This paper examines the impact of the CO2 laser parameters on the tensile strength, which is one of the most important properties of paper packaging in the process of cutting paper material. The study was performed on a paper material sample Fbb Board/Ningbo Spark C1S Ivory Board by examination of the influence of four independent variables: paper material grammage, cutting speed, laser power, and resolution on the tensile strength by using definitive screening design. Optimum process conditions of four variables that maximize the tensile strength were predicted and validated accordingly. Results confirm that laser power, paper material grammage, and cutting speed are the main process parameters that mostly affect the tensile strength. Besides individual parameters, two statistically significant interactions were obtained: laser power and cutting speed, and cutting speed and laser resolution. Maximum tensile strength values (20.37 N/mm) were achieved using the laser power of 60.6%, cutting speed of 3.24%, resolution of 2500 Hz, and a paper material grammage of 326.85 g/m2. With laser power at middle values and at a lower speed, a maximum tensile strength value can be obtained. Increasing the laser power and cutting speed will produce a slight lowering of tensile strength. [ABSTRACT FROM AUTHOR]

Composite materials have been widely used because of their superior properties compared to those of the original material. Separation of the constituent materials is not easy in the recycling process, and such an effort lowers economic viability. As such, this study employed a pyrolysis as a valorizing method for the composite material. Disposable paper cup waste (DPCW) was chosen as the model compound for paper-plastic composites. To offer green/sustainable features, CO2 was employed as a raw and reactive material in the pyrolysis process. It was proved that DPCW primarily composed of cellulose (outer layer) and polyethylene (inner layer). In the single-stage and multistage pyrolysis of DPCW, the CO2 reactivity in the homogeneous reaction of CO2 and DPCW-derived volatiles was not rapid. To accelerate the reaction kinetics governing the reactivity of CO2, the catalytic pyrolysis of DPCW over Ni/SiO2 was performed. The formation of syngas increases significantly, suggesting that CO2 reactivity was catalytically enhanced. The generation of syngas (enhanced by CO2) was inversely related to the DPCW oil generation, indicating that more carbon was assigned from the oil to the gaseous pyrogenic products. The study results would offer a strategic means to valorize paper-plastic composites and CO2 into energy through pyrolysis. [ABSTRACT FROM AUTHOR]

Flexible calcium carbonate (FCC) was developed as a functional papermaking filler for high loaded paper, which was a fiber-like shaped calcium carbonate produced from the in situ carbonation process on the cellulose micro-or nanofibril surface. Chitin is the second most abundant renewable material after cellulose. In this study, a chitin microfibril was utilized as the fibril core for making the FCC. Cellulose fibrils for the preparation of FCC were obtained by fibrillation of the TEMPO (2,2,6,6-tetramethylpiperidine-1-oxyl radical) treated wood fibers. The chitin fibril was obtained from the β-chitin from the born of squid fibrillated in water by grinding. Both fibrils were mixed with calcium oxide and underwent a carbonation process by the addition of carbon dioxide, thus the calcium carbonate attached on the fibrils to make FCC. When used in papermaking, both the FCC from chitin and cellulose gave a much higher bulk and tensile strength simultaneously than the conventional papermaking filler of ground calcium carbonate, while maintaining the other essential properties of paper. The FCC from chitin caused an even higher bulk and higher tensile strength than those of the FCC from cellulose in paper materials. Furthermore, the simple preparation method of the chitin FCC in comparison with the cellulose FCC may enable a reduction in the use of wood fibers, process energy, and the production cost of paper materials. [ABSTRACT FROM AUTHOR]

A free-standing cathode without any binder, conductor, and current collector is attractive due to its reduced weight and cost. This study introduces nitrogen-rich and hierarchical porous carbon fibers in the form of a free-standing carbon paper synthesized by NaBH 4 -aided electrospinning and subsequent CO 2 annealing. This modified process leads to a large mesopore volume of 1.007 cm3 g−1 and exposes the nitrogen inside the polymer to the surface of the fiber, resulting in the outstanding surface nitrogen content of 19.38 wt% with abundant pyridinic-N and pyrrolic-N of 16.24 wt% in total surface atoms, while eliminating any further treatment for increasing porosity or coating the polar active sites. The resultant material impregnated by sulfur and filtered by a graphene solution is directly employed as a cathode without any additives. As a result, the capacity is maintained at 696 mAh g−1 up to the 500th cycle at 0.2 C, and 645 mAh g−1 at a high current density of 5.0 C. Even with a high sulfur loading of 6.11 mg cm−2, a remarkable areal capacity of 3.09 mAh cm−2 is recorded after 500 cycles at 0.2 C with the free-standing form preserved. Image 1 • NaBH 4 -added electrospinning and subsequent heat treatment under CO 2 atmosphere. • High meso pore volume of 1.007 cm3 g−1, and surface nitrogen contents of 19.38 wt%. • Employed as a cathode without any additives due to a free-standing paper form. • High sulfur amount of 6.11 mg cm−2, and capacity of 3.09 mAh cm−2 for 500 cycles. [ABSTRACT FROM AUTHOR]

