1. Impact of Cyclic Densification on Bending Strength and Modulus of Elasticity of Wood from Temperate and Tropical Zones.
- Author
-
Laskowska, Agnieszka
- Subjects
- *
ENGLISH oak , *FLEXURAL strength , *WOOD bending , *BENDING strength , *MODULUS of elasticity , *ALNUS glutinosa - Abstract
Oak (Quercus robur L.), iroko (Milicia excelsa (Welw.) C.C. Berg), and tauari (Couratari spp.) wood were subjected to cyclic thermo-mechanical treatment (CTMT). The densification temperature amounted to 100 °C or 150 °C. The greatest changes in the modulus of rupture (MOR) value of the iroko wood, depending on the number of thermo-mechanical modification cycles, were noted. The MOR of the iroko wood, densified at 100 °C or 150 °C, after second thermo-mechanical modification cycle was twice as high as before the modification. No significant differences were observed between the modulus of elasticity (MOE) of oak wood before and after one modification cycle. Similar dependencies were noted in iroko wood. The thermo-mechanical modification performed over two cycles led to the highest increase, by about 56%, in MOE in oak wood densified at 150 °C. It was demonstrated that modification at 150 °C had a negative impact on iroko wood, which was manifested in the lower compression ratio of iroko at 150 °C than at 100 °C. [ABSTRACT FROM AUTHOR]
- Published
- 2020
- Full Text
- View/download PDF