Search

High modulus aramid fiber, such as Kevlar 49, is conventionally prepared by the heat annealing of high strength aramid fiber under a suitable tension at high temperature, especially higher than 500 °C. This enables the mobility of a rigid molecule chain to be rearranged into a more perfect crystalline or orientation structure under tension. However, annealing decreases the tensile strength, since the thermal degradation of the molecular chain at high temperature cannot be avoided. Kevlar 49 fibers treated in supercritical carbon dioxide (scCO2) under tension could improve their mechanical properties at a low temperature. The effects of the tension on the mechanical properties and structure of the Kevlar 49 fibers were studied by mechanical testing, wide-angle and small-angle X-ray scattering (WAXS, SAXS), and scanning electron microscopy (SEM). The results show that the mechanical properties, crystallinity and orientation of the fiber can be improved when the tension is less than 0.6 cN/dtex, which may be due to the increasing of the mobility of a rigid segment with the help of the plasticization of scCO2 and re-arrangement of macromolecular chain into crystalline and orientation structure under tension. What's more, the amorphous region also was enhanced by crosslinking reaction of toluene 2,4-diisocyanate (TDI) with the chain end groups of the macromolecules in the amorphous regions. However, a decrease of tenacity was found when the tension was higher than 0.6 cN/dtex, which is because the tension was so high that the microfibril was broken. The results indicated that treating the Kevlar 49 fiber in scCO2 under a suitable tension with TDI as a crosslink agent can simultaneously improve both the tenacity and modulus of the fiber. [ABSTRACT FROM AUTHOR]

This article has been withdrawn at the request of the author(s) and/or editor. The Publisher apologizes for any inconvenience this may cause. The full Elsevier Policy on Article Withdrawal can be found at https://www.elsevier.com/about/our-business/policies/article-withdrawal. [ABSTRACT FROM AUTHOR]

High molecular weight poly (p-phenylene-terephthalamide) (h-PPTA) was blended with the commercial PPTA in concentrated sulfuric acid to improve the spinnability of the polymer solutions and the mechanical properties of the as-spun fibers. h-PPTA in the solution has an influence on the temperature of the formation of liquid crystalline phenomenon. The temperature range with the existence of the liquid crystalline phase increases upon the contents of h-PPTA in the solution, and the extended temperature window is helpful for the preparation of PPTA fibers by the dry-jet wet-spinning technology. The long-chains of h-PPTA enhance the inter-macromolecular interactions and induce the orientation of short-chains for PPTA along the fiber axis under the shear stress in the spinneret and the stretching stress at the air gap. These effects also increase the maximum drawing ratio in the spinning process and improve the mechanical properties of the obtained fibers. The crystallinity and crystal orientation of the fibers are investigated by X-ray diffraction, and results from sonic velocity test further confirm ordering state of the macromolecular chains. The fibril morphologies of the fibers are also studied by a scanning electric microscope. [ABSTRACT FROM AUTHOR]

Aramid fibers with low density and high strength, modulus, and thermal resistance are widely used in applications such as bulletproof vests and cables. However, owing to their chemical structure, they are sensitive to ultraviolet light, which degrades the fibers' useful mechanical properties. In this study, titanium dioxide (TiO2) nanoparticles were synthesized both on the aramid III fiber surface and in the interfacial space between the fibrils/microfibrils in supercritical carbon dioxide (scCO2) to improve the UV resistance of aramid fibers. The effects of scCO2 treatment pressure on the TiO2 structure, morphology, surface composition, thermal stability, photostability, and mechanical properties were investigated using Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, thermogravimetric analysis, ultraviolet–visible spectroscopy, and single-fiber test. The results show that amorphous TiO2 formed on the fiber surface and the interface between fibrils/microfibrils, and decreased the photodegradation rate of the aramid III fiber. Moreover, this modification can also improve the tensile strength via treatment at low temperature and without the use of a solvent. The simple synthesis process in scCO2, which is scalable, is used for mild modifications with a green solvent, providing a promising technique for synthesizing metal dioxide on polymers. [ABSTRACT FROM AUTHOR]

Aramid fibers (AFs) with their high Young′s modulus and tenacity are easy to degrade seriously with ultraviolet (UV) radiation that leads to reduction in their performance, causing premature failure and limiting their outdoor end use. Herein, we report a method to synthesize nano-SiO2 on AFs surfaces in supercritical carbon dioxide (Sc-CO2) to simultaneously improve their UV resistance, thermal stability, and interfacial shear strength (IFSS). The effects of different pressures (10, 12, 14, 16 MPa) on the growth of nanoparticles were investigated. The untreated and modified fibers were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). It was found that the nano-SiO2-decorated fibers exhibited improvement of thermal stability and mechanical properties, and the IFSS of the nano-SiO2 modified fibers increases by up to 64% compared with the untreated fibers. After exposure to 216 h of UV radiation, the AFs-UV shows a less decrease in tensile strength, elongation to break and tensile modulus, retaining only 73%, 91%, and 85% of the pristine AFs, respectively, while those of AFs-SiO2-14MPa-UV retain 91.5%, 98%, and 95.5%. In short, this study presents a green method for growing nano-SiO2 on the surface of AFs by Sc-CO2 to enhance the thermal stability, IFSS, and UV resistance. [ABSTRACT FROM AUTHOR]

In this work, the layer-by-layer self-assembly technology was used to modify aramid fibers (AFs) to improve the interfacial adhesion to epoxy matrix. By virtue of the facile layer-by-layer self-assembly technique, poly(l-3,4-Dihydroxyphenylalanine) (l-PDOPA) was successfully coated on the surface of AFs, leading to the formation of AFs with controllable layers (nL-AF). Then, a hydroxyl functionalized silane coupling agent (KH550) was grafted on the surface of l-PDOPA coated AFs. The properties such as microstructure and surface morphology of AFs before and after modification were characterized by FTIR, XPS and FE-SEM. The results confirmed that l-PDOPA and KH550 were successfully introduced into the surface of AFs by electrostatic adsorption. The interfacial properties of AFs reinforced epoxy resin composites before and after coating were characterized by interfacial shear strength (IFSS), interlaminar shear strength (ILSS) and FE-SEM, and the results show that the interfacial adhesion properties of the modified fiber/epoxy resin composites were greatly improved. [ABSTRACT FROM AUTHOR]