For the electro-reduction of CO 2 to syngas, the fabrication of electrodes with excellent and adjustable catalytic performance is a critical step. In this work, Ni particles encapsulated in N-doped carbon nanotubes on carbon paper (Ni@N-CNTs/CP) composites were designed and prepared via an in-situ chemical vapor deposition method. As confirmed by different characterization techniques, the Ni@N-CNTs are successfully synthesized, and the surface of the CP is evenly covered by the Ni@N-CNTs. The effects of Ni content and treating temperature on the textural properties of composites are carefully investigated. The Ni@N-CNTs/CP composites are directly employed as the electrode for electro-reduction of CO 2 , and the action mechanisms of the N species, Ni particles, and N-CNTs structure are explored as well. The electrode exhibits excellent catalytic activity and high stability, reaching a specific current of 10 mA cm−2. The H 2 /CO ratio in the achieved syngas can be tuned in the range of 5/1 to 1/1.5. Image 1 • A in-situ CVD method was employed to fabricate an electrode for electro-reduction of CO 2. • The as-synthesized Ni@N-CNTs evenly cover on the whole surface of CP. • The Ni@N-CNTs/CP electrode exhibits high CO 2 reduction activity and stability. • The ratio of H 2 /CO can be adjusted in the range of 5/1 to 1/1.5. • The action mechanism of different components are detailedly investigated. [ABSTRACT FROM AUTHOR]

Lime mud, a kind of industrial waste that produced in paper mill, was proposed as CO2 sorbent in calcium looping process. The carbonation performance of the lime mud was investigated in a dual‐fixed bed reactor (DFR) and a thermogravimetric analyzer (TGA). The carbonation kinetics of the lime mud in the chemical reaction controlled stage was analyzed by a surface reaction‐controlled kinetic model. The results show that the lime mud presents much poorer carbonation performance during the chemical reaction controlled stage compared with the limestone, mainly due to the high content of chlorine in the lime mud. A prewash treatment process was used to decrease the chlorine content to mitigate the sintering of the lime mud when calcined at high temperature. After prewash treatment, the prewashed lime mud shows much higher CO2 capture capacity during the chemical reaction controlled stage compared with the lime mud. A prolonged carbonation process successfully further enhances the microstructure and improves the carbonation performance of the prewashed lime mud in the chemical reaction controlled stage. The lime mud can be effectively used as CO2 sorbent in calcium looping process after prewash treatment and the following prolonged carbonation treatment. [ABSTRACT FROM AUTHOR]

Zinc nanoparticles were electro-deposited along the fibres of carbon paper (CP) substrate uniformly in a salt-induced pre-phase separation region solution. The as-prepared Zn/CP electrode was used for electro-reduction of CO 2 and exhibited a Faradaic efficiency towards CO of 97.6% with a current density of 340 mA cm−2 in an H-type cell, which is the best result to date. [Display omitted] Efficient electrode design is crucial for the electrochemical reduction of CO 2 to produce valuable chemicals. The solution used for the preparation of electrodes can affect their overall properties, which in turn determine the reaction efficiency. In this work, we report that transition metal salts could induce the change of two-phase ionic liquid/ethanol mixture into miscible one phase. Pre-phase separation region near the phase boundary of the ternary system was observed. Zinc nanoparticles were electro-deposited along the fibres of carbon paper (CP) substrate uniformly in the salt-induced pre-phase separation region solution. The as-prepared Zn(1)/CP electrode exhibits super-wettability to the electrolyte, rendering very high catalytic performance for CO 2 electro-reduction, and the Faradaic efficiency towards CO is 97.6% with a current density of 340 mA cm −2, which is the best result to date in an H-type cell. [ABSTRACT FROM AUTHOR]

