The combination of multiple electrode materials and their reasonable structural design are conducive to the preparation of composite electrodes with excellent performance. In this study, based on carbon nanofibers grown with Ni(OH)2 and NiO (CHO) prepared by electrospinning, hydrothermal growth, and low-temperature carbonization, five transition metal sulfides (MnS, CoS, FeS, CuS, and NiS) were hydrothermally grown on their surfaces, exhibiting that CHO/NiS had the optimal electrochemical properties. Subsequently, the effect of hydrothermal growth time on CHO/NiS revealed that the electrochemical performance of CHO/NiS-3h was optimal, with a specific capacitance of up to 1717 F g−1 (1 A g−1), due to its multistage core–shell structure. Moreover, the diffusion-controlled process of CHO/NiS-3h dominated its charge energy storage mechanism. Finally, the asymmetric supercapacitor assembled with CHO/NiS-3h as the positive electrode demonstrated an energy density of 27.76 Wh kg−1 at a maximum power density of 4000 W kg−1, and it still maintained a power density of 800 W kg−1 at a maximum energy density of 37.97 Wh kg−1, exhibiting the potential application of multistage core–shell composite materials in high-performance supercapacitors. [ABSTRACT FROM AUTHOR]

Highly porous carbon electrodes for supercapacitors with high energy storage performance were prepared by using a new precursor blend of aromatic polyimide (PI) and polyvinylidene fluoride (PVDF). Supercapacitor electrodes were prepared through the electrospinning and thermal treatment of the precursor blends of aromatic PI and PVDF. Microstructures of the carbonized PI/PVDF nanofibers were studied using Raman spectroscopy. Nitrogen adsorption/desorption measurements confirmed their high surface area and porosity, which is critical for supercapacitor performance. Energy storage performance was investigated and carbonized PI/PVDF showed a high specific capacitance of 283 F/g at 10 mV/s (37% higher than that of PI) and an energy density of 11.3 Wh/kg at 0.5 A/g (27% higher than that of PI) with high cycling stability. [ABSTRACT FROM AUTHOR]

Porous carbon nanofibers (CNFs) with high energy storage performance were fabricated with a single precursor polymer, 6FDA-TFMB, without the use of any pore-generating materials. 6FDA-TFMB was synthesized, electrospun, and thermally treated to produce binder-free CNF electrodes for electrochemical double-layer capacitors (EDLCs). Highly porous CNFs with a surface area of 2213 m2 g−1 were prepared by steam-activation. CNFs derived from 6FDA-TFMB showed rectangular cyclic voltammograms with a specific capacitance of 292.3 F g−1 at 10 mV s−1. It was also seen that CNFs exhibit a maximum energy density of 13.1 Wh kg−1 at 0.5 A g−1 and power density of 1.7 kW kg−1 at 5 A g−1, which is significantly higher than those from the common precursor polymer, polyacrylonitrile (PAN). [ABSTRACT FROM AUTHOR]