation while superoxide on a surface with oxygen vacancies is stable up to ca. 270 K and can oxidize CO already at the low temperature of 120 K. The vacancies are not refilled by oxygen from the superoxide, which makes them suitable for long-term operation. Our joint experimental/theoretical effort highlights the relevance of surface vacancies in catalytic oxidation reactions., (© 2021 The Authors. Angewandte Chemie International Edition published by Wiley-VCH GmbH.)

Metalation of anchored porphyrins is essential for their functionality at hybrid interfaces. In this work, we have studied the anchoring and metalation of a functionalized porphyrin derivative, 5-(4-carboxyphenyl)-10,15,20-triphenylporphyrin (MCTPP), on an atomically-defined CoO(100) film under ultrahigh vacuum (UHV) conditions. We follow both the anchoring to the oxide surface and the self-metalation by surface Co 2+ ions via infrared reflection absorption spectroscopy (IRAS). At 150 K, MCTPP multilayer films adsorb molecularly on CoO(100) without anchoring to the surface. Upon heating to 195 K, the first layer of porphyrin molecules anchors via formation of a bridging surface carboxylate. Above 460 K, the MCTPP multilayer desorbs and only the anchored monolayer resides on the surface up to temperatures of 600 K approximately. The orientation of anchored MCTPP depends on the surface coverage. At low coverage, the MCTPP adopts a nearly flat-lying geometry, whereas an upright standing film is formed near the multilayer coverage. Self-metalation of MCTPP depends critically on the surface temperature, the coverage and on the molecular orientation. At 150 K, metalation is largely suppressed, while the degree of metalation increases with increasing temperature and reaches a value of around 60 % in the first monolayer at 450 K. At lower coverage higher metalation fractions (85 % and above) are observed, similar as for increasing temperature., (© 2020 The Authors. Published by Wiley-VCH GmbH.)

We have studied the adsorption and interfacial reactions of 2H-tetraphenylporphyrin (2HTPP) with cobalt-terminated Co 3 O 4 (111) and oxygen-terminated CoO(111) thin films using synchrotron-radiation X-ray photoelectron spectroscopy. Already at 275 K, we find evidence for the formation of a metalated species, most likely CoTPP, on both surfaces. The degree of self-metalation increases with temperature on both surfaces until 475 K, where the metalation is almost complete. At 575 K the porphyrin coverage decreases drastically on the reducible cobalt-terminated Co 3 O 4 (111) surface, while higher temperatures are needed on the non-reducible oxygen-terminated CoO(111). The low temperature self-metalation is similar to that observed on MgO(100) surfaces, but drastically different from that observed on TiO 2 (110), where no self-metalation is observed at room temperature., (© 2019 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.)

Metal-support interactions are frequently invoked to explain the enhanced catalytic activity of metal nanoparticles dispersed over reducible metal oxide supports, yet the atomic-scale mechanisms are rarely known. In this report, scanning tunneling microscopy was used to study a Pt1-6/Fe3O4 model catalyst exposed to CO, H2, O2, and mixtures thereof at 550 K. CO extracts lattice oxygen atoms at the cluster perimeter to form CO2, creating large holes in the metal oxide surface. H2 and O2 dissociate on the metal clusters and spill over onto the support. The former creates surface hydroxy groups, which react with the support, ultimately leading to the desorption of water, while oxygen atoms react with Fe from the bulk to create new Fe3O4(001) islands. The presence of the Pt is crucial because it catalyzes reactions that already occur on the bare iron oxide surface, but only at higher temperatures., (© 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.)