Pulp and paper mill sludge (PPMS) is applied on agricultural soils as an organic fertilizer. Although it is well accepted that land application of PPMS has benefits for soils and crops, information on PPMS-induced soil N 2 O emissions is still limited. We assessed the effect of substituting mineral N fertilizer for PPMS on soil N 2 O emissions after a single application at planting on a clay loam cropped to wheat ( Triticum aestivum L.) over two snow-free seasons in eastern Canada. Fertilization treatments consisted of 0, 25, 50, 75, and 100% of crop N requirements derived from N supplied by PPMS, the remaining N being supplied as urea-N. Soil CO 2 and CH 4 emissions were also measured and not affected by the fertilizer addition; a slight CH 4 oxidation occurred. Area-based N 2 O emissions from PPMS fertilization (4.4 to 12.1 kg N 2 O-N ha −1 ) were similar or higher than from urea alone (3.4 and 6.2 kg N 2 O-N ha −1 ). Although crop yields were not affected by the type of fertilizer, yield-based N 2 O emissions, N uptake efficiency and N surplus (applied N minus aboveground N uptake in crop biomass) indicated that N availability from the mineral fertilizer was higher than from PPMS for the wheat crop. However, treatments with PPMS had fertilizer-induced N 2 O emission factors (FIEF, applied N lost as N 2 O-N; 0.8 to 3.1%) similar to urea alone (−0.3 and 4.5%). Although substituting urea-N with PPMS in agricultural fields might reduce N 2 O emissions under moderate soil moisture conditions, PPMS land application produced greater N 2 O emissions under high soil moisture conditions. Further research on a variety of agricultural practices is needed before concluding that including PPMS in the fertilization plan could result in a global GHG abatement as compared to mineral fertilizers under the cool climate of eastern Canada. [ABSTRACT FROM AUTHOR]

Utilization of the quality-upgraded waste paper in the manufacture of paper and board will reduce the wood consumption and pulping energy. While the optical property of the fibers from recycled old newspaper is very poor, in-situ calcium carbonate formation on those fibers by injecting carbon dioxide to the mixed slurry of those pulp and calcium oxide improved their brightness. Upgrading recycled old newspaper to substitute more expensive wood furnish, such as recycled old magazine, was successfully demonstrated in the present study. This study showed that the in-situ calcium carbonate formation process improved the optical quality of the recycled old newspaper by covering colored impurities with newly formed calcium carbonate, and improved calcium carbonate retention in papermaking process by attaching them to fibers. The strength reduction by the presence of newly formed calcium carbonate in the paper was recovered by adding strength agent. High ash retention at high ash content under the strong turbulence in the modern paper mill was achieved by the application of the in-situ calcium carbonate formation method. The quality-upgrade of recycled fibers and cost saving in the manufacture of duplex paperboard were demonstrated in the mill trial. [ABSTRACT FROM AUTHOR]

Highlights • Sizing of paper is carried out using liquid CO 2 as an alternative medium. • Sucrose Octaacetate (SOA) is used as a CO 2 -philic and renewable size compound. • The method is inherently dry and industrially viable. • The SOA-coated surface shows reduced optical reflectance. • The sized paper shows enhanced non-wetting nature and improved mechanical properties. Abstract The development of low cost, non-fluorous, CO 2 -philic materials such as sugar acetates have opened up new opportunities for enabling the utilization of liquid and supercritical carbon dioxide (scCO 2) as a green solvent platform for industrial processes by virtue of the high solubility of these materials in CO 2. In the present work, we report the sizing of paper surface with sucrose octaacetate (SOA) using this alternative solvent system. Characterization of the bare and sized paper samples has been carried out using spectroscopic and surface imaging techniques. The studies reveal a smooth and uniform coating of the surface with SOA. Contact angle measurements and sorption studies show that the SOA-coated paper surface is hydrophobic. The mechanical properties of the SOA-coated paper are observed to be superior to that of the uncoated one. Since the solvent and the size can be completely recycled, this can be developed into an industrially viable green technology. [ABSTRACT FROM AUTHOR]

A scalable papermaking process was employed herein to manufacture cellulosic papers from native and phosphorylated cellulose microfibers (referred to as CMF and PCMF, respectively) impregnated with polyethyleneimine (PEI) for Direct Air Capture (DAC) applications. These papers were analyzed in terms of their physico-chemical properties using several techniques. The impact of PEI content on desorbing the co-adsorbed H 2 O and CO 2 from the air, as well as on the anisotropic microporous network, was explicitly analyzed. The results indicated that phosphorylation promotes the uptake of both CO 2 and H 2 O in the corresponding neat and PEI-loaded papers, reaching a superior CO 2 adsorption capacity of ∼0.7–0.9 mmol.g−1 for PCMF papers versus 0.07–0.3 mmol.g−1 for CMF papers. Furthermore, the CMF and PCMF papers exhibited H 2 O adsorption capacities in the range of 1.5–1.8 mmol.g−1 and 2.2–3.8 mmol.g−1, respectively. This work further highlights the combined role of phosphorylation and favorable PEI impregnation in tuning the cellulose CO 2 adsorption properties under humid conditions, facilitating the rapid release of the adsorbed CO 2 under mid conditions. [Display omitted] • Manufacturing of scalable solid cellulosic papers with amine functionalities and enhanced carbon capture. • Microstructural and chemical characterization of amine functionalized paper with various amine ratios. • Valorization of Alfa biomass in Carbon capture applications. • The combined role of phosphorylation and PEI impregnation in tuning the H 2 O and CO 2 co-adsorption properties. [ABSTRACT FROM AUTHOR]

