Search

This paper presents experimental results from three-point bending tests for a composite made of quadriaxial glass fiber fabrics and an epoxy resin. Two composites were tested, one with 8 layers and the other with 16 layers; both had the same matrix (the epoxy resin). Tests were carried out, using five different test rates from 10 mm/min to 1000 mm/min. The following parameters were recorded and calculated: Young's modulus, flexural stress, flexural strain, energy, force, and all four for the first peak. The experimental data reveal no sensitivity for these materials based on the test rates, at least for the analyzed range; but, the characteristics for the thicker composite, with 16 layers of fabric, are slightly lower than those for the thinner composite, with 8 layers. The results pointed out that, for the same thickness of composite, certain characteristics, such as stress at the first peak, the flexural modulus, strain at the first peak, and energy at the first peak, are not sensitive to the test rate in the range 10–1000 mm/min. The energy at the first peak is double for the 16-layer composite compared to the 8-layer composite, but the specific energy (as energy on cross-sectional area) has close values: 103.47 kJ/m2 for the 8-layer composite and 106.51 kJ/m2 for the 16-layer composite. The results recommend this composite for applications in components with resistance to bending or for low-velocity impact protection. [ABSTRACT FROM AUTHOR]

This paper presents an analysis based on experimental data for pointing out the behavior of rapeseed oil when it is additivated with a modifier of friction and wear, the nano hexagonal Boron nitride. All tests are done on a four-ball machine, in mild regime. Test parameters were sliding velocity (0.38 m/s, 0.53 m/s, 0.69 m/s, corresponding to the spindle rotational speed of the four-ball machine of 1000 rpm, 1400 rpm, 1800 rpm (±10 rpm),), force (100 N – 300 N), test duration 1 h. There were calculated the average friction coefficient during the test and the average wear scar diameter (WSD) for each test. The same test parameters were done twice and the values in this paper are the average of these two tests. Wear was discussed for the same velocity range, in terms of WSD, but for comparing tests with different sliding velocity (implicitly, different sliding distances), there was used the wear rate of the wear scar diameter. The results on wear parameters, using additivated rapeseed oil, do not show spectacular results for the parameters tested in this study, but underline the “insensitivity” of the lubricants to the variation of the test regime (especially with respect to sliding speed), which is desirable for certain applications. [ABSTRACT FROM AUTHOR]

This paper presents results from numerical and experimental investigation on Charpy tests in order to point out failure mechanisms and to evaluate new polymeric blends PP + PA6 + EPDM. Charpy tests were done for initial velocity of the impactor of 0.96 m/s and its mass of 3.219 kg and these data were also introduced in the finite element model. The proposed model takes into account the system of four balls, including support and the ring of fixing the three balls and it has a finer discretization of the impact area to highlight the mechanisms of failure and their development in time. The constitutive models for four materials (polypropylene with 1% Kritilen, two blends PP + PA6 + EPDM and a blend PA6 + EPDM) were derived from tensile tests. Running simulations for each constitutive model of material makes possible to differentiate the destruction mechanisms according to the material introduced in the simulation, including the initiation and the development of the crack(s), based on equivalent plastic strain at break (EPS) for each material. The validation of the model and the simulation results were done qualitatively, analyzing the shape of broken surfaces and comparing them to SEM images and quantitatively by comparing the impact duration, energy absorbed by the sample, the value of maximum force during impact. The duration of the destruction of the specimen is longer than the actual one, explainable by the fact that the material model does not take into account the influence of the material deformation speed in Charpy test, the model being designed with the help of tests done at 0.016 m/s (1000 mm/min) (maximum strain rate for the tensile tests). Experimental results are encouraging for recommending the blends 20% PP + 42% PA6 + 28% EPDM and 60% PA6 + 40% EPDM as materials for impact protection at low velocity (1 m/s). Simulation results are closer to the experimental ones for the more brittle tested materials (with less content of PA6 and EPDM) and more distanced for the more ductile materials (with higher content of PA6 and EPDM). [ABSTRACT FROM AUTHOR]