The aim of achieving integration of lightweight, high strength, high‐temperature resistant, and satisfactory electromagnetic (EM) wave absorption was successfully accomplished in the present study by synthesizing TiC–TiB2 fibers reinforced Si3N4 composites, which were pressureless sintered at 1650°C for 2 h. The preparation of TiC–TiB2 fibers was conducted through a chloride‐assisted carbothermic method. This work focused on investigating the effects of incorporating TiC–TiB2 fibers on the mechanical properties and EM wave absorption characteristics of the composites. The 30 wt% TiC–TiB2/Si3N4 composite displayed the bulk density of 1.89 g/cm3, bending strength of 93.11 ± 3.91 MPa, fracture toughness of 1.81 ± 0.10 MPa m1/2, minimum reflection loss of −38.87 dB, and effective absorption bandwidth of 1.43 GHz in the Ku‐band, respectively. The as‐synthesized TiC–TiB2/Si3N4 composites are promising candidates for EM wave absorbing load‐bearing materials due to their outstanding mechanical properties and microwave absorption properties. [ABSTRACT FROM AUTHOR]

In view of the lack of conformal, load‐bearing, light‐weight, and high temperature‐resistant integrated wave‐absorbing composites suitable for extremely complex conditions, the gel‐casting process was successfully applied to porous Si3N4 wave‐absorbing composites in this work. A universal low‐slurry for gel casting was prepared by using two dispersants acting together (tetramethylammonium hydroxide solution and sodium lauryl sulfate), which ensured the smooth completion of the gel casting process. Combining the thermogravimetric and differential thermal gravity curves of the composite green body, reasonable parameters of the rubber discharge process are given to avoid the problem of the green body swelling and cracking. The porous TiC/Si3N4 composites were successfully prepared by holding them at 1650°C for 3 h. The bending strength, density, minimum reflection loss, absorption bandwidth, and matched thickness in the P‐band of the composites with 30 wt.% TiC addition were 54.08 ± 3.02 MPa, 1.906 g/cm3, ‐37.75 dB, 1.9 GHz, and 4.1 mm, respectively. The electromagnetic wave loss mechanisms of the composites are a combination of conductivity loss, multiple reflections and scattering, interfacial polarization, and defect polarization. [ABSTRACT FROM AUTHOR]

A sol-gel method was employed for the synthesis of new High-entropy boride (HEB) powders, (Hf 0.2 Nb 0.2 Cr 0.2 Ta 0.2 Mo 0.2)B 2 , with nanoscale. The as-synthesized powders were obtained at a relatively low temperature of 1650 °C, and had small average particle size of 62.09 nm. X-ray diffraction confirmed that the (Hf 0.2 Nb 0.2 Cr 0.2 Ta 0.2 Mo 0.2)B 2 powders were hexagonal single-phase without any oxide impurities. In particular, electrochemical performance of the (Hf 0.2 Nb 0.2 Cr 0.2 Ta 0.2 Mo 0.2)B 2 powders with multiphase and high-entropy single phase were investigated using a three-electrode system. The improved electrochemical performance of the HEB powders is realized, with 27% higher in specific capacitance compared to the powders with multiphase. The HEB powders electrode exhibits a high capacitance retention of 97.03% after 5000 cycles. [ABSTRACT FROM AUTHOR]

The boron nitride nanosheets (BNNSs)/aluminum nitride (AlN) composites were prepared by hot press sintering at 1600°C. The microstructure, mechanical properties, and thermal conductivity of the samples were measured, and the effect of adding BNNSs to AlN ceramics on the properties was studied. It is found that the addition of BNNSs can effectively improve the mechanical properties of AlN. When the additional amount is 1 wt%, the bending strength of the sample reaches the maximum value of 456.6 MPa, which is 23.1% higher than that of the AlN sample without BNNSs. The fracture toughness of the sample is 4.47 MPa m1/2, a 68.7% improvement over the sample without BNNSs. The composites obtained in the experiment have brilliant mechanical properties. [ABSTRACT FROM AUTHOR]