Hybrid calcium carbonate (HCC) is prepared by pre-flocculating calcium oxide and ground calcium carbonate (GCC) with ionic polymers, and by injecting carbon dioxide to the pre-flocculated flocs until termination of the reaction at neutral pH. When used in papermaking, HCC gave higher bulk, higher stiffness, and higher tensile strength than GCC did. Furthermore, when higher wet pressing pressure was applied to the paper containing HCC, higher solid content was achieved with still better stiffness, smoothness, and tensile strength in comparison with the paper containing GCC. Actually, very high bulk of the HCC containing paper was compromisingly reduced to obtain high solid content by applying higher wet pressing pressure. Higher solid content achieved by combination of HCC technology and higher wet pressing pressure resulted in paper drying energy savings of more than 10%, while a high quality of all the essential printing paper properties was maintained. Drying energy savings may contribute to greenhouse gas (GHG) reduction and lowering of the paper production cost. [ABSTRACT FROM AUTHOR]

Pyrolysis of paper mill sludge (PMS) was conducted to produce syngas (H 2 and CO) and fabricate magnetic biochar (PMS biochar) for use as an adsorbent for As(V). The enhanced generation of CO was observed in the CO 2 atmosphere due to reactions triggered by CO 2 . Particularly, the generation of syngas from pyrolysis of PMS in CO 2 (9.6 mol% at 720 °C) was superior to the cases of pyrolysis of acid-washed PMS ( i.e. , minerals-eliminated PMS) in CO 2 (2.9 mol% at 720 °C), which evidences catalytic effects attributed by Fe and Ca species contained in PMS. Based on the results of X-ray diffraction (XRD), pyrolysis of PMS in CO 2 led to the conversion of Fe species into magnetite (Fe 3 O 4 ) solid phase that imparted the magnetic property to the biochar (saturation magnetization: 28.4 emu g −1 ). The PMS biochar exhibited high As(V) adsorption capacity of 34.1 mg g −1 in a given condition, which could be attributed to the great adsorption affinity of Fe 3 O 4 /CaCO 3 mixture toward As(V). The integrated approach for the utilization of PMS could satisfy growing demand for renewable energy and environmental sustainability. [ABSTRACT FROM AUTHOR]

Highlights: [•] Carbon monoxide is one of the key toxic components in cigarette mainstream smoke. [•] Carbon dioxide delivery can be discouraged by engineering of cigarette paper. [•] The relevant concepts on engineering of cigarette paper are reviewed. [ABSTRACT FROM AUTHOR]

Research Highlights: Long-term exposure of paper birch to elevated carbon dioxide (CO2) and ozone (O3) modified metabolite content of over-wintering buds, but no evidence of reduced freezing tolerance was found. Background and Objectives: Atmospheric change may affect the metabolite composition of over-wintering buds and, in turn, impact growth onset and stress tolerance of perennial plant species in spring. Materials and Methods: Low molecular weight compounds of paper birch (Betula papyrifera) buds, including lipophilic, polar and phenolic compounds were analyzed, and freezing tolerance (FT) of the buds was determined prior to bud break after 11 growing seasons exposure of saplings to elevated concentrations of CO2 (target concentration 560 µL L−1) and O3 (target concentration 1.5 × ambient) at the Aspen FACE (Free-Air CO2 and O3 Enrichment) facility. Results: The contents of lipophilic and phenolic compounds (but not polar compounds) were affected by elevated CO2 and elevated O3 in an interactive manner. Elevated O3 reduced the content of lipids and increased that of phenolic compounds under ambient CO2 by reallocating carbon from biosynthesis of terpenoids to that of phenolic acids. In comparison, elevated CO2 had only a minor effect on lipophilic and polar compounds, but it increased the content of phenolic compounds under ambient O3 by increasing the content of phenolic acids, while the content of flavonols was reduced. Conclusions: Based on the freezing test and metabolite data, there was no evidence of altered FT in the over-wintering buds. The impacts of the alterations of bud metabolite contents on the growth and defense responses of birches during early growth in spring need to be uncovered in future experiments.

