Search

In this study, the performance of braided composite tubes under low-velocity transverse impact loading at mid-span was investigated using both numerical and experimental methods. Three types of braided composite tubes with different braiding angles (30°, 45°, and 60°) were manufactured. The transverse punch behavior of the tubes was examined on a low-velocity imspact test bench. A meso-level finite element model of the composite tube was also established for identifying the damage initiation and development. The numerical results showed a good correlation with the experimental data. The mechanical response including force–time histories, force–displacement histories, and fracture morphologies was compared between three types of composite tubes for analyzing the influence of braiding angle on the impact response and failure mode. Although suffering from the low bending stiffness depends on fiber volume fraction at initial impact stage, the braided tube with 30° angle engaged more portion to resist impact loading in subsequent process and thus presented higher peak loading than the one with large angle. In addition, there are distinct different failure modes between composite tubes with various braiding angles. Shear yarn breakage underneath the punch was prone to occur in 30° sample because the braiding yarn was closer to the axial direction of tube. In contrast, the resin was deboned severely from the braiding yarn and then the braiding yarn exhibits plastic deformation in 60° sample due to the stress concentration caused by the large braiding angle. [ABSTRACT FROM AUTHOR]

The aim of this study is to characterize and assess the effect of fabric structure on the damage resistance subjected to low velocity impact. Composite panels reinforced by layered unidirectional (LU), layered woven (LW) and 3D orthogonal woven (OW) fabric were prepared respectively and the impact tests were carried out on a low-velocity testbench. Finite element models at yarn-level were established to numerically investigate the material deformation and failure mechanism. The impact tests showed that the OW composite possessed better impact resistance with respect to impact-induced deformation and inelastic energy absorption. The roles of the z-binder have also been identified through comparison of impacted morphology and numerical results. The z-binder serves as cracking trigger due to the weak debonding with resin pocket around it and its zig-zag configuration impedes the growth of delamination by damage deflection. Therefore, the discontinuous resin damage in 3D composite allows the enhancement of impact resistance instead of delamination failure in the 2D panel. In addition, the in-plane interlacement of woven fabric causes that primary yarn breaks in the high stress region and forms a circle damage area, whereas the penetrating cracking along the fiber orientation of superficial layer is induced in the unidirectional composite. [ABSTRACT FROM AUTHOR]

Failure mechanism of complex profile component is always different from that of conventional plate counterpart due to the coupling effect of material and structure. In this work, the low-velocity impact (LVI) and compression after impact (CAI) behaviors of Ω-shape hybrid carbon/Kevlar 3 D orthogonal woven (3DOW) composite made for vehicle B-pillar were comprehensively studied by mechanical tests and mesoscale finite element (FE) analysis at component level, high-speed infrared (IR) thermal imaging, acoustic emission (AE) detection, and microscopic damage morphology characterization. It is found that a through-thickness stress concentration ring leads to high stress state and damage zone penetrating from the impact side to non-impact side along the ring path instead of at the lowest impactor position. The slope effect can not only help the stress conduction downward, but also inhibit the damage propagation from the impact side to the slope. Impact-induced cracks are concentrated around the R corners and extended along the axial direction of the specimen, forming the strip-shaped damage concentration zone along the upper eave of the slope. The Progressive Top-Down Crushing (PTDC) mode of compression after impact is due to the complex deformation process of each yarn such as squeezing, folding and eversion in the crushing process from the top of specimen. And the Middle Indentation Fracture (MIF) mode is the result of bending instability and abrupt fracture. This work presents a reference significance for the further development of composite strengthening components in vehicle bodywork. [ABSTRACT FROM AUTHOR]

• The structural hybridization effect on low-velocity impact response of braided/unidirectional (UD) laminates was investigates. • Continuum shell finite element models based on the anisotropic constitutive relationship of braided and UD plies were established to reveal the damage onset and propagation. • The extensive delamination formed rapidly when impacted on the fabric side. • The damage characterized by severe fiber breakage occurs at the impact site when impacted on UD ply side. This work investigated the structural hybridization effect on the low-velocity impact response of braided/unidirectional(UD) laminate. Two groups of hybridization laminates, namely interleaving and clustering groups, were manufactured. The impact performance of the specimens was characterized by combining dropping testbench, optical camera and ultra-sound detector. A continuum shell finite element model was established to reveal the progressive damage behavior of hybridization laminate. The specimen in the interleaving group presented overwhelming performance than that in the clustering group. The impact side effect on failure modes was discussed in detail. When impacted on the braided fabric side, extensive delamination formed on the edge of the specimen due to bending deformation. It further resulted in-plane crushing failure of UD sub-laminate. In contrast, severe fiber breakage occurs at the impact site due to combination stress of tensile and shear when impacted on UD side. Therefore, the fabric-impacted specimen exhibits better impact resistance than that impacted on UD side with respect to higher peak load and lower absorbed energy. [Display omitted] [ABSTRACT FROM AUTHOR]