Silica is one of the most widely used ceramics due to its excellent chemical stability and dielectric property. However, its destructive brittle nature inhabits it from wider application as a functional ceramic. An improvement in toughness is a challenging topic for silica ceramic, as well as other ceramics. In the paper, silica ceramic with different types of boron nitride powders and alumina platelets was fabricated by hot-pressing. Introduction of the additives had great influence on the composites' mechanical properties and microstructure. The silica matrix composite containing micro-sized boron nitride powders possessed the best mechanical properties, including the bending strength (134.5 MPa) and the fracture toughness (1.85 Mpa·m1/2). Meanwhile, the introduction of alumina platelets combined with boron nitride nanosheets achieved an effective enhancement of fracture toughness while maintaining the bending strength. Compared with the monolithic silica, the composite with simultaneous addition of alumina platelets and boron nitride nanosheets had a fracture toughness of 2.23 Mpa·m1/2, increased by approximately 27% (1.75 Mpa·m1/2). The crack deflection and platelet pullout were contributing to enhancement of the fracture toughness. The improved mechanical properties, combined with the intrinsic excellent dielectric and chemical properties, make the silica matrix composites promising wave transparent and thermal protection materials. [ABSTRACT FROM AUTHOR]

Alumina is one of the most commonly used and researched structural ceramic because of its excellent properties. However, its intrinsic brittleness is the fatal drawback, which hinders it from wider applications. How to improve its fracture toughness as well as the bending strength is always challenging for material researchers. In this paper, alumina matrix composites were fabricated by hot-pressing, in which some additives, including zirconia, alumina platelets, and MXene, were incorporated. The influence of the introduced additives on their microstructure and mechanical properties was investigated. Compare with the monolithic alumina, both bending strength and fracture toughness of all samples were improved greatly. Incorporation of zirconia was beneficial to the mechanical properties due to the phase-transformation strengthening and toughening mechanism. While alumina platelets resulted in high fracture toughness because of the self-toughening of elongated grains. The synergistic effect of alumina platelets and MXene enormously improved the fracture toughness from 2.9 ± 0.3 MPa·m1/2 for monolithic alumina to 7.5 ± 0.4 MPa·m1/2 for the composite, which was increased by 159%. This work will provide useful references for the fabrication of high-strength and high-toughness alumina ceramics by introducing additives properly. [ABSTRACT FROM AUTHOR]

Upconversion (UC) luminescence modulation is quite important in controlling and processing light for active components of light sources, photoswitches, optical memories, and optical sensing devices. In this work, we reported one kind of novel phosphor, Ho3+/Yb3+‐doped SrBi4Ti4O15 ceramics, which displayed both strong UC luminescence and obvious photochromic (PC) reaction. The UC luminescence, PC effect, and the modulation of UC performance based on PC behavior were investigated in detail. By alternating visible light irradiation and thermal stimulus, the UC luminescence could be reversibly regulated. Meanwhile, the modulation was unveiled to tightly rely on the irradiation time and thermal treatment processes. Excellent reproducibility was also achieved. In addition, as an alternative method to thermal treatment, the manipulation of luminescence by electric field was also explored. Finally, the mechanism related to the UC luminescence manipulation was illustrated. The results indicate that these samples could be potentially utilized in optical data storage and anti‐counterfeiting security fields. [ABSTRACT FROM AUTHOR]

Strontium has been widely used in bone repair materials due to its roles in promoting osteoclast apoptosis and enhancing osteoblast proliferation. In this work, synthesis and the effects of Sr2+ doping α-tricalcium phosphate at low-temperature was studied. The setting time and the mechanical properties of α-tricalcium phosphate were controlled by varying the content of Sr2+. The synthesized compounds were evaluated by XRD, SEM, XPS, setting time, compressive strength, SBF immersion, and colorimetric CCK-8 assay. The results showed that Sr2+ can improve the compressive strength and cell activity of calcium phosphate bone cement. [ABSTRACT FROM AUTHOR]