Electric‐driven conversion of carbon dioxide (CO2) to carbon monoxide (CO) under mild reaction conditions offers a promising approach to mitigate the greenhouse effect and the energy crisis. Surface engineering is believed to be one of the prospective methods for enhancing the electrocatalytic activity of CO2 reduction. Herein, hydroxyl (OH) groups were successfully introduced to cadmium nanosheets to form cadmium and cadmium hydroxide nanocomposites (i. e. Cd/Cd(OH)2 nanosheets) via a facile two‐step method. The as‐prepared Cd/Cd(OH)2/CP (CP indicates carbon paper) electrode displays excellent electrocatalytic activity for CO2 reduction to produce CO. The Faradaic efficiency of CO reaches 98.3 % and the current density achieves 23.8 mA cm−2 at −2.0 V vs. Ag/Ag+ in a CO2‐saturated 30 wt% 1‐butyl‐3‐methylimidazole hexafluorophosphate ([Bmim]PF6)‐65 wt% acetonitrile (CH3CN)‐5 wt% water (H2O) electrolyte. And the CO partial current density can reach up to 71.6 mA cm−2 with the CO Faradaic efficiency of more than 85 % at −2.3 V vs. Ag/Ag+, which stands out against Cd/CP, Cd(OH)2/CP, and Cd/CdO/CP electrodes. The excellent electrocatalytic performance of the Cd/Cd(OH)2/CP electrode can be attributed to its unique structural properties, suitable OH groups, perfect interaction with electrolyte, abundant active sites and fast electron transfer rate. [ABSTRACT FROM AUTHOR]

This study estimated paper and paperboard demand, pulpwood demand, and carbon dioxide (CO2) emissions from production of paper and paperboard through 2050 in ten Asian countries. Under scenarios of varying population, gross domestic product (GDP), and per capita paper and paperboard demand, we analyzed the relationship between economic growth and consumption of paper and paperboard. We also evaluated options to reduce CO2 emissions through increased use of black liquor, waste paper pulping, and wood chemical pulping, as well as improvements in pulp, paper, and paperboard production technology. The quadratic curve model (inverted U) for per capita consumption of paper and paperboard against per capita GDP resulted in significant regression coefficients and higher adjusted R2 values than linear and logarithmic curve models for all uses of paper and paperboard. The estimated paper and paperboard demand in the ten countries in 2050 ranged from 112% (328%) to 156% (454%) of total 2005 consumption for the world (for the ten Asian countries). Of this estimated paper and paperboard demand, China accounted for about 50% and India 20%. The estimated pulpwood demand in these ten countries in 2050 ranged from 13% (48%) to 21% (84%) of global (ten country) 2005 wood supply potential. The introduction or increase of the use of black liquor, waste paper pulping, the combination of wood chemical pulping and black liquor, and technological improvements produced CO2 reductions of 24%, 5%, 32%, and 25%, respectively, compared to 2050 emission levels in the no-measure (unadjusted) option, assuming sustainable forest management. [ABSTRACT FROM AUTHOR]

A recent commentary by Santhosh and Ravindran on our paper (Int. J. Hydrogen Energy 2014, 39:10,606) demonstrated that the interaction between H 2 and MXene (Sc 2 C and Ti 2 C) phases are not Kubas-type and should be of weak physisorption, and thus made a conclusion that 2D Sc 2 C and Ti 2 C are not suitable for practical hydrogen storage applications. In this responses, we recalculated hydrogen adsorption on 2D Sc 2 C and Ti 2 C by using different exchange-correlation functionals. And based on the calculated results, bare MXenes (especially the Ti 2 C) are suitable as hydrogen storage materials at temperatures of several tens degrees lower than room temperature. And the hydrogen adsorptions on the MXenes terminated with oxygen group were also investigated. Among the Ti 2 C, Sc 2 C and their oxygen-functional counterparts, the binding energy of H 2 on Sc 2 CO 2 surface is the closest to the ideal range of 0.16–0.42 eV/H 2 at ambient conditions, and thus the Sc 2 C with oxygen group is expected to be more suitable as hydrogen storage materials. [ABSTRACT FROM AUTHOR]

