Search

With the aim of providing better control of shooting experiments performed with replicas of prehistoric projectiles, we have conducted an instrumental archaeology study on the efficiency of prehistoric projectile points by placing emphasis on their adhesion and ballistic characteristics. In order to avoid any reproducibility problems, hafting adhesives were made with controlled mixtures of commercial rosin (also called 'colophany') and beeswax added as a plasticizer. An original experimental device has been developed to instrument a bow, allowing the control of both the trajectories and the velocities of the different shoots. In the course of an experimental programme on Sauveterrian microliths from the Mesolithic period of the South of France, the experimental system was applied to composite replica projectile tips of Mesolithic hunters. Arrows being shot at transparent targets were filmed in order to evaluate the penetration length and residual damage. Interestingly, this study reveals that the properties of the mixture are highly dependent on the velocity of the arrows. It was shown that-contrary to previous experiments that usually used a mixture in which rosin predominates- the most efficient adhesive is made of 70 wt% beeswax with only 30 wt% rosin. This result is of great importance for improving further shooting experiments and overcoming the problems frequently mentioned due to the loss of the flint armatures before they reach the animal target, or at least before penetration. When using this appropriate mixture, the lateral armatures are resistant to most of the shots. Experiments performed on real boars' flesh have also shown that the presence of lateral microliths allows the laceration inflicted on the target to be enlarged. Finally, a critical parameter has been identified, which is the location on the arrow of the microlithic element. [ABSTRACT FROM AUTHOR]

Blends of rosin and beeswax were studied in terms of their thermal and mechanical behaviors. Their glass transition and α relaxation were both characterized, either by differential scanning calorimetry or by dynamic mechanical thermal analysis. In this study, we focused particularly on the impact of the microstructure on the mechanical properties, as studied by compression, shear, and nanoindentation tests. It is shown that at room temperature, these blends exhibited a viscous behavior in both the elastic and plastic regimes. From these measurements, a superplastic behavior was highlighted for blends with more than 60 wt % rosin. This superplastic behavior constitutes a real new potential in the mechanical reliability of adhesives based on rosin, which are more generally known for their very brittle behavior. As a result, it should open the way for the design of new shapes. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013 [ABSTRACT FROM AUTHOR]

The article discusses a study which evaluated the response to Berkovich indents of tetragonal and cubic phases in terms of hydrothermal degradation by using nonoindentation techniques, atomic force microscopy and Focused Ion Beam. Yttria-doped zirconia ceramics possess mechanical properties, such as strength and fracture toughness, which arise from the submicron average grain size. Results showed that microcracking is the primary reason of the drop in mechanical properties.

Electron beam-physical vapour deposited (EB-PVD) yttria-stabilized zirconia (YSZ) thermal barrier coatings have been investigated by nanoindentation. It is shown that the mechanical properties, and particularly the Young's modulus, of these coatings are closely related to their columnar microstructure. The transition from intracolumnar to intercolumnar deformation is characterized by a difference between the mechanical properties of the bulk YSZ and those of the coatings. The use of different indenter shape showed that the contact area was the parameter characteristic of this scale dependence. Deformation mechanisms studied by AFM have shown a good correlation with the evolution of the mechanical properties during the deformation. [ABSTRACT FROM AUTHOR]

This study investigates the incipient plasticity during a nanoindentation test with a spherical indenter in magnesium oxide single crystals. The load–displacement curves show multiple pop-ins, interspaced by elastic deformation, and reveal the transition from an initial elastic deformation regime to a continuous elastoplastic one. Nanoindentations have been stopped after the first pop-in and the dislocation structures have been three-dimensionally characterized by AFM observations of the surface deformation and by nanoetching. The dislocation pattern shows two activated slip systems. The resolved shear stress has been calculated just before the pop-in, for all of the activated slip systems. The final positions of the dislocations generated during the first pop-in reveal that they were all nucleated at the point of maximum resolved shear stress. [ABSTRACT FROM AUTHOR]

The instrumented indentation response of polycrystalline alumina and alumina-based ceramic multilayers with well-known residual stresses is investigated. Young's modulus and hardness were evaluated as a function of penetration depth with Berkovich and spherical indenters by continuous stiffness measurements. A size effect was observed due to the length scale of the microstructure. Values of hardness and Young's modulus were in good agreement with previous works. No significant differences in the P – h curves were observed for materials with and without residual stress, making it difficult to employ the various methodologies in the literature for estimation of residual stress or crack length evaluation. Crack length had, therefore, to be measured by direct observation. Thus, cube corner indentations did not produce well-developed radial cracks but chipping of the material, whereas indentations with Berkovich indenters produced radial cracks suitable for apparent fracture toughness estimation and, consequently, residual stress. [ABSTRACT FROM AUTHOR]

This letter is based on recent progress in the observation of dislocation distributions around nanoindentations by chemical etching. This so-called nanoetching technique is used to determine the dislocation mechanisms associated with the pop-in phenomenon in MgO and LiF. Successive stages of highly controlled chemomechanical polishing have revealed that these dislocations are half-loops lying in the classical slip systems of MgO or LiF. However, they do not extend on the surface in the classical rosette-arms pattern but stay concentrated around the imprint. A mechanism of dislocation interactions, enhanced by the fact that the dislocations are suddenly nucleated in a small volume, is proposed to explain this specific distribution. [ABSTRACT FROM AUTHOR]

Abstract: Two cases of scavenging postmortem freshwater shrimps (Gammarus pulex) are presented. We report the two first illustrated observations of cutaneous postmortem injuries inflicted by a G. pulex population, a small freshwater crustacean, on two non putrefied drowning victims, and we describe their particular histological features and their potential in forensic investigations. [Copyright &y& Elsevier]