Ni 1 − x TixMnSb polycrystalline alloys in the range 0 ≤ x ≤ 0. 2 0 were synthesized employing the standard solid-phase synthesis method. The crystal, magnetic, as well as electrical properties of the alloys were investigated using neutron powder diffraction and magneto-resistance measurements. The results reveal that the substitution of Ti for Ni within the temperature range of 2.5–300 K does not induce alterations in the crystal and magnetic structures of NiMnSb. The ordered Ni magnetic moment approaches zero. The study of the electrical transport properties of the Ni 1 − x TixMnSb alloys, where 0 ≤ x ≤ 0. 2 0 , has demonstrated a half-metallic state at low temperatures and metallic conductivity for temperatures exceeding 160 K. A semiconductor state manifests at titanium concentrations of x = 0.2 and was observed at temperatures below 21 K. The obtained experimental results are elucidated through first-principles theoretical calculations. [ABSTRACT FROM AUTHOR]

The pressure-driven phase transformation in polycrystalline BaTi 1 − x FexO3 (x = 1 %), synthesized by a solid-state reaction method, was investigated using synchrotron X-ray diffraction and Raman spectroscopy. All measurements were performed at room temperature within a large pressure range up to 36.5 GPa. The results clearly demonstrate a phase transformation from the ferroelectric tetragonal structure of P4mm symmetry to the paraelectric cubic structure of Pm-3m symmetry in the studied sample at the pressure of about 18 GPa. This phase transformation pressure is much higher than those previously reported for BaTiO3-based systems, indicating the stabilization of the ferroelectric phase by doping 1% Fe into BaTiO3. Feature modes of the tetragonal phase still persist while some new modes appear in the Raman spectra at pressures above 18 GPa. This is probably due to accumulated stress and/or local microscopic disorders in the sample, which are associated with the displacement of the Ti atoms along unit-cell diagonals. [ABSTRACT FROM AUTHOR]