Abstract: Pr3+, Yb3+ co-doped CaYAlO4 (Pr, Yb: CYA) single crystal was grown using the Czochralski (CZ) method. For near-infrared quantum-cutting system, a quantum efficiency of 145% for Pr3+, Yb3+-codoped CYA crystal has been obtained by ignoring the nonradiative losses. Under excitation at 940nm, high intensities of 502nm, 555nm, 628nm, 661nm and 729nm emissions turn up. Fluorescence decay time of 3P0→3F2 emission of Pr3+ ions and 2F5/2→2F7/2 transition of Yb3+ ions were also studied as evidences for energy transfer. [Copyright &y& Elsevier]

Abstract: Infrared (1.2–1.6μm) luminescence in a ytterbium aluminium garnet (YbAG) crystal, doped with Cr (0.05at.%) ions, was investigated under CW laser diode pumping (λ =940nm). The Cr4+ emission band was observed with its peak at 1.34μm and measured to be about 1.3 times with respect to Yb3+ IR luminescence (λ =1.03μm). We demonstrate that for the excitation wavelength of 940nm Yb3+ ions act as sensitizers of the 3B2(3T2)–3B1(3A2) emission of Cr4+ ions. This crystal is promising as a high-efficient system for tunable laser (1.2–1.6μm) output. [Copyright &y& Elsevier]

Abstract: In this paper, we present results on upconversion luminescence performed on Yb3+-doped yttrium aluminum garnets under 940nm excitation. The upconversion luminescence was ascribed to Yb3+ cooperative luminescence and the presence of rare earth impurity ions. The cooperative luminescence spectra as a function of Yb concentration were measured and the emission intensity variation with Yb concentration was discussed. Yb3+ energy migration quenched the cooperative luminescence of Yb:YAG crystals with doping level over 15at%. [Copyright &y& Elsevier]

Abstract: Infrared (1.2–1.6μm) luminescence in a yttrium aluminium garnet (YAG) crystal, co-doped with Yb (10 at.%) and Cr (0.05 at.%) ions, was investigated under CW laser diode pumping (λ =940nm). The Cr4+ emission band was observed with its peak at 1.35μm and measured to be about 6% with respect to Yb3+ IR luminescence (λ =1.03μm). Analysis of the crystal absorption and luminescence spectra allows one to conclude that Yb3+–Cr4+ energy transfer is a mechanism responsible for the 3B2(3T2)–3B1(3A2) emission of Cr4+ ions. This crystal is promising as an efficient source of the near infrared emission. [Copyright &y& Elsevier]