In this research, a novel layered O3-type NaNi0.48Mn0.3Ti0.2Ru0.02O2 is fabricated by using solid-state method for sodium-ion batteries. Sodium-ion battery (SIB) can be a promising alternative to the current lithium-ion battery (LIB) technology due to the shortage of lithium in nature and higher cost. As a promising cathode material, NaNi0.48Mn0.3Ti0.2Ru0.02O2 electrode shows a high reversible capacity of 155.3 mA h g−1 at 0.05 C (12 mA g−1) in the range of 1.5-4.5 V and exhibits a favorable coulombic efficiency. DFT calculation and X-ray diffraction, Raman, X-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy analysis are introduced to reveal the effects of substitution of Ru4+ for Ni2+ including the decreasing electronic localization, more stable material structure, wider sodium-ion diffusion channels and good diffusion coefficient of Na. The doping of Ru has paved a new way to enhance the electrochemical performances of O3-type cathode materials for SIBs. [ABSTRACT FROM AUTHOR]

Well-dispersed boron nitride nanosheets (BNNSs) reinforced fused silica composites were successfully fabricated by surface modification assisted flocculation method. Surface modification can enhance the performance of flocculation process. BNNSs were homogeneously mixed with fused silica through the electrostatic interaction between hydroxylated BNNSs with negative charge and amino-modified fused silica with positive charge. The BNNSs can act as excellent nanofillers for enhancing the mechanical properties of fused silica composites. Approximately 74% and 48% increases in flexure strength and fracture toughness can be achieved for the 1.5 wt% BNNSs/fused silica composite, respectively. The toughening mechanisms were analyzed by microstructural characterization, especially for pull-out mechanism. [ABSTRACT FROM AUTHOR]

Objectives Emerging studies have demonstrated that micro RNAs (mi RNAs) play crucial roles in carcinogenesis of many developing human tumours. However, the functions and mechanisms of miR-297 in lung cancer have, up to now, been largely undefined. Materials and methods Here, miR-297 expression was measured in lung adenocarcinoma tissues and cell lines, using qRT- PCR. Lung adenocarcinoma cell line was treated with an miR-297 mimic. MTT and colony analysis were performed to detect cell proliferation and colony formation. The direct target gene of miR-297 was assessed by qRT- PCR, Western blotting and luciferase assays. Results We demonstrated that miR-297 expression was upregulated in lung adenocarcinomas compared to adjacent normal tissues. Expression of miR-297 was also upregulated in tested lung adenocarcinoma cell lines. Ectopic expression of miR-297 enhanced lung adenocarcinoma cell proliferation and colony formation. Furthermore, overexpression of miR-297 promoted cell migration and invasion. In addition, we identified Glypican-5 ( GPC5) as a direct target gene of miR-297 in lung adenocarcinoma cells. Expression of GPC5 was downregulated in both lung adenocarcinoma tissues and cell lines. Moreover, expression of GPC5 was inversely associated with expression of miR-297 in lung adenocarcinoma tissues. Conclusions These results suggest that miR-297 acted as an oncogenic mi RNA, partly by targeting GPC5, adenocarcinoma of the lung. [ABSTRACT FROM AUTHOR]

Morphology of transition metal oxide largely affects its electrochemical energy storage properties. This also applies to its composites. In this paper, NiFe 2 O 4 /Graphene nanosheets composites (NFO/GNSs) are successfully prepared by a facile hydrothermal method. NiFe 2 O 4 (NFO) in the sample exhibits a unique nanosheet morphology, vertically arranging on the graphene nanosheets (GNSs). Microscopically, NFO nanosheets interpenetrate on the surface of graphene to form a continuous network structure. The sample exhibits excellent specific capacitance and rate performance. It is worth mentioning that the specific capacitance increases to 140% after 5000 cycles, showing superior cycle stability. This may be due to the conductive network formed by NFO nanosheets and GNSs. Excellent electrochemical performance indicates excellent application prospects of materials in supercapacitor electrodes. Image 1 • Unique NiFe 2 O 4 nanosheets structure with graphene nanosheets was successfully prepared by a hydrothermal method. • NiFe 2 O 4 nanosheets/graphene performed a better specific capacitance, arriving at 464.15 F/g at current density of 1 A/g. • The network structure formed between NiFe 2 O 4 nanosheets and graphene nanosheets provides excellent cycle performance. [ABSTRACT FROM AUTHOR]