The Swedish pulp and paper industry accounts for half of industrial final energy use in Sweden and 2.3 % in EU-27. On the basis of a disaggregated set of physical production data, a Logarithmic Mean Divisia Index decomposition method is applied to disentangle the influence from activity, structure and energy efficiency improvement (EEI) on its fuel, electricity and primary energy use. An extended analysis tracks the fossil energy use and carbon dioxide (CO) emissions to discern past and present developments of industrial decarbonisation. In 1984-2011, the total production output increased by 49 %, whereas growth in primary energy use was limited to 26 %. Compared with an activity-based scenario, 50 PJ of primary energy use has been avoided through EEI and 6 PJ through structural change. The production has become oriented towards more electricity-intensive but less fuel-intensive segments. The electricity use EEI was negligible until year 2000 but sizeable thereafter as it started to outpace the counteracting impact from structural change. Results are consistent with previous bottom-up evaluations, and the policy context is further elaborated in a discussion about the role of relevant energy and climate policies in facilitating the enhanced EEI observed over the last decade. [ABSTRACT FROM AUTHOR]

This work presents an unconventional use of capacitively coupled contactless conductivity detector (C4D) for detection of gas absorption by moist paper with potential application for chemical analysis. To be suitable for measuring conductivity of moist paper absorbent, the C4D sensor was therefore designed in planar configuration. A layer of dry filter paper, only 20 mm × 25 mm in size, was placed on the C4D sensor and the device installed inside a specifically designed vaporization chamber. A vial (16 mm i.d., 8 mm high) containing a 150-μL solution of sodium bicarbonate was placed alongside. The filter paper was loaded with 110 μL of deionized water through an injection hole in the cover lid. A 100-μL aliquot of 2 M hydrochloric acid solution was directly dispensed into the vial through a second hole in the lid to generate CO 2 gas from the bicarbonate solution. It was observed that the C4D sensor gave real-time response that corresponded to the absorption of the gas and subsequent production of H+ and HCO 3 − in the moist paper. The monitored signal reached a constant value at 160 s after the addition of the acid. Chemistry of the absorption process and equivalent circuit for the C4D are proposed. Direct measurement of cement powder was chosen to demonstrate the potential use of this device for quantifying the CaCO 3 content of the cement. The calibration curve for 0.5–3 mg CaCO 3 was linear for signals recorded at 160 s: V dc = (0.172 ± 0.005) · (mg CaCO 3) + (0.016 ± 0.009), with coefficient of determination of 0.9965. Linear calibrations were also observed when the signals were monitored at various time less than 160 s. The limit of quantitation (3 SD of intercept/slope) was 0.17 mg CaCO 3. The method provided acceptable precision with %RSD of 4.6 (2 mg CaCO 3 , n = 10). Image 1 • Unconventional use of planar contactless conductivity detector is presented. • Real-time in-situ detection of CO 2 absorption by moist paper was demonstrated. • The absorption chemistry by moist paper and C4D equivalent circuit are proposed. • Potential application in direct measurement of cement powder is demonstrated. [ABSTRACT FROM AUTHOR]

• Black liquor gasification was coupled with calcium looping. • Calcium looping for CO 2 capture and H 2 production was compared. • CO 2 capture route (39 €/t) was less expensive than H 2 production route (48.8 €/t). • CO 2 avoided cost was highly dependent on capital cost of black liquor gasification. • Export of H 2 had the lowest CO 2 avoided cost among black liquor gasification cases. Although considered one of the major energy-intensive industries (EIIs), the pulp and paper industry has also the potential for energy production from an industrial waste, black liquor. This study proposes black liquor gasification (BLG) coupled with calcium looping (CaL) as a CO 2 capture route for the pulp and paper industry. BLG with H 2 production (BLG-CaL-H 2), BLG with gas turbine combined cycle (BLG-CaL-GT) or with solid oxide fuel cell (BLG-CaL-SOFC) were considered. The dependence of carbon capture and storage (CCS) cost on the natural gas, limestone, electricity imported and H 2 sale prices aside the expenditures related with BLG-CaL were evaluated. The CCS route, based on CaL retrofitted to the pulp and paper plant, was found to have a lower cost of CO 2 avoided (39.0 €/tCO 2) when compared with BLG-CaL (48.8–57.1 €/tCO 2). Between the BLG-CaL scenarios, BLG-CaL-H 2 presented the lowest cost of CO 2 avoided (48.8 €/tCO 2) but the highest energy penalty. Based on the thermodynamic performance, it was shown that CaL retrofit and BLG-CaL-SOFC presented the best overall performance, turning the electricity importer reference plant into electricity exporter. The economic sensitivity showed that the capital requirement of BLG-CaL has a strong effect on the cost of CO 2 avoided for all alternatives. The H 2 production is also strongly affected by the H 2 sale price while BLG-CaL-SOFC and BLG-CaL-GT are strongly dependent on natural gas price. [ABSTRACT FROM AUTHOR]

