Search

Efficient enhancement of the toughness of epoxy resins has been a bottleneck for expanding their suitability for advanced applications. Here, polysulfone (PSF) was adopted to toughen and modify the epoxy. The influences of PSF on the mechanical and thermal properties of the epoxy resin were systematically studied by optical microscopy, Fourier transform infrared spectrometer (FT-IR), differential scanning calorimetry (DSC), thermogravimetric analyzer (TG), dynamic mechanical thermal analyzer (DMA), mechanical tests and scanning electron microscope (SEM). The dissolution experimental results showed that PSF presents a good compatibility with the epoxy resin and could be well dissolved under controlled conditions. The introduction of PSF was found to promote the curing reaction of the epoxy resin without participating in the curing reaction and changing the curing mechanism as revealed by the FT-IR and DSC studies. The mechanical properties of PSF/epoxy resin blends showed that the fracture toughness and impact strength were significantly improved, which could be attributed to the bicontinuous phase structure of PSF/epoxy blends. Representative phase structures resulted from the reaction induced phase separation process were clearly observed in the PSF/epoxy blends during the curing process of epoxy resin, which presented dispersed particles, bicontinuous and phase inverted structures with the increase of the PSF content. Our work further confirmed that the thermal stability of the PSF/epoxy blends was slightly increased compared to that of the pure epoxy resin, mainly due to the good heat resistance of the PSF component. [ABSTRACT FROM AUTHOR]

To satisfy the light weight requirements of vehicles owing to the aggravation of environmental pollution, carbon-fiber (CF)-reinforced epoxy composites have been chosen as a substitute for traditional metal counterparts. Since the current processing methods such as resin transfer molding (RTM) and compression molding (CM) have many limitations, an integrated and optimal molding method needs to be developed. Herein, we prepared high-performance composites by an optimized molding method, namely compression resin transfer molding (CRTM), which combines the traditional RTM and CM selectively and comprehensively. Differential scanning calorimetry (DSC) and rotational rheometry were performed to optimize the molding parameters of CRTM. In addition, metallurgical microscopy test and mechanical tests were performed to evaluate the applicability of CRTM. The experimental results showed that the composites prepared by CRTM displayed superior mechanical properties than those of the composites prepared by RTM and CM. The composite prepared by CRTM showed up to 42.9%, 41.2%, 77.3%, and 5.3% increases in tensile strength, bending strength, interlaminar shear strength, and volume fraction, respectively, of the composites prepared by RTM. Meanwhile, the porosity decreased by 45.2 %. [ABSTRACT FROM AUTHOR]

In this study, a series of GO with different oxidation levels were prepared via a modified Hummers' method, in which the oxidant/graphite ratio and oxidation time were varied. The change of GO structure as a function of oxidation level was investigated by X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, Raman spectroscopy, and X-ray diffraction measurements. The prepared GO were used for reinforcing epoxy resins, and the surfaces of GO were functionalized by the amine hardener during the dispersion process. Microscopic observations show that the oxidation level has a significant impact on the dispersion state of GO in the epoxy matrix. Both GO with the low and high oxidation levels tend to have low degree of dispersion, even aggregate. The influences of oxidation level on the performances of epoxy/GO composites, including curing behaviors, rheological, thermal and mechanical properties, were investigated in detail. Notably, the GO with optimum level of oxidation (denominated as GO-4) shows superior toughening effects on the epoxy matrix, compared to the reported epoxy/GO composites. The incorporation of merely 0.2 wt% GO-4 would yield 56 and 128% enhancement in the critical stress intensity factor ( K IC ) and the critical strain energy release rate ( G IC ), respectively. [ABSTRACT FROM AUTHOR]

In this study, a phase inversion approach was employed to fabricate four different thicknesses (20 μm to 100 μm) of polyethersulfone (PES) porous films with visible holes (1 hole/cm2) on the surface, applied as interleaves to improve the interlaminar fracture toughness of carbon fiber/epoxy composite laminates prepared by vacuum assistant resin infusion process (VARI). The film could dissolve into the epoxy resin which as clearly evident by the optical microscopy under a controlled condition. It was noted that the thickness of the resin-rich layer and the distribution of PES microspheres in the interlaminar layer depended on the thickness of the PES porous film. Also, mode I and mode II fracture toughness, interlaminar shear strength (ILSS), flexural properties as well as tensile properties of the CF/EP composites had all been characterized and analyzed in detail and in order. The results demonstrated that mode I and mode II fracture energies at the optimal interleaved laminates for the toughened system were increased by 61.5% and 55.1% compared to the composites without interleaves, respectively. Besides, PES porous film interleaved laminates displayed an increase of 32% for the interlaminar shear strength and no significant changes in the flexural and tensile properties. It was observed that the films induced toughening via two mechanisms: i) cohesive failure in a thicker resin region and ii) crack deflection and microcrack caused by PES microspheres, illustrated in the microstructure analysis of the failure surfaces and the observations of the crack propagation path. [ABSTRACT FROM AUTHOR]