Bimetallic carbides have aroused wide attention for energy-storage applications recently. In this work, one-dimensional Fe 2 MoC/CNFs (Fe 2 MoC/C nanofibers) are successfully synthesized via a facile electrospinning method for the first time. To obtain the most integrated structure between the Fe 2 MoC nanoparticles and carbon nanofibers, we explore the optimal heating rate during the carbonization treatment. Fe 2 MoC/CNFs exhibits an integrated one-dimensional structure under 800 °C with a heating rate of 5 °C/min. As revealed in the experimental results, Fe 2 MoC/CNFs possesses a high specific surface area of 196.9 m2/g, a high specific capacitance of 347.8 F/g at the current density of 1 A/g, an excellent rate capability of 91% capacitance retention from 1 A/g to 40 A/g, and shows superior cycling stability with the capacitance retention of about 85.6% and Coulombic efficiency of about 100% after 5000 cycles. An asymmetric supercapacitor coin-cell device using Fe 2 MoC/CNFs as the positive electrode displays an energy density of 14.5 Wh/kg at a power density of 300 W/kg and an outstanding cycling life of 93% retention after 5000 cycles. The impressive electrochemical performance indicates that the Fe 2 MoC/CNFs composite is a promising material for efficient supercapacitors. Image 1 • Fe 2 MoC nanofibers can be prepared via a facile electrospinning method. • Fe 2 MoC/CNFs-5 exhibits a superior rate capability and cycle stability. • ASC coin-cell device shows a promising energy and power density. [ABSTRACT FROM AUTHOR]

Boron nitride nanosheets (BNNSs) with relatively low dielectric constant and excellent mechanical strength were employed for fabrication of BNNSs/fused silica (FS) composites. High-temperature mechanical behavior and microstructural evolution of the composites were investigated. The addition of BNNSs can improve the mechanical properties of FS efficiently, and the reinforcement from BNNSs can be preserved during the high temperature service. The flexural strength of BNNSs/FS composites exhibited anomalous gains at certain high temperature range, which can be explained by the softening of FS matrix, the heal of defect tips, and the reinforcement from BNNSs. [ABSTRACT FROM AUTHOR]

Abstract Boron nitride nanosheets (BNNSs) have attracted increasing attention in the field of two-dimensional materials. In the paper, the BNNSs/alumina composites were fabricated by a flocculation method and hot pressing. It is found that the BNNSs were dispersed uniformly in the alumina matrix by the flocculation technique via pH adjustment. The experimental results showed that with the increasing BNNSs content, the density of the composites decreased. Compared with the monolithic alumina, bending strength of the composite with 1.0 wt% BNNSs was increased by 58.6%; while the fracture toughness was increased slightly. The addition of BNNSs changed the fracture pattern, refined the grains of composites and inhibited abnormal grain growth, which contributed to the improvement of mechanical properties of the composites. [ABSTRACT FROM AUTHOR]

A facile, low-cost, and room-temperature UV-ozone (UVO) assisted solution process was employed to prepare zirconium oxide (ZrO x ) films with high dielectric properties. ZrO x films were deposited by a simple spin-coating of zirconium acetylacetonate (ZrAcAc) precursor in the environment-friendly solvent of ethanol. The smooth and amorphous ZrO x films by UVO exhibit average visible transmittances over 90% and energy bandgap of 5.7 eV. Low leakage current of 6.0 × 10 −8 A/cm 2 at 3 MV/cm and high dielectric constant of 13 (100 Hz) were achieved for ZrO x dielectrics at the nearly room temperature. Moreover, a fully room-temperature solution-processed oxide thin films transistor (TFT) with UVO assisted ZrO x dielectric films achieved acceptable performances, such as a low operating voltage of 3 V, high carrier mobility of 1.65 cm 2 V −1 s −1 , and on/off current ratio about 10 4 –10 5 . Our work indicates that simple room-temperature UVO is highly potential for low-temperature, solution-processed and high-performance oxide films and devices. [ABSTRACT FROM AUTHOR]