In 2017, a carbon emissions trading market will be launched nationwide by the China government. Calculating the enterprise carbon emissions is an important prerequisite and basis for trading. This paper discussed types of greenhouse gases, calculation boundaries and methods, energy consumption, carbon emissions, and intensity of a representative integrated pulp and paper mill in China based on China Guidance and Greenhouse Gas Protocol Tools. The results showed that there were 435,000 tonnes (t) of CO2 emissions from that mill in 2014 that did not contain emissions of biomass energy, which was 8 times higher than that of fossil energy. The pulp carbon intensity based on the mill was 0.230 t CO2/Adt, which accounted for 7.50% to 57.4% in other pulps' based on the product. Intensity based on Gross Domestic Product (GDP) was 1.090 t CO2e/1000 USD and accounted for 56.8% intensity in the China paper industry. The intensity based on sales accounted for 52.6% in the firstclass enterprise in the developed country. It also showed that intensity was influenced by the species of raw material, energy, and products, which provided the mill with measures for energy saving and emissions reduction to obtain the redundant carbon emissions in the trading. [ABSTRACT FROM AUTHOR]

The combustion of biomass and waste paper sludge in a fluidized bed is ecologically profitable. However, a large amount of by-product with high hydraulic reactivity is produced and is considered as wastes. Most of the time the waste paper fly ash (WPFA) goes to landfills, therefore new utilization methods are necessary. In some countries, the high content of metallic and metalloids trace elements (MMTE) in WPFA, more specifically Barium (Ba) and Lead (Pb) makes its valorization difficult. In this paper, the Lightweight Aggregates (LWA) was produced from WPFA by granulating with water in high-intensity granulator. Since WPFA is rich in CaO, the addition of water promotes rapid setting and hydration compared to other types of ash. In this study, different granulation parameters were investigated, such as the rotation modes between the steel pan and the impeller, the rotation speed of the steel pan, the granulation time, in order to improve the mass percentage of the targeted LWA (2–16 mm). In order to evolve the immobilization potential of Ba and Pb, a carbonation process was performed, exposing the manufactured LWA to pure carbon dioxide (CO 2) gas at laboratory scale. The physical, morphological, thermal and mechanical characterizations were performed on LWA for use in mortars, concretes or civil engineering constructions. Results have demonstrated the influence of the rotation mode between the steel pan and the on the distribution of WPFA inside the steel pan and the change in the growth rate of the granules can be observed. Increased density and improved compressive strength with low porosity and water absorption were also found in LWA after carbonation. This was due to the occurrence of both a carbonation reaction and a hydration reaction. Furthermore, the results of thermogravimetry and SEM-EDS confirmed the formation of hydrated phases (ettringite, carboaluminates), also the formation of calcite in the pores and the external surface of the LWA. Regarding environmental aspects, the results have revealed that Ba and Pb were well immobilized in the solid matrix after carbonation. [Display omitted] • LWA was manufactured from WPA without any agglomerating agents. • The physical-chemical properties of LWA were improved after carbonation. • The resulted LWA meet the requirements of NF EN -13,055-1. • The microstructure of LWA was studied before and after carbonation. • Influence of time, mode and rotation speed on the size of the manufactured LWA. [ABSTRACT FROM AUTHOR]

A completely lab-made paper/graphene-based 3D pop-up device (3D-PP) for the analysis of carbaryl (CBR), a pesticide widely used in crop production, is proposed. The device is composed of a nitrocellulose sensor equipped with reduced graphene oxide (rGO) and a foldable 3D paper pop-up. The rationale of the device is based on 3D and 2D configurations to allow the whole analytical procedure. In the 3D arrangement sample pre-concentration and hydrolysis occur; after folding (2D), contact with the complementary nitrocellulose-based sensor is ensured. The sensor, constituted by nanostructured graphene film, allows to obtain the necessary electroanalytical performance. 3D-PP has been shaped and nanostructured using a CO 2 -laser plotter and finished using low-cost benchtop instruments, ensuring in-series manufacturing of the device modules. 3D-PP includes the main steps required for CBR determination, i.e. (i) pre-concentration/purification, (ii) hydrolysis, (iii) medium neutralization, and (iv) electrochemical detection. 3D-PP was challenged for CBR quantification in model solutions and different grain samples. The response linearity (1.5–33 μM) and LOD (0.4 μM) obtained ensures CBR determination at the European-law admitted maximum residue levels (MRL). As proof of applicability, to simulate contaminates samples, different grains (i.e. soft and durum wheat, kamut, and barley) were spiked, before extraction, with CBR at three concentration levels corresponding to 0.5x, 1x, and 1.5x MRL; in all cases, quantitative and reproducible recoveries were obtained (93–109%; RSD ≤ 6%, n = 3). 3D-PP is produced using cellulosic components and solvent-free approaches, includes all CBR analysis steps, and returns reliable results in 15 min, resulting portable and usable with a smartphone [Display omitted] • A paper/graphene-based device for integrated carbaryl (CBR) analysis is proposed. • CO 2 -laser was used to shape and nanostructure the paper-based platform. • Complete CBR analysis is strategically enclosed in a 3D foldable paper pop-up (3D-PP). • 3D-PP design and sensing ability allow CBR residues analysis at EU-law limits. • 3D-PP analysis ability was proven in soft and durum wheat, kamut, and barley. [ABSTRACT FROM AUTHOR]

