In this paper, nanosized ZnFe 2 O 4 with different morphologies were prepared by electrospinning method. The choice of initial parameters, such as PVP concentration, metal salt concentration, electrostatic voltage, calcination temperature and calcination rate, were investigated to prepare desired morphologies. The as-prepared samples exhibited various shapes of nano-particle, nano-rods, nano-beads and nano-fiber. The relationship between microstructure and electromagnetic properties was discussed in detail. It has been found that the saturation magnetization of ZnFe 2 O 4 ferrite not changed significantly with the various morphologies and the values were nearly 13 emu/g. However, the coercivity was varied with the different morphologies, and the maximum value of 48.79 Oe was observed in the ZnFe 2 O 4 nano-fiber. Moreover, the magnetic loss capacity of ZnFe 2 O 4 was improved with the enhancement of the morphology anisotropy. The various shaped ZnFe 2 O 4 can be promising lightweight microwave absorbers and it is significant to develop novel microwave absorption mechanism of ZnFe 2 O 4 ferrite. [ABSTRACT FROM AUTHOR]

In this work, an Al powder was coated with antimony-doped tin oxide (ATO) to obtain an infrared-laser compatible stealth material. The composites are prepared via a coprecipitation method, characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD), and measured by ultraviolet spectrophotometer and dual band infrared emissometer. The morphology and microstructure show that the flaky Al powder was coated by the ATO nanoparticles and doped into the SnO 2 rutile structure by an Sb5+ ion. The optimal Al content was 20%, and the optimized Sn/Sb molar ratio was 10: 1. Meanwhile, the reflectivity of the composites was 43.454%, and the infrared emissivity in 8–14 μm far infrared waveband range was 0.708. It may shed light on a new material design orientation to obtain high performance laser-infrared compatible stealth materials. [ABSTRACT FROM AUTHOR]