Highlights • THM-GC was applied to monitor the change in copolymer composition of film samples during soil burial test. • 3 HHx moieties in the polymer chains were preferentially biodegraded owing to their low crystallinity. • Local variation in the degree of biodegradation using only 30 μg of P(3HB-co-3HHx) film sample. Abstract Soil burial biodegradation behavior of poly(3-hydroxybutyrate- co -3-hydroxyhexanoate) [P(3HB- co -3HHx)] was studied based on its copolymer composition determined by thermally assisted hydrolysis and methylation-gas chromatography (THM-GC). The change in copolymer composition of P(3HB- co -3HHx) film samples during soil burial degradation test was monitored in detail by THM-GC. As a result, the copolymer compositions of 3HB units gradually increased, while those of 3HHx units decreased with soil burial time, almost correlating with recovery weight. Based on these results, the biodegradation mechanism of P(3HB- co -3HHx) was elucidated with considering the influence of the crystallinity on the biodegradability. Furthermore, local differences in biodegradability of a given P(3HB- co -3HHx) film after soil burial test were also successfully evaluated from the copolymer compositions obtained by THM-GC. [ABSTRACT FROM AUTHOR]

Abstract: In our previous paper, thermally assisted hydrolysis and methylation-gas chromatography (THM-GC) measurements of poly(butylene succinate-co-butylene adipate) (PBSA) in the presence of tetramethylammonium hydroxide had revealed that the butylene adipate (BA) content in the PBSA films gradually decreased with soil burial degradation time. In order to clarify the cause of this change in copolymer composition, biodegradation behavior of PBSA with lowered crystallinity was evaluated by THM-GC. PBSA film samples with lower degree of crystallinity, prepared by heating and cooling quickly the original commercially available films, were subjected to a soil burial biodegradation test at 30°C for up to 4 weeks. The copolymer compositions between BA and butylene succinate (BS) units in various stages of the degraded film samples were estimated on the basis of chromatograms obtained by THM-GC with less than 5% of the relative standard deviations. As a result, the change in copolymer composition for the heated PBSA films during soil burial was relatively small compared to the original films, suggesting that biodegradation for the heated films proceeded with the comparable rate for both BA and BS-rich moieties due to lowered crystallinity. Based on these results, the reason for the change in copolymer composition observed for the original PBSA films was clarified as follows: (1) the BA-rich moieties in the copolymer chains could show relatively lower crystallinity than the BS-rich moieties and (2) the BA-rich moieties were preferentially biodegraded during soil burial test, leading to the decrease in the BA content as the biodegradation proceeded. [Copyright &y& Elsevier]