Abstract: The pulp and paper industry both uses and produces large amounts of energy and rising fuel prices bring along significant challenges to the sector. Several strategies can be applied in order to remain competitive e.g. an increase in energy efficiency, a switch in fuel and/or a novel energy conversion technology. In this study, we investigate if improved energy conversion strategies can reduce energy costs, primary energy use and CO2 emissions of paper mills within different European countries (The Netherlands, Poland and Sweden). Our results show that differences in history and availability of resources has led to different conversion strategies in the three countries. We found that a natural gas combined cycle, which is largely implemented in The Netherlands due to long term domestic availability of natural gas, has the lowest primary energy demand. Due to a long history of low electricity prices, CHP has not been common in Sweden. Many Swedish mills use biomass as an energy source and due to low CO2 emissions of the national grid the CO2 emission profile of the Swedish paper industry is very low. Our results imply that future conversion routes for the Swedish paper and board industry are again wood based; in case of increasing electricity prices these would be biomass gasification based CHP solutions. With a reduction of 800kg CO2/ton paper on average, a switch from coal to biomass would reduce CO2 emissions in the Polish pulp and paper industry with approximately 0.6Mton/year. A carbon price of 20–25€/ton would, according to our results, be enough to provoke this switch. Due to the high share of natural gas, the CO2 emission reduction potential of the Dutch paper industry (1.5Mton/year) is even larger than in Poland. Due to high biomass prices and relative low CO2 emission profile of natural gas, a carbon prices of more than 60€/ton CO2 would be needed to provoke a switch in The Netherlands. Provided with few alternatives, the most effective strategy in The Netherlands would be an increase in energy efficiency. [Copyright &y& Elsevier]

In this paper an approach for analysing the potential for implementation of different technology pathways for the European pulp and paper industry (PPI) is presented. The approach is based on detailed technical research and aggregates the knowledge from previous studies to incorporate the whole European PPI. Thus, the potential for different technology pathways can be estimated on a European level whilst still considering important characteristics of individual mills. The usefulness of the approach was exemplified by applying it to a case study of the potential for introduction of carbon capture and storage (CCS) within the European PPI. The results from the case study show that for the European PPI, CCS has an up-hill road in order to be a viable, large scale alternative for reduction of CO2 emissions. If CCS is to be introduced in large scale within the European PPI, large biomass-based point sources of CO2 emissions need to be included when planning for CCS infrastructure and also the infrastructure needs to be built out for clusters emitting <20 MtCO2/yr. [ABSTRACT FROM AUTHOR]

The present study investigated the fresh, hardened, and physicochemical properties of CO 2 -cured belite-rich cement (BRC) paste incorporating hygiene tissue paper (HTP) as an additive. HTP was added at 0.5% and 1.0% by wt. of BRC paste. The BRC paste was prepared at a water-to-cement ratio of 0.4 and cured under water and carbonation. The results demonstrated that upon carbonation, the incorporation of HTP at 1.0% increases the CO 2 uptake and compressive strength of specimens by 18.60% and 22.29%, respectively. A pore structure analysis shows a decrease in the threshold pore size diameter with an increase in the HTP content for CO 2 -cured samples. An SEM analysis revealed precipitation and impregnation of calcites in and around the HTP microfiber particles. The incorporation of HTP under water curing on the other hand did not significantly influence the strength or the physicochemical properties. It was observed that HTP contributes to improving the properties of CO 2 -cured BRC paste in two ways; the porous structure of HTP provides pathways for the deep permeation of CO 2 into the matrix, and the surface of HTP offers an additional area for calcite precipitation. [ABSTRACT FROM AUTHOR]